Flame-retardant PVC injection molding material for branch cables and preparation method thereof

A branch cable and plastic injection technology, which is applied in the direction of plastic/resin/wax insulators, circuits, electrical components, etc., can solve the problems of rough and not fine injection molding surface, poor flame retardant effect, poor processing performance, etc., to achieve smooth and delicate surface, Excellent flame retardancy and low production cost

Active Publication Date: 2017-08-08
SHANGHAI KAIBO SPECIAL CABLE FACTORY
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the defects in the prior art that the products made of polyvinyl chloride injection plastics for branch cables have poor processability, rough and not fine injection molding surface, poor flame retardant effect and high production cost, and provide a Excellent injection molding processing performance, excellent flame retardant effect, low production cost, and the surface of the injection molded product is smooth and delicate, and a flame retardant PVC injection compound for branch cables with a temperature resistance of 70 or 90 ° C and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant PVC injection molding material for branch cables and preparation method thereof
  • Flame-retardant PVC injection molding material for branch cables and preparation method thereof
  • Flame-retardant PVC injection molding material for branch cables and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] 1. Experimental materials

[0025]

[0026] 2. Preparation method:

[0027] a. 100 kg of PVC resin, 50 kg of plasticizer a dioctyl phthalate, 5 kg of composite environmental-friendly heat stabilizer, 15 kg of plasticizer b52# chlorinated paraffin, 0.5 kg of polyethylene wax, and three 10 kg of antimony oxide, 0.8 kg of barium stearate, 0.5 kg of calcium stearate, 0.6 kg of stearic acid, 2 kg of ACR401 auxiliary agent, and 30 kg of industrial precipitated calcium carbonate were placed in a high-speed kneader and heated for high-speed stirring. The temperature of the kneader is controlled at 100-120°C, and the kneading time is 5-10 minutes;

[0028] b. The uniformly stirred raw materials are directly fed into the twin-screw feeder for extrusion, and the heating temperature of each section of the twin-screw feeder is equally divided from 120-160°C according to the number of heating sections;

[0029] c. The finished products of extruded materials are packaged and put ...

Embodiment 2

[0031] 1. Experimental materials

[0032]

[0033]

[0034] 2. Preparation method

[0035] Using the raw materials of this example, the method for preparing the flame-retardant PVC injection compound for branch cables is the same as that in Example 1.

Embodiment 3

[0037] 1. Experimental materials

[0038]

[0039] 2. Preparation method

[0040] Using the raw materials of this example, the method for preparing the flame-retardant PVC injection compound for branch cables is the same as that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention relates to a flame-retardant PVC injection molding material for a branch cable. The flame-retardant PVC injection molding material comprises the following raw materials by weight: 90 to 100 parts of PVC resin, 30 to 60 parts of a plasticizer a, 15 to 25 parts of a plasticizer b, 4 to 8 parts of a heat stabilizer, 8 to 15 parts of a fire retardant, 0.2 to 0.4 part of polyethylene wax, 0.5 to 1 part of a lubricant a, 0.2 to 0.5 part of a lubricant b, 0.3 to 0.8 part of a lubricant c, 2 to 3 parts of a processing modifier and 20 to 50 parts of a filler. The injection molding material has excellent injection molding performance, excellent flame retardation effect and low production cost; and an injection molding product has smooth and fine surface, and the temperature resistance grade of the product reaches 70 to 90 DEG C.

Description

technical field [0001] The invention relates to a cable injection compound and a preparation method thereof, in particular to a flame-retardant PVC injection compound for branch cables and a preparation method thereof. Background technique [0002] Because branch cables have the characteristics of excellent power supply reliability, good shock resistance, air tightness, waterproof, convenient construction, low environmental requirements, and maintenance-free, the application of branch cables in China has been rapidly promoted. With the acceleration of various infrastructure construction and real estate development in our country, the market has continuously increased the application types and performance requirements of branch cables. At present, although domestic manufacturers can prepare flame-retardant PVC injection molding materials for branch cables, the injection molding performance of the products is poor, the injection molding surface is rough and not delicate, the f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06H01B3/44C08K13/02B29B9/06B29C47/92B29C48/92
CPCB29B9/06B29C48/92B29C2948/92209C08K2201/014C08L27/06C08L2201/02C08L2201/08C08L2203/20C08L2205/035H01B3/443C08L91/06C08L23/06C08L33/04C08K13/02C08K5/12C08K3/2279C08K5/098C08K5/09C08K2003/265
Inventor 崔德刚魏国宝
Owner SHANGHAI KAIBO SPECIAL CABLE FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap