A kind of glazed tile made of loess

A glazed tile and loess technology, used in clay products, applications, household appliances, etc., can solve the problems of insufficient smoothness, insufficient glaze gloss, cracked glaze, etc., to achieve a smooth and tidy surface, bright and bright colors, and improved smoothness. degree of effect

Inactive Publication Date: 2016-10-05
SINO RISING SUN CONSTR GRP
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Existing glazed tiles are usually fired with a mixture of various mud materials. The glaze layer is generally thick and produces stress. The quality is heavy, and it is easy to cause cracks and cracks on the glazed surface of the product.
Not smooth enough, and the mud is prone to pollution in the production process, high cost and energy consumption, the quality of the product is not stable enough, the gloss of the glaze is not enough, and the color is not rich and stable enough. Fades easily in sunlight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A glazed tile made of loess,

[0030] The glazed tile green body is composed as follows in parts by weight:

[0031] 110 parts of loess; 25 parts of high alumina bauxite; 9 parts of albite; 2 parts of quartz; 2 parts of fused magnesia; 2 parts of carbon fiber; 2 parts of phenolic resin; 2 parts of starch; 2 parts of rice husk;

[0032] This glazed tile glaze composition by weight is as follows,

[0033] Iron oxide yellow 45 parts; titanium dioxide 2 parts; feldspar powder 2 parts; nano zinc oxide 2 parts; silicon carbide 2 parts; carbon fiber 2 parts; tin dioxide 2 parts; TEOS 2 parts; polytetrafluoroethylene 2 parts;

[0034] The chemical composition of loess is: SiO2 55wt%, Al2O3 25wt%, Fe2O3 8%, CaO 7wt%, other components 5wt%.

[0035] The particle size of high alumina bauxite is less than 1 μm.

[0036] Its preparation method is as follows:

[0037] (1) Mixing: weighing, crushing and sieving the raw materials of the glazed tile body, adding water to mix, and ag...

Embodiment 2

[0043] A glazed tile made of loess,

[0044] The glazed tile green body is composed as follows in parts by weight:

[0045] 112 parts of loess; 26 parts of high alumina bauxite; 8 parts of albite; 2 parts of quartz; 4 parts of fused magnesia; 2 parts of carbon fiber; 4 parts of phenolic resin; 2 parts of starch; 2 parts of rice husk;

[0046] This glazed tile glaze composition by weight is as follows,

[0047] Iron oxide yellow 46 parts; titanium dioxide 2 parts; feldspar powder 2 parts; nano zinc oxide 2 parts; silicon carbide 2 parts; carbon fiber 2 parts; tin dioxide 2 parts; TEOS 2 parts; polytetrafluoroethylene 2 parts;

[0048] The chemical composition of loess is: SiO2 55wt%, Al2O3 25wt%, Fe2O3 8%, CaO 7wt%, other components 5wt%.

[0049] The particle size of high alumina bauxite is less than 1 μm.

[0050] Its preparation method is as follows:

[0051] (1) Mixing: weighing, crushing and sieving the raw materials of the glazed tile body, adding water to mix, and ag...

Embodiment 3

[0057] A glazed tile made of loess,

[0058] The glazed tile green body is composed as follows in parts by weight:

[0059] 109 parts of loess; 22 parts of high alumina bauxite; 9 parts of albite; 5 parts of quartz; 5 parts of fused magnesia; 5 parts of carbon fiber; 5 parts of phenolic resin; 5 parts of starch; 5 parts of rice husk;

[0060] This glazed tile glaze composition by weight is as follows,

[0061] Iron oxide yellow 42 parts; titanium dioxide 2 parts; feldspar powder 2 parts; nano zinc oxide 2 parts; silicon carbide 2 parts; carbon fiber 2 parts; tin dioxide 2 parts; TEOS 2 parts; polytetrafluoroethylene 2 parts;

[0062] The chemical composition of loess is: SiO2 55wt%, Al2O3 25wt%, Fe2O3 8%, CaO 7wt%, other components 5wt%.

[0063] The particle size of high alumina bauxite is less than 1 μm.

[0064] Its preparation method is as follows:

[0065] (1) Mixing: weighing, crushing and sieving the raw materials of the glazed tile body, adding water to mix, and agin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to glazed tile prepared from yellow soil. The green body of the glazed tile comprises yellow soil, high alumina bauxite, albite, quartz, fused magnesite, carbon fiber, phenol formaldehyde resin, starch and rice hull; glaze of the glazed tile comprises iron oxide yellow, titanium dioxide, feldspar powder, nano-zinc oxide, silicon nitride, carbon fiber, stannic oxide, TEOS and polytetrafluoroethylene. The glazed tile is smooth and clean in surface and bright in color, has good properties of crush resistance, fire resistance and acid and alkali resistance, and is light in mass, low in water absorption, good in breathability and low in cost.

Description

technical field [0001] The invention belongs to the field of glazed tiles, in particular to a glazed tile prepared from loess. Background technique [0002] Glazed tile is an ancient and traditional ceramic material in my country. With the development of tourism, people's demand for glazed tiles is also increasing, and their requirements are also getting higher and higher. [0003] Glazed tiles, solid materials, bright colors, and smooth glaze, have always been used as traditional Chinese building components. After successive developments and quality improvements, they have been widely used in modern buildings due to their various excellent functions. [0004] Existing glazed tiles are usually made by mixing and firing various mud materials. The glaze layer is generally thick and stress is generated, and the quality is heavy, which easily leads to defects such as cracks and chipping on the glazed surface of the product. Not smooth enough, and the mud is prone to pollution ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/04C04B33/13C04B33/34
Inventor 张国阳
Owner SINO RISING SUN CONSTR GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com