Firing technique of blue and white porcelain

A blue-and-white porcelain and craft technology, which is applied to clay products, other household appliances, household appliances, etc., can solve the problems of low firing temperature and inconsistent blue and white colors, reduce firing temperature, improve the bonding performance of blank-glaze, and improve surface gloss. degree of effect

Active Publication Date: 2015-07-08
潮州市华利达陶瓷制作有限公司
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a firing process of blue and white porcelain with low firing temperature, which can effectively avoid defects such as smoking, yellowing, and inconsistent blue and white color

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 1) Prepare blank, glaze and green material:

[0023] The blank is composed of the following raw materials in parts by weight: 30 parts of Nixing pottery clay, 8 parts of potassium feldspar, 5 parts of quartz, 1 part of calcined talc and 0.1 part of zirconium silicate; the Nixing pottery clay is composed of east mud and west mud , whose weight ratio is 10:0.1;

[0024] The glaze is composed of the following raw materials in parts by weight: 65 parts of lead-free cadmium frit, 10 parts of potassium feldspar, 6 parts of calcined talc, 25 parts of wollastonite, and 12 parts of Nixing pottery clay;

[0025] The green material is composed of the following raw materials by weight: 20 parts of blank, 10 parts of glaze and 70 parts of cobalt blue material; the cobalt blue material is composed of the following raw materials by weight: SiO 2 46, CoO 48;

[0026] 2) Prepare the green body: crush the green body and mix it, pass through a 220-mesh sieve to remove iron, press, smelt...

Embodiment 2

[0030] 1) Prepare blank, glaze and green material:

[0031] The blank is composed of the following raw materials in parts by weight: 50 parts of Nixing pottery clay, 15 parts of potassium feldspar, 12 parts of quartz, 5 parts of calcined talc and 0.5 part of zirconium silicate; the Nixing pottery clay is composed of east clay and west clay , whose weight ratio is 15:1;

[0032] The glaze is composed of the following raw materials in parts by weight: 65 parts of lead-free cadmium frit, 10 parts of potassium feldspar, 6 parts of calcined talc, 25 parts of wollastonite, and 12 parts of Nixing pottery clay;

[0033] The green material is composed of the following raw materials by weight: 20 parts of blank, 10 parts of glaze and 70 parts of cobalt blue material; the cobalt blue material is composed of the following raw materials by weight: SiO 2 52 parts, Fe 2 o 3 2 copies, 52 copies of CoO;

[0034] 2) Prepare the green body: crush the green body and mix it, pass through a 220...

Embodiment 3

[0038] 1) Prepare blank, glaze and green material:

[0039] The blank is composed of the following raw materials in parts by weight: 40 parts of Nixing pottery clay, 12 parts of potassium feldspar, 10 parts of quartz, 3 parts of calcined talc and 0.3 part of zirconium silicate; the Nixing pottery clay is composed of east mud and west mud , whose weight ratio is 10:1;

[0040] The glaze is composed of the following raw materials in parts by weight: 60 parts of lead-free cadmium frit, 8 parts of potassium feldspar, 4 parts of calcined talc, 20 parts of wollastonite, and 10 parts of Nixing pottery clay;

[0041] The blue material is composed of the following raw materials by weight: 15 parts of blank, 8 parts of glaze and 50 parts of cobalt blue material; the cobalt blue material is composed of the following raw materials by weight: SiO 2 50 parts, Fe 2 o 3 1 copy, 50 copies of CoO;

[0042] 2) Prepare the green body: crush the green body and mix it, pass through a 220-mesh s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a firing technique of blue and white porcelain, which comprises the following steps: 1) a blank is composed of Nixing argil, potash feldspar, quartz, calcined talcum and zirconium silicate; a glaze is composed of lead-free cadmium fusion cake, potash feldspar, calcined talcum, wollastonite and Nixing argil; and a blue material is composed of 10-20 parts of blank, glaze and a cobalt blue material; and 2) making the blank into a billet, trimming, drawing patterns or writing characters on the billet surface by sing the blue material, carrying out glazing treatment, airing, firing in a kiln at 1060-1160 DEG C for 10-15 hours, cooling, and discharging to obtain the finished product. The technique has the advantage of lower firing temperature. The finished blue and white porcelain product has the advantages of high glaze whiteness, bright blue-and-white coloration and clear lines without blooming, and is very delicate.

Description

technical field [0001] The invention relates to a manufacturing process of ceramics, in particular to a firing process of blue and white porcelain. Background technique [0002] Blue and white porcelain, also known as white ground blue and white porcelain, often referred to as blue and white porcelain, is one of the mainstream varieties of Chinese porcelain and belongs to underglaze colored porcelain. Blue-and-white porcelain is made of cobalt ore containing cobalt oxide as raw material. The blue-and-white porcelain body is painted with decorations, and then covered with a layer of transparent glaze. After high-temperature physical and chemical changes, the blue and white are consolidated between the glazes, which are not afraid of acid and alkali corrosion, are not easy to wear, never fade, and never peel off. Traditional blue and white pigments used to paint blue and white porcelain bodies need to be fired at high temperature for 18 to 24 hours before they can appear blue...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/22C04B33/24
Inventor 马健
Owner 潮州市华利达陶瓷制作有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com