Special nonflammable atomization silicon oil for spinneret plates of chemical fiber factories and preparation method of special nonflammable atomization silicon oil

A technology of burning atomized silicone oil and spinneret, which is applied in the petroleum industry, base materials, additives, etc., can solve the problems of easy safety accidents and short duration of atomized silicone oil, so as to reduce potential safety hazards, reduce replacement and The number of sprays, the effect of good radiation resistance

Inactive Publication Date: 2015-09-09
DONGGUAN JIADAN LUBRICATE
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of this, the present invention aims at the deficiencies in the prior art, and its main purpose is to provide a non-flammable atomized silicone oil specially used for spinnerets in chemical fiber factories and its preparation method, which can effectively solve the problem of the existing atomized silicone oil. Short action time and easy to cause safety accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0016] A method for preparing nonflammable atomized silicone oil specially used for spinnerets in chemical fiber factories, comprising the following steps:

[0017] (1) Add polysiloxane resin, antioxidant, dispersant and preservative into the container, and use a high-speed disperser to mix evenly;

[0018] (2) Add phenyl silicone oil and continue stirring for 30-60 minutes, set aside;

[0019] (3) Fill and shape the above-mentioned prepared materials and R-134a propellant (ie 1,1,1,2-tetrafluoroethane) through an automatic filling machine, and put them into storage after passing the inspection.

Embodiment 1

[0022] A nonflammable atomized silicone oil specially used for spinnerets in chemical fiber factories, made of the following raw materials in parts by weight: polysiloxane resin 2%, phenyl silicone oil 96%, antioxidant 0.6%, dispersant 0.4% and Preservatives 1%. The antioxidant is alkylated diphenylamine, the dispersant is silicon dioxide, and the preservative is barium sulfonate.

[0023] A method for preparing nonflammable atomized silicone oil specially used for spinnerets in chemical fiber factories, comprising the following steps:

[0024] (1) Add polysiloxane resin, antioxidant, dispersant and preservative into the container, and use a high-speed disperser to mix evenly;

[0025] (2) Add phenyl silicone oil and continue to stir for 30 minutes, set aside;

Embodiment 2

[0028] A nonflammable atomized silicone oil specially used for spinnerets in chemical fiber factories, made of the following raw materials in parts by weight: polysiloxane resin 8%, phenyl silicone oil 90%, antioxidant 1%, dispersant 0.3% and Preservatives 0.7%. The antioxidant is 2,6-di-tert-butyl-p-cresol, the dispersant is silicon dioxide, and the preservative is barium sulfonate.

[0029] A method for preparing nonflammable atomized silicone oil specially used for spinnerets in chemical fiber factories, comprising the following steps:

[0030] (1) Add polysiloxane resin, antioxidant, dispersant and preservative into the container, and use a high-speed disperser to mix evenly;

[0031] (2) Add phenyl silicone oil and continue to stir for 35 minutes, set aside;

[0032] (3) Fill and shape the above-mentioned prepared materials and R-134a propellant (ie 1,1,1,2-tetrafluoroethane) through an automatic filling machine, and put them into storage after passing the inspection. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses special nonflammable atomization silicon oil for spinneret plates of chemical fiber factories and a preparation method of the special nonflammable atomization silicon oil. The special nonflammable atomization silicon oil is made of, by weight, 2%-8% of polysiloxane resin, 90%-97% of phenyl silicon oil, 0.1%-2% of antioxidants, 0.1%-0.4% of dispersant and 0.1%-1% of preservatives. By adoption of the polysiloxane resin, excellent film forming performance and adsorbability are achieved, a uniform film can be formed in each mesh of the spinneret plates. In addition, the phenyl silicon oil has excellent irradiation resistance performance, high oxidation stability, high heat resistance, high flame resistance, high ultraviolet resistance and high chemical resistance. By addition of the antioxidants including alkylated diphenylamine and 2, 6-butylated hydroxytoluene, high temperature performance is further improved, operation temperature requirements of the spinneret plates can be met completely, and service lives of products are long. Effects of current products on the market last for two hours by once spraying while effects of the special nonflammable atomization silicon oil last for six hours by once spraying, and accordingly replacement and spraying frequencies are reduced, and production efficiency is improved.

Description

technical field [0001] The invention relates to the technology in the field of silicone oil, in particular to a non-flammable atomized silicone oil specially used for spinnerets in chemical fiber factories and a preparation method thereof. Background technique [0002] The preparation of chemical fibers is usually made of natural or synthetic polymers or inorganic substances into a spinning melt or solution, then filtered, metered, extruded from a spinneret (plate) into a liquid stream, and then Solidified into fibers. The holes of the spinneret are usually sprayed with atomized silicone oil, so that the fibers formed by the spinning solution or melt from these microholes through final solidification or cooling are not easy to break. At present, the atomized silicone oils used in the market are filled with medium-viscosity dimethyl silicone oil or aralkyl silicone oil and propellant petroleum gas or dimethyl ether. The cost of this atomized silicone oil is low, but the pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10M107/50C10M161/00C10M155/02C10M133/12C10M129/16C10M131/04C10N30/10C10N30/12C10N30/08
Inventor 肖桦
Owner DONGGUAN JIADAN LUBRICATE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com