Phosphorus-nitrogen-boron compounded system-containing timber fire retardant

A flame retardant and system technology, applied in wood treatment, wood impregnation, wood impregnation, etc., can solve the problems of poor compatibility, large amount of addition, adverse effects, etc., and achieve low hygroscopicity, simple preparation process, and dimensional stability convenient effect

Inactive Publication Date: 2015-05-27
高天红
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The currently used wood flame retardants can be divided into phosphorus flame retardants, halogen flame retardants, boron flame retardants, metal hydroxide flame retardants and combination flame retardants of various elements according to the effective flame retardant elements. Among these flame retardants, halogen flame retardants will produce a large amount of harmful gases when burned, which will have adverse effects on the human body and the environment, and have been gradually eliminated and banned; metal hydroxides such as aluminum hydroxide and magnesium hydroxide Flame retardants have not been widely used due to the large amount of addition and poor compatibility with organic substances; due to the advantages of phosphorus, nitrogen and boron multi-component composite systems, which are easily soluble in water and have good flame retardancy and smoke suppression, they are currently suitable for wood retardancy. Most of the flame retardants are phosphorus nitrogen boron flame retardants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The technical solutions of the present invention will be further described below in conjunction with specific preferred embodiments.

[0012] A kind of wood flame retardant containing phosphorus, nitrogen and boron compound system, its components are proportioned by mass percentage: phosphoric acid 33%, dicyandiamide 15%, boric acid 15%, triphenyl phosphate 15%, aluminum sulfate 10% , Ammonium molybdate 8%, Triethanolamine 3%, Pentaerythritol 1%. Wherein, the mass percent concentration of the phosphoric acid is 75%-85%.

[0013] Its preparation method is as follows: (1), weighing each component according to the mass percentage ratio; (2), mixing phosphoric acid and dicyandiamide, reacting at 90°C-130°C for 0.5-2 hours, and waiting for complete reaction and After converting into ureidophosphate, cool to room temperature, add boron compound, triphenyl phosphate, aluminum sulfate, ammonium molybdate, triethanolamine and pentaerythritol, mix well, then dry, crush and sieve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a phosphorus-nitrogen-boron compounded system-containing timber fire retardant. The phosphorus-nitrogen-boron compounded system-containing timber fire retardant comprises, by mass, 20-40% of phosphoric acid, 15-20% of dicyandiamide, 5-15% of a boron compound, 5-20% of triphenyl phosphate, 5-15% of aluminum sulfate, 5-10% of ammonium molybdate, 0.5-3% of triethanolamine and 0.1-1% of pentaerythritol. Phosphoric acid and dicyandiamide undergo an in situ reaction to produce carbamido phosphate, the carbamido phosphate is mixed with a boron compound, triphenyl phosphate and aluminum sulfate, and the mixture is added with ammonium molybdate as a smoke inhibition synergist, triethanolamine as a surfactant and pentaerythritol as a charring synergist so that the phosphorus-nitrogen-boron compounded system-containing timber fire retardant is obtained. The fire retardant has good fire retardant and smoke inhibiting effects, low hygroscopicity, good size stability and use convenience, does not contain halogen, satisfies environmental protection requirements and has anticorrosion and anti-moth functions.

Description

technical field [0001] The invention relates to the technical field of wood flame retardants, in particular to a wood flame retardant containing phosphorus, nitrogen and boron compound system. Background technique [0002] Wood is extremely flammable, and it is easy to cause a fire and cause damage to people and property. In order to reduce the risk of fire, the necessary fire-retardant treatment should be carried out on the wood. The currently used wood flame retardants can be divided into phosphorus flame retardants, halogen flame retardants, boron flame retardants, metal hydroxide flame retardants and combination flame retardants of various elements according to the effective flame retardant elements. Among these flame retardants, halogen flame retardants will produce a large amount of harmful gases when burned, which will have adverse effects on the human body and the environment, and have been gradually eliminated and banned; metal hydroxides such as aluminum hydroxide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/52
CPCB27K3/52B27K2240/30
Inventor 不公告发明人
Owner 高天红
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products