Medical low-temperature reversible temperature-indicating coating and preparation method thereof

A temperature-indicating coating and low-temperature technology, which is applied in the field of medical materials, can solve the problems of poor water resistance and dry-erase performance, and achieve the effects of good heat resistance, good brushability, and simple and easy-to-obtain raw materials

Inactive Publication Date: 2015-09-09
SUZHOU BEC BIOLOGICAL TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The invention provides a non-toxic, fast, simple and reliable medical low-temperature reversible temperature-indicating coating and a preparation method thereof, which solves technical problems such as poor water resistance and poor dry-erase performance of existing medical materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Step 1: Weigh 100 parts of epoxy-modified silicone resin, 5 parts of lead dioxide, 1 part of ethyl cellulose, 10 parts of cadmium carbonate, 15 parts of calcium fluoride, and 4 parts of talcum powder according to the ratio of parts by mass , 12 parts of barium sulfate, 1 part of Sudan orange, 0.5 part of titanium dioxide, and 1 part of red cyanine.

[0023] Step 2: Put epoxy-modified silicone resin, lead dioxide, ethyl cellulose, cadmium carbonate and talcum powder into the reaction kettle, and stir for 30 minutes at a speed of 400 r / min.

[0024] Step 3: Put the stirred liquid aside for 26 hours, add calcium fluoride, barium sulfate, Sudan orange, titanium dioxide and red cyanine, mix well, put it into a grinder and grind for 40 minutes.

[0025] The product is a reversible single color change at 70-90°C, the color changes from red to purple, and from purple to orange at 140-180°C; the product has a viscosity of 60s, water resistance 3d, no foaming, non-toxic, good hea...

Embodiment 2

[0027] Step 1: Weigh 100 parts of epoxy-modified silicone resin, 25 parts of lead dioxide, 20 parts of ethyl cellulose, 30 parts of cadmium carbonate, 35 parts of calcium fluoride, and 16 parts of talcum powder according to the ratio of parts by mass , 18 parts of barium sulfate, 5 parts of Sudan orange, 2.5 parts of titanium dioxide, and 3 parts of red cyanine.

[0028] Step 2: put epoxy-modified silicone resin, lead dioxide, ethyl cellulose, cadmium carbonate and talcum powder into the reaction kettle, and stir for 50 minutes at a speed of 600 r / min.

[0029] Step 3: Leave the stirred liquid to stand for 30 hours, add calcium fluoride, barium sulfate, Sudan orange, titanium dioxide and red cyanine, mix well, put it into a grinder and grind for 60 minutes.

[0030] The product is a reversible single color change at 70-90°C, the color changes from red to purple, and from purple to orange at 140-180°C; the product has a viscosity of 65s, a water resistance of 4d, no foaming, no...

Embodiment 3

[0032] Step 1: Weigh 100 parts of epoxy-modified silicone resin, 10 parts of lead dioxide, 5 parts of ethyl cellulose, 15 parts of cadmium carbonate, 20 parts of calcium fluoride, and 6 parts of talcum powder according to the ratio of parts by mass , 14 parts of barium sulfate, 2 parts of Sudan orange, 1 part of titanium dioxide, and 1.5 parts of red cyanine.

[0033] Step 2: Put epoxy-modified silicone resin, lead dioxide, ethyl cellulose, cadmium carbonate and talcum powder into the reaction kettle, and stir for 35 minutes at a speed of 450 r / min.

[0034] Step 3: Put the stirred liquid aside for 27 hours, add calcium fluoride, barium sulfate, Sudan orange, titanium dioxide and red cyanine, mix well, put it into a grinder and grind for 45 minutes.

[0035] The product is a reversible single color change at 70-90°C, the color changes from red to purple, and from purple to orange at 140-180°C; the product has a viscosity of 70s, water resistance of 5d, no foaming, non-toxic, g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a medical low-temperature reversible temperature-indicating coating and a preparation method thereof; raw materials comprise epoxy modified organic silicon resin, lead dioxide, ethyl cellulose, cadmium carbonate, calcium fluoride, a talcum powder, barium sulfate, Sudan orange, titanium dioxide and red cyanine; the product is in reversible single color change at the temperature of 70-90 DEG C, a color is turned from red to purple, and the color is turned from purple to orange at the temperature of 140-180 DEG C; the product has the viscosity of 60-80 s, is resistant to water for 3-7 d without blistering, is non-toxic and has good heat resistance, and the temperature measurement range is from room temperature to 200 DEG C; and temperature measurement is fast, simple and reliable, and the product can be widely produced and constantly replaces conventional materials.

Description

technical field [0001] The invention relates to the technical field of medical materials, in particular to a medical low-temperature reversible temperature-indicating coating and a preparation method thereof. Background technique [0002] Temperature-indicating paint, when the coating is heated to a certain temperature, the color or other phenomena change to indicate the surface temperature and temperature distribution of the object is called temperature-indicating paint, usually also called color-changing paint or heat-sensitive paint. Screen printing ink Screen printing type anti-counterfeiting ink can be used under 350 mesh, the pattern effect is good, smooth, and the color is full, and all the above-mentioned anti-counterfeiting materials can meet the requirements of silk screen printing. [0003] According to the stability of the color after the temperature-indicating coating changes color, it can be divided into reversible temperature-indicating coatings and irreversi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/06C09D7/12
Inventor 徐勤霞李苏杨
Owner SUZHOU BEC BIOLOGICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap