Dry powder briquette adhesive, briquette including adhesive and preparation method of briquette

A technology of binder and briquette, applied in the preparation of briquette and briquette, and the field of dry powder briquette binder, can solve the problems of low cold and hot strength, large amount of addition, poor thermal stability, etc., and achieves cold and hot strength High, high ball formation rate, good waterproof effect

Active Publication Date: 2015-09-23
河北东慈环保科技有限公司
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the deficiencies such as large addition amount, low hot and cold strength, and poor thermal stability of the briquette binder in the prior art, the present invention provides a dry powder briquette binder, briquette and briquette containing the binder. preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] (1) Take 100kg of coal powder and 2.5kg of binder, wherein the binder is composed of the following components: 1.5kg of bentonite, 0.75 kg of oxidized starch, 0.0125kg of sodium carboxymethyl cellulose, 0.0125kg of polyvinyl alcohol, Sodium carbonate 0.025kg, calcium oxide 0.125kg, sodium chloride 0.075kg; mix the above raw materials evenly;

[0044] (2) Spray and add water to the mixture obtained in step (1), the amount of water added is 8kg, and stir while spraying;

[0045] (3) Send the mixed material processed in step (2) into a molding machine and extrude it under a pressure of 25MPa to obtain wet briquettes;

[0046] (4) Dry the wet briquette obtained in step (3) in a drying kiln at 100° C. to obtain a briquette product, and the water in the dried briquette product is 2% of the mass of coal powder.

[0047] The briquette product detection analysis result of embodiment 1 is as follows:

[0048] The average wet bulb strength is 83N / piece; the average cold strength...

Embodiment 2

[0050] (1) Take 100kg of coal powder and 2kg of binder, wherein the binder is composed of the following components: 1.2kg of bentonite, 0.56kg of oxidized starch, 0.01kg of sodium carboxymethyl cellulose, 0.01kg of polyvinyl alcohol, carbonic acid Sodium 0.02kg, calcium oxide 0.1kg, sodium chloride 0.1kg; mix the above raw materials evenly;

[0051] (2) Spray and add water to the mixture obtained in step (1), the amount of water added is 11kg, and stir while spraying;

[0052] (3) Send the mixture processed in step (2) into a molding machine and extrude it under a pressure of 20MPa to obtain wet briquettes;

[0053] (4) Dry the wet briquette obtained in step (3) in a drying kiln at 60° C. to obtain a briquette product, and the water in the dried briquette product is 3% of the mass of coal powder.

[0054] The briquette product detection analysis result of embodiment 2 is as follows:

[0055] The average wet bulb strength is 80N / piece; the average cold strength is 800N / piece;...

Embodiment 3

[0057] (1) Take 100kg of coal powder and 3kg of binder, wherein the binder is composed of the following components: 2.4kg of bentonite, 0.3kg of oxidized starch, 0.15kg of sodium carboxymethyl cellulose, 0.03kg of polyvinyl alcohol, carbonic acid Sodium 0.03kg, calcium oxide 0.06kg, sodium chloride 0.03kg; mix the above raw materials evenly;

[0058] (2) Spray and add water to the mixture obtained in step (1), the amount of water added is 7kg, and stir while spraying;

[0059] (3) Send the mixed material processed in step (2) into a molding machine and extrude it under a pressure of 28MPa to obtain wet briquettes;

[0060] (4) Dry the wet briquette obtained in step (3) in a drying kiln at 160° C. to obtain a briquette product, and the water in the dried briquette product is 1% of the mass of coal powder.

[0061] The briquette product detection analysis result of embodiment 3 is as follows:

[0062] The average wet bulb strength is 75N / piece; the average cold strength is 820N / ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a dry powder briquette adhesive, which is made by mixing the following raw materials in parts by weight: 40 to 85 parts of bentonite, 10 to 50 parts of oxidized starch, 0.1 to 5 parts of sodium chlorides, 0.1 to 1 part of polyvinyl alcohol, 0.1 to 5 parts of sodium carbonate, 1 to 10 parts of calcium oxides and 0.5 to 10 parts of sodium carboxymethylcellulose. The invention also relates to a briquette including the adhesive and a preparation method thereof. By using the dry powder briquette adhesive, the briquette including the adhesive and the preparation method thereof, the disadvantages that a briquette adhesive has a large addition amount and a briquette is low in cold and hot strength and poor in heat stability, and the like in the prior art are solved.

Description

technical field [0001] The invention belongs to the field of molded coal processing, and in particular relates to a dry powder molded coal binder, molded coal containing the binder and a preparation method of molded coal. Background technique [0002] Binders must be added to the production of briquettes, and the performance of the binders directly determines the quality of the briquettes. Binders are the core technology of the briquette technology; the current types of briquette binders can be divided into Organic, inorganic and compound three categories. Among them, the composite binder is composed of two or more organic and / or inorganic binders to make up for the deficiency of a single binder, so that the briquette can achieve better quality. [0003] However, the composition of the present composite binders varies greatly, and the difference in the composition has a great influence on the final quality of the briquette and the addition amount is also relatively large, u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10L5/14
Inventor 李晓东李慈
Owner 河北东慈环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap