Preparation method of graphene/xylogen-based active carbon

A technology based on lignin and activated carbon, which is applied in the chemical industry, can solve the problems of graphene agglomeration cost and low conductivity of activated carbon, and achieve the effect of improving reuse, increasing sources, and simple methods

Inactive Publication Date: 2015-05-06
江苏江大环保科技开发有限公司
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problems of low conductivity of activated carbon, severe graphene agglomeration and high cost in the prior art, the invention provides a preparation method of graphene and activated carbon composite material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Mix and dissolve 3 g lignin and 9 g potassium hydroxide in 50 mL deionized water, stir in a constant temperature water bath at 70 °C for 2 hours, evaporate the solvent slowly, place in a tube furnace, and heat at 5 °C / The temperature was raised to 850 °C for 1 hour at a constant temperature, cooled and taken out, washed with water until neutral, filtered with suction, and vacuum-dried at 70 °C to obtain lignin-based activated carbon. Weigh 0.25 g of graphite oxide and ultrasonically disperse it in deionized water to form a stable graphene oxide dispersion, add 2.25 g of lignin-based activated carbon, add 24 mM glutaraldehyde, 12 mM resorcinol, 0.08 mM borax, and ultrasonically react for 2 hours, filtered, and dried at 60°C to obtain graphite oxide / lignin-based activated carbon composites. Weigh 3 g of graphite oxide / lignin-based activated carbon composite and 9 g of potassium hydroxide, ultrasonically disperse in deionized water, stir at 60 °C for 3 hours, filter and d...

Embodiment 2

[0030] Mix and dissolve 3 g lignin and 12 g potassium hydroxide in 50 mL deionized water, stir in a constant temperature water bath at 70 °C for 2 hours, evaporate the solvent slowly, place in a tube furnace, and heat at 5 °C / The temperature was raised to 750 °C for 2 hours at a constant temperature, cooled and taken out, washed with water until neutral, filtered with suction, and vacuum-dried at 70 °C to obtain lignin-based activated carbon. Weigh 0.25 g of graphite oxide and ultrasonically disperse it in deionized water to form a stable graphene oxide dispersion, add 2.5 g of lignin-based activated carbon, add 24 mM glutaraldehyde, 12 mM resorcinol, 0.08 mM borax, and ultrasonically react for 2 hours, filtered, and dried at 60°C to obtain graphite oxide / lignin-based activated carbon composites. Weigh 3 g of graphite oxide / lignin-based activated carbon composite and 12 g of potassium hydroxide, ultrasonically disperse in deionized water, stir at 60 °C for 2 hours, filter and...

Embodiment 3

[0032] Mix and dissolve 3 g lignin and 15 g potassium hydroxide in 50 mL deionized water, stir in a constant temperature water bath at 70 °C for 2 hours, evaporate the solvent slowly, place in a tube furnace, and heat at 5 °C / The temperature was raised to 650 °C for 3 hours at a constant temperature, cooled and taken out, washed with water until neutral, filtered with suction, and vacuum-dried at 70 °C to obtain lignin-based activated carbon. Weigh 0.25 g of graphite oxide and ultrasonically disperse it in deionized water to form a stable graphene oxide dispersion, add 2 g of lignin-based activated carbon, add 24 mM glutaraldehyde, 12 mM resorcinol, 0.08 mM borax, and ultrasonically react for 3 hours, filtered, and dried at 60°C to obtain graphite oxide / lignin-based activated carbon composites. Weigh 3 g of graphite oxide / lignin-based activated carbon composite and 15 g of potassium hydroxide, ultrasonically disperse in deionized water, stir at 60 °C for 4 hours, filter and d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of chemistry, and provides a preparation method of graphene / xylogen-based active carbon; the method comprises the following steps: 1) preparing xylogen-based active carbon; 2) mixing graphite oxide with active carbon to obtain graphite oxide / xylogen-based active carbon compound; 3) activating the compound by alkali, treating with pyrolysis and reduction, so as to prepare graphene / xylogen-based active carbon composite material; 4) preparing an electrode slice. Comparing to the prior art, the obtained graphene / xylogen-based active carbon provides a larger specific surface, a smaller mass transfer resistance, and a better conductivity. Additionally, applying the synthesized graphene / xylogen-based active carbon to the electrode material of a super capacitor is much better than the existing active carbon material from cost and performance.

Description

technical field [0001] The invention belongs to the field of chemical industry, in particular to a preparation method of graphene / lignin-based activated carbon. Background technique [0002] Supercapacitor is a new type of energy storage device developed in the 1970s and 1980s. It is a power source with special properties between traditional capacitors and batteries. It mainly relies on electric double layers and redox pseudocapacitance to store electrical energy. , which is different from traditional chemical power sources. The outstanding advantages of supercapacitors are high power density, short charge and discharge time, long cycle life and wide operating temperature range. They have broad application prospects in national defense, railways, electric vehicle electronics, communications, aerospace and other fields. According to different energy storage mechanisms, supercapacitors can be divided into three categories: electric double layer capacitors based on porous carb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01G11/86H01G11/34H01G11/36H01G11/26H01G11/38H01G11/44
CPCY02E60/13H01G11/86H01G11/26H01G11/34H01G11/36H01G11/38H01G11/44
Inventor 李在均殷园园蔡金飞张明
Owner 江苏江大环保科技开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com