Water-based elastic fluorocarbon paint and formula thereof

A technology of fluorocarbon paint and elasticity, applied in the direction of coating, etc., can solve the problems that restrict the promotion of fluorocarbon paint, achieve the effect of satisfying the appearance and service life, solving the problem of cracking, and high fracture degree

Inactive Publication Date: 2015-08-12
上海奥泽涂料有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since this type of coating is still a baking type coating, although the baking temperature is much lower than that of PTFE, about 230°C, it cannot be used on site and requires factory processing, which also restricts the further promotion of fluorocarbon coatings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The formula of the water-based elastic fluorocarbon paint described in the embodiments of the present invention, the adopted formula and its percentage weight are:

[0032] Water 20%-25%;

[0033] Dispersant 0.3%-0.5%;

[0034] Wetting agent 0.2%-0.3%;

[0035] Defoamer 0.3%-0.5%;

[0036] Rutile titanium dioxide 15%-20%;

[0037] Filler 15%-20%;

[0038] Multifunctional additives 0.2%-0.3%;

[0039] Coalescing agent 0.5%-1%;

[0040] Ethylene glycol 0.5%-1%;

[0041] Fluorocarbon emulsion 10%-15%;

[0042] Elastic emulsion 20%-30%;

[0043] Thickener 0.3%-0.5%;

[0044] Leveling agent 0.1%-0.3%.

[0045] The above water-based elastic fluorocarbon paint and formula thereof described in the embodiments of the present invention, the construction steps are:

[0046] ⑴Insulation base surface inspection: no hollowing, cracking, oil stains, do a good job of waterproofing and anti-cracking treatment on the edge of the window sill and the wall table, whether the mesh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a formula of a water-based elastic fluorocarbon paint. The formula comprises 20-25% of water, 0.3-0.5% of a dispersant, 0.2-0.3% of a wetting agent, 0.3-0.5% of an antifoaming agent, 15-20% of rutile titanium dioxide powder, 15-20% of a filling material, 0.2-0.3% of a multifunctional auxiliary agent, 0.5-1% of a coalescing agent, 0.5-1% of glycol, 10-15% of a fluorocarbon emulsion, 20-30% of an elastic emulsion, 0.3-0.5% of a thickening agent and 0.1-0.3% of a leveling agent. Long straight chain and low branched chain of a high-molecular elastic cross-linking agent react with a fluorine-containing polymer to form a highly-straight-chain and low-branched-chain polymer, the structure of which is jagged. The ultimate embodiment of properties is reflected in appropriate surface strength, excellent elasticity, telescopic springback function, high tensile strength and fracture resistance, low surface polarity and strong resistance to soiling and weatherability.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based elastic fluorocarbon paint and its formula that can be widely used in the fields of protection, decoration and decoration of interior and exterior walls, concrete surfaces, inorganic and organic material surfaces, and the like. Background technique [0002] The earliest "fluorocarbon coating" was born as early as 1938. It is the well-known DuPont Teflon coating, that is, polytetrafluoroethylene (PTFE), polyperfluoropropylene (FEP) and other copolymers. This kind of material is known as "corrosion-resistant, non-stick Teflon" due to its unique and excellent heat resistance (180°C-260°C), low temperature resistance (-200°C), self-lubrication and chemical stability. , Fluorocarbon paint is generally divided into trifluoro and tetrafluoro, tetrafluoro anti-corrosion performance is higher. Due to the extremely high liquefaction temperature required for use, the dispers...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D127/12C09D7/12
Inventor 杨和柏王波张锡芬李亚东吴海霞
Owner 上海奥泽涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com