Heat-proof chemical-resistant pad for laboratory table board

A chemical-resistant and laboratory countertop technology, which is applied in the field of heat-resistant and chemical-resistant laboratory countertop pads, can solve the problems of heat resistance and chemical resistance that cannot meet the requirements, and achieve excellent air tightness and fast vulcanization speed , Excellent cold resistance

Inactive Publication Date: 2015-10-21
ANHUI YUAN LAB EQUIP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of society, people have put forward higher requirements for the performance of laboratory countertops, and the heat resistance and chemical resistance of existing countertop pads can no longer meet the requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A heat-resistant and chemical-resistant laboratory table mat proposed by the present invention is made of a modified bromobutyl rubber material, wherein the raw materials of the modified bromobutyl rubber material include the following components by weight: 50 parts of bromobutyl rubber, 30 parts of epoxidized natural rubber, 10 parts of polytetrafluoroethylene, 35 parts of carbon black, 15 parts of modified graphene, 10 parts of aluminum oxide, 2 parts of magnesium oxide, 6 parts of zinc methacrylate 1.5 parts of zinc oxide, 5 parts of stearic acid, 0.2 parts of sulfur, 2.5 parts of brominated phenolic resin, 1 part of benzoyl peroxide, 5 parts of rosin, 2 parts of dioctyl phosphate, 2 parts of anti-aging agent 2246, anti-aging 4 parts of agent RD, 3 parts of accelerator DTDM;

[0033] Wherein, the modified graphene is prepared according to the following process:

[0034] S1. Introduce nitrogen into the reaction vessel, add 30 parts of tetraisopropyl titanate and 0.6 ...

Embodiment 2

[0037] A heat-resistant and chemical-resistant laboratory table mat proposed by the present invention is made of a modified bromobutyl rubber material, wherein the raw materials of the modified bromobutyl rubber material include the following components by weight: 70 parts of bromobutyl rubber, 10 parts of epoxidized natural rubber, 25 parts of polytetrafluoroethylene, 20 parts of carbon black, 30 parts of modified graphene, 5 parts of aluminum oxide, 6 parts of magnesium oxide, 2 parts of zinc methacrylate 3 parts of zinc oxide, 2 parts of stearic acid, 0.6 parts of sulfur, 1 part of brominated phenolic resin, 2 parts of benzoyl peroxide, 2 parts of rosin, 7 parts of dioctyl phosphate, 3 parts of antioxidant 4010NA, Agent DM 6 parts;

[0038] Wherein, the modified graphene is prepared according to the following process:

[0039] S1. Introduce nitrogen into the reaction vessel, add 40 parts of tetraisopropyl titanate and 0.2 parts of N,N-diethylhydroxylamine in parts by weigh...

Embodiment 3

[0042] A heat-resistant and chemical-resistant laboratory table mat proposed by the present invention is made of a modified bromobutyl rubber material, wherein the raw materials of the modified bromobutyl rubber material include the following components by weight: 60 parts of bromobutyl rubber, 25 parts of epoxidized natural rubber, 19 parts of polytetrafluoroethylene, 31 parts of carbon black, 21 parts of modified graphene, 9.2 parts of aluminum oxide, 3.9 parts of magnesium oxide, 4.6 parts of zinc methacrylate 2.3 parts of zinc oxide, 4 parts of stearic acid, 0.35 parts of sulfur, 2.2 parts of brominated phenolic resin, 1.4 parts of benzoyl peroxide, 4.2 parts of rosin, 3.8 parts of dioctyl phosphate, 5.6 parts of antioxidant MBZ, 2 parts of agent DM, 1 part of accelerator DPTT, 1.2 parts of accelerator ZDC, 1.4 parts of accelerator TMTD;

[0043] Wherein, the modified graphene is prepared according to the following process:

[0044] S1. Introduce nitrogen into the reactio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Strength retentionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a heat-proof chemical-resistant pad for a laboratory table board. The pad is made of a modified brominated butyl rubber material which comprises the following raw materials: brominated butyl rubber, epoxidized natural rubber, polytetrafluoroethylene, carbon black, modified graphene, aluminum oxide, magnesium oxide, zinc methacrylate, zinc oxide, stearic acid, sulfur, brominated phenolic resin, benzoyl peroxide, rosin, dioctyl phosphate, an antiager and an accelerator. The pad provided by the invention is high in strength and heat resistance, and excellent in chemical resistance and wear resistance.

Description

technical field [0001] The invention relates to the technical field of laboratory materials, in particular to a heat-resistant and chemical-resistant laboratory table mat. Background technique [0002] At present, all places where experiments need to be done in schools, scientific research institutes, factories and mines generally require experimental benches, which are mainly used for placing items and performing experimental operations. Traditional experimental benches are generally wooden experimental benches, reinforced concrete (marble) experimental benches, metal experimental benches or physical and chemical board experimental benches. However, because the equipment in the laboratory needs to face a variety of experimental environments, the existing various experimental benches have certain limitations in the process of use, such as poor heat resistance and chemical resistance, and short service life. The application of the test bench is limited. [0003] The laborat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L15/00C08L27/18C08L93/04C08L61/14C08K13/06C08K3/04C08K3/22C08K3/06C08K5/521C08K5/098C09C1/46C09C3/08
CPCC08L23/28C08L2201/08C08L2205/035C09C1/46C09C3/08C08L15/00C08L27/18C08L93/04C08L61/14C08K13/06C08K3/04C08K2003/2227C08K2003/222C08K2003/2296C08K3/06C08K5/521C08K5/098
Inventor 张然袁巍王跃
Owner ANHUI YUAN LAB EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com