Polybutylene terephthalate composite material and preparation method therefor

A polybutylene terephthalate and composite material technology, applied in the field of composite materials, can solve problems such as bending and deformation of materials, and achieve the effects of good fracture resistance, easy industrial production, and good mechanical strength

Inactive Publication Date: 2015-10-21
JIN BAOLI TECH SUZHOU
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to its excellent performance, it is widely used in the fields of automobiles, home appliance shells, mechanical equipment, precision instrument parts, electronic appliances, textiles, etc., but in the process of use, PBT materials need to have certain mechanical strength and relatively Good weather resistance, but the crystallization of PBT is very rapid, which easily leads to bending deformation of the material due to uneven cooling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) Weigh 80kg of polybutylene terephthalate, 8kg of polyalkylene glycol, 5kg of barium metaborate, 4kg of styrene oxide, 1kg of hydroxyethyldiethylenetriamine, 1kg of zirconium dioxide, Diphenylamine 1kg, polydimethylsiloxane diquaternary ammonium salt 0.5kg, mix well;

[0032] (2) Add the above components into a propulsion mixer and mix evenly, slowly add a mixture of 3kg of phenyl phosphate diglycidyl ester and 2kg of methyl isobutyl ketone, and add it to the twin-screw extruder, 15 kg of polyamide fibers with a diameter of 15 nanometers were added to the side feeding port, melted, extruded, dried, and pelletized to obtain a polybutylene terephthalate composite material.

[0033] The temperature of each section of the twin-screw extruder is as follows: the temperature of the first zone is 170°C, the temperature of the second zone is 200°C, the temperature of the third zone is 220°C, and the temperature of the fourth zone is 200°C.

[0034] The performance test re...

Embodiment 2

[0036] (1) Weigh 80kg of polybutylene terephthalate, 8kg of polyalkylene glycol, 5kg of barium metaborate, 4kg of styrene oxide, 1kg of hydroxyethyldiethylenetriamine, 1kg of zirconium dioxide, Diphenylamine 1kg, polydimethylsiloxane diquaternary ammonium salt 0.5kg, color powder 1kg and pentaerythritol stearate 1kg, mix well;

[0037] (2) Add the above components into a propulsion mixer and mix evenly, slowly add a mixture of 3kg of phenyl phosphate diglycidyl ester and 2kg of methyl isobutyl ketone, and add it to the twin-screw extruder, 15 kg of polyamide fibers with a diameter of 15 nanometers were added to the side feeding port, melted, extruded, dried, and pelletized to obtain a polybutylene terephthalate composite material.

[0038] The temperature of each section of the twin-screw extruder is as follows: the temperature of the first zone is 170°C, the temperature of the second zone is 200°C, the temperature of the third zone is 220°C, and the temperature of the fourth ...

Embodiment 3

[0041] (1) Weigh 88kg of polybutylene terephthalate, 14kg of polyalkylene glycol, 8kg of barium metaborate, 6kg of styrene oxide, 2kg of hydroxyethyldiethylenetriamine, 2kg of zirconium dioxide, Diphenylamine 2kg, polydimethylsiloxane diquaternary ammonium salt 2kg, color powder 1kg and pentaerythritol stearate 1kg, mix well;

[0042] (2) Add the above components into a propulsion mixer and mix evenly, slowly add a mixture of 8 kg of phenyl phosphate diglycidyl ester and 4 kg of methyl isobutyl ketone, and add it to the twin-screw extruder. 25 kg of polyamide fibers with a diameter of 18 nanometers were added to the side feeding port, melted, extruded, dried, and pelletized to obtain a polybutylene terephthalate composite material.

[0043] The temperature of each section of the twin-screw extruder is as follows: the temperature of the first zone is 190°C, the temperature of the second zone is 210°C, the temperature of the third zone is 230°C, and the temperature of the fourt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The present invention discloses a polybutylene terephthalate composite material and a preparation method therefor. The polybutylene terephthalate composite material is prepared by using the following components in parts by weight: 80-88 parts of polybutylene terephthalate, 15-25 parts of polyamide fiber, 8-14 parts of polyalkylene glycol, 5-8 parts of barium metaborate, 4-6 parts of styrene oxide, 3-8 parts of amino acid phenyl ester glycidyl, 2-4 parts of methyl isobutyl ketone, 1-2 parts of amino hydroxy ethyl diethylenetriamine, 1-2 parts of zirconium dioxide, 1-2 parts of diphenylamine and 0.5-2 parts of polydimethylsiloxane quaternary ammonium salt. The present invention also provides the preparation method for the polybutylene terephthalate composite material.

Description

technical field [0001] The invention belongs to the field of composite materials, in particular to a polybutylene terephthalate composite material and a preparation method thereof. Background technique [0002] Polybutylene terephthalate (PBT), also known as polytetramethylene terephthalate, is a polyester made by polycondensation of terephthalic acid and 1,4-butanediol. PBT is milky white translucent to opaque, semi-crystalline thermoplastic polyester. [0003] Polybutylene terephthalate is a common general-purpose resin. It has good comprehensive properties, is not resistant to strong acids and alkalis, can resist organic solvents, and is easy to decompose at high temperatures. However, due to its excellent performance, it is widely used in the fields of automobiles, home appliance shells, mechanical equipment, precision instrument parts, electronic appliances, textiles, etc., but in the process of use, PBT materials need to have certain mechanical strength and relatively...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L77/00C08L71/02C08L83/04C08K13/02C08K3/38C08K5/523C08K5/17C08K3/22C08K5/18C08K5/103B29C47/92B29C48/92
Inventor 李明华
Owner JIN BAOLI TECH SUZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap