High-strength anti-ageing skid-proof conveying belt
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An anti-aging, conveyor belt technology, applied in the direction of conveyors, transportation and packaging, non-polymer adhesive additives, etc., can solve problems such as delamination, cross-cutting, and inability to adapt to such high requirements, and achieve heat resistance and wear resistance Etc. performance improvement, smoothing of glue, and improvement of appearance quality
Inactive Publication Date: 2015-06-03
QINGDAO ALLPOLY CONVEYOR BELT
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the current working conditions of domestic production enterprises cannot meet such high requirements, so problems such as delamination and cross-cutting of conveyor belts caused by long-term high-temperature operation often occur
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0013] A high-strength anti-aging anti-slip conveyor belt is characterized in that the components of the raw materials are composed as follows in parts by weight:
[0014] 35 parts of natural rubber, 15 parts of nitrile rubber, 2 parts of nano-scale activated clay, 10 parts of polyvinyl chloride resin, 2 parts of VP adhesive, 1.5 parts of plasticizer composed of plasticizer TMTD and plasticizer DNP according to 2:1 , 3 parts of calcium carbonate, 2 parts of stearic acid, 6 parts of carbon black N754, 6 parts of white carbon black, 1 part of coumarone, 4 parts of aromatic oil, 1 part of engine oil, 4 parts of sulfur, 1 part of antioxidant DFC.
Embodiment 2
[0016] A high-strength anti-aging anti-slip conveyor belt is characterized in that the components of the raw materials are composed as follows in parts by weight:
[0017] 38 parts of natural rubber, 18 parts of nitrile rubber, 3 parts of nano-scale activated clay, 13 parts of polyvinyl chloride resin, 3 parts of VP adhesive, 2 parts of plasticizer composed of plasticizer TMTD and plasticizer DNP according to 2:1 , 4 parts of calcium carbonate, 3 parts of stearic acid, 8 parts of carbon black N754, 8 parts of white carbon black, 2 parts of coumarone, 5 parts of aromatic oil, 1.2 parts of engine oil, 5 parts of sulfur, 2 parts of antioxidant DFC.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a high-strength anti-ageing skid-proof conveying belt. The high-strength anti-ageing skid-proof conveying belt is characterized by being prepared from the following raw materials in parts by weight: 30-40 parts of natural rubber, 15-20 parts of nitrile rubber, 2-3 parts of nanometer-grade active argil, 8-15 parts of polyvinyl chloride resin, 2-3 parts of a VP adhesive, 1.5-2 parts of a plasticizer, 2-4 parts of calcium carbonate, 2-4 parts of stearic acid, 6-10 parts of carbon black N754, 6-8 parts of white carbon black, 1-2 parts of coumarone, 4-5 parts of aromatic hydrocarbon oil, 1-1.2 parts of engine oil, 4-5 parts of sulfur and 1-2 parts of an anti-ageing agent. The high-strength anti-ageing skid-proof conveying belt disclosed by the invention is improved in appearance quality, and a damaged part is flatly replenished with the adhesive, so that the adhesion between frame canvases of the conveying belt maintains the properties of an original common heat-resisting conveying belt adhesive, the thermal oxidization and ageing resistance of the adhesive is enhanced; the performances such as tensile strength, layer-layer adhesion strength, heat resistance and wear resistance are all improved; the high-strength anti-ageing skid-proof conveying belt can be applied to large machineries for coal mines, stone materials and the like.
Description
technical field [0001] The invention belongs to the technical field of conveyor belt materials, and in particular relates to a high-strength anti-aging and anti-slip conveyor belt. Background technique [0002] The non-slip conveyor belt is carefully processed by polyester-cotton interweaving, EP, PP canvas through calendering, molding and vulcanization. The main feature is anti-slip, the anti-slip function is better, and the anti-slip conveyor belt is durable and has a long service life. There are mainly ordinary herringbone, convex herringbone, horizontal grid, round nail and other types. This product is suitable for conveying bulk, granular, bagged and powdered materials at a large inclination angle, such as coal, charcoal, wood, sand, cement bags, grain and other materials. Main application industries: tobacco, logistics, packaging, printing, food, wood, etc. The non-slip conveyor belt is used for conveying materials with a conveying angle of more than 17°. [0003] ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.