High-energy-density strontium bismuth titanate based composite ceramic and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high energy storage density, strontium bismuth titanate technology, applied in the field of dielectric energy storage ceramic materials, can solve the problems of low breakdown strength and achieve the effects of high density, fine and uniform grains, and low sintering temperature
Inactive Publication Date: 2015-06-17
GUILIN UNIV OF ELECTRONIC TECH
View PDF3 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Generally, ferroelectric ceramic dielectric materials have high dielectric constant but low breakdown strength. Therefore, finding a high energy storage density dielectric material with high dielectric constant while maintaining high breakdown strength is a current challenge.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0022] The preparation ingredients are: (1- x - y )Sr 1-1.5z( Bi 0.8 La 0.2 ) z TiO 3 - x (Bi 0.5 Na 0.5 ) 1-m Mg m TiO 3 - y Bi 0.5 Li 0.5 (Ti 0.92 mn 0.08 )
[0023] o 3 ,in x =0.7, y =0.1, z =0.1, m =0.05 high energy storage density strontium bismuth titanate based composite ceramic dielectric material,
[0024] The preparation method comprises the following steps:
[0025] (1) To analyze pure Bi 2 o 3 、Na 2 CO 3 , SrCO 3 , MgO, TiO 2 , Li 2 CO 3 , MnO 2 and La 2 o 3 As a raw material, according to the chemical formula (1- x - y )Sr 1-1.5z (Bi 0.8 La 0.2 ) z TiO 3 - x (Bi 0.5 Na 0.5 ) 1-m Mg m TiO 3 - y Bi 0.5 Li 0.5 (Ti 0.92 mn 0.08 )O 3 ( x =0.7, y =0.1, z =0.1, m =0.05), carry out batching, take dehydrated alcohol as the medium vibrating ball mill 24 hours, after drying in the crucible with 850 ℃ of pre-burning insulation 4 hours synthetic powder;
[0026] (2) After the powder is dried, add a 2% (weight percentage...
Embodiment 2
[0031] Composition expression is the same as embodiment 1:
[0032] The preparation ingredients are: (1- x - y )Sr 1-1.5z( Bi 0.8 La 0.2 ) z TiO 3 - x (Bi 0.5 Na 0.5 ) 1-m Mg m TiO 3 - y Bi 0.5 Li 0.5 (Ti 0.92 mn 0.08 )
[0033] o 3 ,in x =0.6, y =0.2, z =0.2, m =0.1 high energy storage density strontium bismuth titanate based composite ceramic dielectric material
[0034] The preparation method is the same as in Example 1, except that the pre-burning insulation is 900°C, and the performance is as shown in table 1
Embodiment 3
[0036] Composition expression is the same as embodiment 1:
[0037] The preparation ingredients are: (1- x - y )Sr 1-1.5z( Bi 0.8 La 0.2 ) z TiO 3 - x (Bi 0.5 Na 0.5 ) 1-m Mg m TiO 3 - y Bi 0.5 Li 0.5 (Ti 0.92 mn 0.08 )
[0038] o 3 ,in x =0.4, y =0.15, z =0.08, m =0.12 high energy storage density strontium bismuth titanate based composite ceramic dielectric material
[0039] The preparation method is the same as in Example 1, except that the pre-burning insulation is 800°C, and the performance is as shown in table 1
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
energy density
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses a high-energy-density strontiumbismuthtitanate based composite ceramic and a preparation method thereof. Constituents of the high-energy-density strontiumbismuthtitanate based composite ceramic are expressed by a general formula (1-x-y)Sr(1-1.5)z(Bi0.8La0.2)zTiO(3-x)(Bi0.5Na0.5)(1-m)MgmTiO(3-y)Bi0.5Li0.5(Ti0.92Mn0.08)O3, wherein x, y, z and m represent molar fractions; x is greater than or equal to 0.2 and less than or equal to 0.7; y is greater than or equal to 0.01 and less than or equal to 0.2; z is greater than or equal to 0.05 and less than or equal to 0.3; m is greater than or equal to 0.02 and less than or equal to 0.2. The high-energy-density strontiumbismuthtitanate based composite ceramic is prepared by adjusting the constituents to form a composite composition, and adopting microwavesintering to form a dense structure with uniform and small crystal grains, so as to keep a high dielectric constant and obtain a high withstand voltage. The preparation method disclosed by the invention is simple and stable in preparation process and suitable for industrial popularization and application. The high-energy-density composite ceramicdielectric material is excellent in energy storage characteristic and energy storage efficiency; the stored energy density can be up to 1.9 J / cm<3>; the energy storage efficiency can be up to 65%; the high-energy-density composite ceramicdielectric material is environment-friendly, low in loss and good in practicability.
Description
technical field [0001] The invention relates to a dielectric energy storage ceramic material, in particular to a strontium bismuth titanate-based composite ceramic with high energy storage density and a preparation method thereof. Background technique [0002] With the acceleration of economic growth in developing countries and the growing demand for energy, the problems of improving the efficiency of traditional energy utilization and expanding the practical scope of new energy have become increasingly prominent. Energy storage capacitors have the advantages of large discharge power, high utilization efficiency, large space for energy storage density increase, fast charge and discharge speed, anti-cycle aging, suitable for extreme environments such as high temperature and high pressure, and stable performance. They are gradually becoming the storage capacitors in pulse power equipment. Energy components are widely used in national defense and modern industrial fields such a...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 