Powder coating with metal flashing effect, as well as preparation method and application method of powder coating

A metal flash and powder coating technology, applied in powder coatings, polyester coatings, epoxy resin coatings, etc., can solve the problems of high cost, man-hours, high energy consumption, labor consumption, and weakened product competitiveness. The effect of reducing installation costs, saving energy consumption and reducing labor costs

Inactive Publication Date: 2015-11-11
SAIGAO POWDER TECH YANTAI
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this process method, the workpiece needs to be coated twice, baked twice and cooled twice, and the man-hours, energy consumption and labor consumption are very large, the cost is high, and the product competitiveness is weakened.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Powder coating with metal flashing effect, as well as preparation method and application method of powder coating
  • Powder coating with metal flashing effect, as well as preparation method and application method of powder coating
  • Powder coating with metal flashing effect, as well as preparation method and application method of powder coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The metal glitter effect powder coating described in the present embodiment is compounded by 3 components, and 3 components are respectively made of the raw materials of following percentage by weight:

[0042] A component:

[0043]

[0044] B component:

[0045] A component 94.5%;

[0046] Flake copper powder pigment 2.0%;

[0047] Mica titanium pearlescent pigment 3.5%;

[0048] C component:

[0049]

[0050] The preparation method is as follows:

[0051] (1) Preparation of component A: After fully mixing E-12, 6055, leveling agent 588, benzoin, permanent yellow, lemon orange, carbon black, rutile titanium dioxide and calcium carbonate, in a twin-screw extruder Melt and extrude at 100°C, after cooling and tableting, pulverize with a jet mill, separate with a multi-stage cyclone separator, and sieve with a rotary sieve to obtain powder particles with an average particle size of 15-40 μm, which is component A.

[0052] (2) Preparation of component B: mix fla...

Embodiment 2

[0058] The metal glitter effect powder coating described in the present embodiment is compounded by 3 components, and 3 components are respectively made of the raw materials of following percentage by weight:

[0059] A component:

[0060]

[0061] B component:

[0062] A component 94.5%;

[0063] Flake aluminum powder pigment 1.0%;

[0064] Mica titanium pearlescent pigment 4.5%;

[0065] C component:

[0066]

[0067] The preparation method is as follows:

[0068] (1) Preparation of component A: After fully mixing E-12, 6055, leveling agent 588, benzoin, carbon black, rutile titanium dioxide and calcium carbonate, melt extrude in a single-screw extruder at 90°C , after cooling and tableting, pulverize with a jet mill, separate through a single-stage cyclone separator, and sieve with a rotary sieve to obtain powder particles with an average particle size of 15-40 μm, which is component A.

[0069] (2) Preparation of component B: mix flake aluminum powder pigment and...

Embodiment 3

[0075] The metal glitter effect powder coating described in the present embodiment is compounded by 3 components, and 3 components are respectively made of the raw materials of following percentage by weight:

[0076] A component:

[0077]

[0078] B component:

[0079] A component 95.5%;

[0080] Mica titanium pearlescent pigment 4.5%;

[0081] C component:

[0082]

[0083]

[0084] The preparation method is as follows:

[0085] (1) Preparation of component A: After fully mixing E-12, 6055, leveling agent 588, benzoin, carbon black and calcium carbonate, melt and extrude in a twin-screw extruder at 80°C, cool and press Finally, pulverize with a jet mill, separate through a single-stage cyclone separator, and sieve with a rotary sieve to obtain powder particles with an average particle size of 15-40 μm, which is component A.

[0086] (2) Preparation of component B: mix the mica titanium pearlescent pigment with the component A prepared in step (1) in a bonding m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of functional powder coating, and particularly relates to powder coating with a metal flashing effect, as well as a preparation method and an application method of the powder coating. The powder coating is prepared by combining a composition A, a composition B and a composition C, wherein the composition A comprises the following raw materials in percentage by weight: 26.0-35.0% of bisphenol A-type ethoxyline resin, 32.5-42.0% of carboxyl terminated polyester resin, 0.5-1.0% of a leveling agent, 0.3-0.6% of a degassing agent, 2.0-33.5% of one or more pigments and 10-20.0% of a filler; the composition B comprises the following raw materials in percentage by weight: 90-99% of the composition A and 1-10% of one or more metal pigments; the composition C comprises the following raw materials in percentage by weight: 77.3-80.3% of GMA-type acrylic resin, 18.2-21.2% of dodecanedioic acid, 0.5-1% of the leveling agent and 0.3-0.6% of the degassing agent. A double-layer coating film is formed after application of the powder coating, so that the powder coating is high in impact resistance and bending resistance. The invention further provides the preparation method and the application method of the powder coating.

Description

technical field [0001] The invention belongs to the field of functional powder coatings, and in particular relates to a metallic glitter effect powder coating, a preparation method and an application method thereof. Background technique [0002] Metal glitter effect powder coating presents a multi-color effect metallic color due to the use of flake pigments such as copper powder, aluminum powder, and mica powder. exterior decoration. The use of flake pigments also brings the defect of poor rub resistance. The crux of the problem is that the flake pigments floating on the surface of the coating film to provide a metallic glitter effect are damaged by friction and the environment is eroded, and the coating film is prone to blackening. Phenomenon. For this reason, it is usually necessary to coat the surface with a transparent coating for protection. The usual practice is to coat a layer of transparent powder after the metal glitter effect coating is cured, and then cure agai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D163/00C09D167/00C09D7/12C09D5/03C09D5/46C09D5/36
Inventor 彭勇窦新鹏窦心涛
Owner SAIGAO POWDER TECH YANTAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap