A method of preparing superhydrophobic self-cleaning surface of aluminum alloy by using short pulse laser

A short-pulse laser and aluminum alloy technology, which is applied in the field of surface modification of metal substrates, to achieve the effects of easy control of process parameters, convenient operation and stable performance

Active Publication Date: 2017-12-05
金顿激光科技(佛山)有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the difficulties and problems existing in the superhydrophobic and self-cleaning functions of the aluminum alloy surface prepared in the prior art, the purpose of the present invention is to provide a preparation of a multifunctional aluminum alloy surface with simple process, high processing efficiency, low cost and green environmental protection method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method of preparing superhydrophobic self-cleaning surface of aluminum alloy by using short pulse laser
  • A method of preparing superhydrophobic self-cleaning surface of aluminum alloy by using short pulse laser
  • A method of preparing superhydrophobic self-cleaning surface of aluminum alloy by using short pulse laser

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A method for preparing an aluminum alloy superhydrophobic self-cleaning surface using a short-pulse laser in this embodiment includes the following specific steps:

[0044] Step 1: Polish the 2a12 aluminum alloy to be processed, select a metallographic sample pre-grinding machine with a power of 370W, a grinding disc rotation speed of 450 rpm, and a grinding disc diameter of 230 mm. The polishing process requires an auxiliary diameter of 200 mm and 1000 mesh SiC water sandpaper is used to polish the surface of the aluminum alloy, and the polishing range is 100cm 2 , the polishing time is 10 minutes, and the aluminum alloy sample after surface polishing is obtained;

[0045] Step 2: Clean the aluminum alloy sample after the surface polishing described in step 1 with an ultrasonic cleaner. The ultrasonic frequency of the ultrasonic cleaner is 40 kHz, and the surface of the sample is submerged with deionized water with a resistivity of 18.25 megohms. Minutes, and then cle...

Embodiment 2

[0053] A method for preparing an aluminum alloy superhydrophobic self-cleaning surface using a short-pulse laser in this embodiment includes the following specific steps:

[0054] Step 1: Polish the 2a12 aluminum alloy to be processed, select a metallographic sample pre-grinding machine with a power of 370W, a grinding disc rotation speed of 450 rpm, and a grinding disc diameter of 230 mm. The polishing process requires an auxiliary diameter of 200 mm and 1000 mesh SiC water sandpaper is used to polish the surface of the aluminum alloy, and the polishing range is 100cm 2 , the polishing time is 10 minutes, and the aluminum alloy sample after surface polishing is obtained;

[0055] Step 2: Clean the aluminum alloy sample after the surface polishing described in step 1 with an ultrasonic cleaner, the ultrasonic frequency of the ultrasonic cleaner is 40 kHz, submerge the surface of the sample with deionized water with a resistivity of 18.25 megohm, and clean continuously at room ...

Embodiment 3

[0063] A method for preparing an aluminum alloy superhydrophobic self-cleaning surface using a short-pulse laser in this embodiment includes the following specific steps:

[0064] Step 1: Polish the 2a12 aluminum alloy to be processed, select a metallographic sample pre-grinding machine with a power of 370W, a grinding disc rotation speed of 450 rpm, and a grinding disc diameter of 230 mm. The polishing process requires an auxiliary diameter of 200 mm and 1000 mesh SiC water sandpaper is used to polish the surface of the aluminum alloy, and the polishing range is 100cm 2 , the polishing time is 10 minutes, and the aluminum alloy sample after surface polishing is obtained;

[0065] Step 2: Clean the aluminum alloy sample after the surface polishing described in step 1 with an ultrasonic cleaner, the ultrasonic frequency of the ultrasonic cleaner is 40 kHz, submerge the surface of the sample with deionized water with a resistivity of 18.25 megohm, and clean continuously at room ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
poweraaaaaaaaaa
energyaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a superhydrophobic self-cleaning surface of an aluminum alloy by using a short-pulse laser, and belongs to the technical field of surface modification of metal substrates. In this method, the aluminum alloy sample is first polished and pretreated, and then the surface of the sample is cleaned with deionized water and absolute ethanol respectively, and then dried with cold air or air-dried, and then the laser processing technology is used to adjust the relevant process parameters by using a short pulse laser. Surface treatment is carried out on the sample, and countless microstructures are processed on the surface of the sample. After the processing is completed, the processed sample is baked in an electric drying oven to obtain an aluminum alloy superhydrophobic self- Clean surface, which has very good superhydrophobic properties and excellent self-cleaning function. The preparation method of the invention has the advantages of simple process, convenient operation, high efficiency, less energy consumption, low cost, environmental protection and easy industrial application.

Description

Technical field: [0001] The invention belongs to the technical field of surface modification of metal substrates, and relates to a method for preparing a superhydrophobic self-cleaning surface on an aluminum alloy substrate. More specifically, the invention relates to a method for preparing an aluminum alloy superhydrophobic self-cleaning surface by using a short pulse laser . Background technique: [0002] In nature, many sciences and technologies currently used by human beings are inspired and enlightened from nature, and super-hydrophobic surfaces are a very common phenomenon in nature. For example, the surface of the lotus leaf has strong hydrophobicity and self-cleaning function. The revelation of the hydrophobicity of the lotus leaf surface to humans is mainly the study of superhydrophobicity, and self-cleaning is the result of superhydrophobicity. Therefore, the preparation of superhydrophobic surfaces on metal materials has attracted more and more attention. Due to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22F3/00
Inventor 吴颖刘顿赵城彼得·班尼特陈列翟中生娄德元杨奇彪关来庆
Owner 金顿激光科技(佛山)有限公司