Special modified acrylic resin paint for building external walls

A technology of acrylic resin and building exterior walls, applied in the field of coatings, can solve the problems of unsatisfactory strength, aging resistance and water resistance, etc., and achieve poor stain resistance and aging resistance, long service life, and improved The effect of storage stability

Inactive Publication Date: 2015-05-20
安徽嘉年华漆业有限公司
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The strength, aging resistance and water resistance of the existing coatings for building exterior walls are not very satisfactory, and need to be improved to meet the requirements of a rapidly developing society

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021]The special modified acrylic resin coating for building exterior wall of the present invention, its raw material comprises the following components by weight: 70 parts of acrylic resin, 30 parts of fluorocarbon emulsion, 35 parts of nano-silica sol, 5 parts of light calcium carbonate, expanded leech 15 parts of stone, 5 parts of sepiolite, 15 parts of nano-titanium dioxide, 1 part of diatomaceous earth, 15 parts of water, 1 part of ethylene glycol, 2 parts of glycerin, 1.5 parts of polyethylene glycol, 2 parts of wetting agent, 0.3 parts of defoamer, 1.5 parts of 2-O-methylated-β-cyclodextrin, 0.1 part of 2,3,6-trimethoxy-β-cyclodextrin, 0.6 parts of surfactant, compound thickener 0.5 parts, 2 parts of film-forming aids.

Embodiment 2

[0023] The special modified acrylic resin coating for building exterior wall of the present invention, its raw material comprises the following components by weight: 85 parts of acrylic resin, 15 parts of fluorocarbon emulsion, 20 parts of nano-silica sol, 12 parts of light calcium carbonate, expanded leech 3 parts of stone, 20 parts of sepiolite, 5 parts of nano-titanium dioxide, 5 parts of diatomaceous earth, 5 parts of water, 3 parts of ethylene glycol, 0.5 parts of glycerol, 4 parts of polyethylene glycol, 0.8 parts of wetting agent, 1 part of defoamer, 0.2 part of 2-O-methylated-β-cyclodextrin, 1 part of 2,3,6-trimethoxy-β-cyclodextrin, 0.2 part of surfactant, compound thickener 2 parts, 0.3 parts of film-forming aid;

[0024] Wherein, the composite thickener is prepared according to the following process: dissolve 30 parts of acrylamide in 70 parts of water by weight, add 2 parts of attapulgite and stir evenly, then add 0.1 part of ammonium persulfate and 0.6 part of azo...

Embodiment 3

[0026] The special modified acrylic resin coating for building exterior wall of the present invention, its raw material comprises the following components by weight: 78 parts of acrylic resin, 26 parts of fluorocarbon emulsion, 27 parts of nano-silica sol, 8 parts of light calcium carbonate, expanded leech 13 parts of stone, 9 parts of sepiolite, 12 parts of nano-titanium dioxide, 2.5 parts of diatomaceous earth, 11 parts of water, 1.8 parts of ethylene glycol, 1.8 parts of glycerol, 2.5 parts of polyethylene glycol, 1.7 parts of wetting agent, 0.5 parts of defoamer, 1.3 parts of 2-O-methylated-β-cyclodextrin, 0.3 parts of 2,3,6-trimethoxy-β-cyclodextrin, 0.46 parts of surfactant, compound thickener 0.9 parts, 1.8 parts of film-forming aids;

[0027] Wherein, the average particle diameter of the nano-silica sol is 20nm; the surfactant is sodium dodecylsulfonate; The mixture of ratio; The defoamer is emulsified benzyl silicone oil;

[0028] The composite thickener is prepared...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
elongation at breakaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a special modified acrylic resin paint for building external walls, which is prepared from the following raw materials in parts by weight: 70-85 parts of acrylic resin, 15-30 parts of fluorocarbon emulsion, 20-35 parts of nano silica sol, 5-12 parts of light calcium carbonate, 3-15 parts of expanded vermiculite, 5-20 parts of meerschaum, 5-15 parts of nano titanium dioxide, 1-5 parts of kieselguhr, 5-15 parts of water, 1-3 parts of ethylene glycol, 0.5-2 parts of glycerol, 1.5-4 parts of polyethyleneglycol, 0.8-2 parts of wetting agent, 0.3-1 part of defoaming agent, 0.2-1.5 parts of 2-O-methylated-beta-cyclodextrin, 0.1-1 part of 2,3,6-trimethoxy-beta-cyclodextrin, 0.2-0.6 part of surfactant, 0.5-2 parts of composite thickener and 0.3-2 parts of film forming assistant. The special modified acrylic resin paint for building external walls has the advantages of high strength, excellent aging resistance, excellent water resistance and excellent heat-insulating property.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a special modified acrylic resin coating for building exterior walls. Background technique [0002] Exterior wall coatings are used to paint the exterior walls of buildings. The application environment is relatively harsh. Ultraviolet rays, heat energy, microorganisms, water, and air pollutants can all cause the aging of polymers in the coatings. Therefore, coatings for building exterior walls UV aging resistance, water resistance and self-cleaning properties are required. The strength, aging resistance and water resistance of the existing coatings for building exterior walls are not very satisfactory, and need to be improved to meet the requirements of a rapidly developing society. Contents of the invention [0003] The invention provides a special modified acrylic resin coating for building exterior walls, which has high strength, good aging resistance and water resistance,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D127/12C09D5/14C09D7/12
CPCC09D133/00C08K2201/011C08K2201/014C08L2205/025C08L2205/035C09D5/14C09D5/1681C09D7/61C09D7/63C08L27/12C08L71/00C08L5/16C08L83/04C08L33/26C08K13/02C08K3/36C08K2003/265C08K3/34C08K2003/2237C08K5/053C08K3/346
Inventor 张存标
Owner 安徽嘉年华漆业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com