Biodegradable solid particle emulsifier and papermaking sizing agent

A technology of solid particles and emulsifiers, applied in the directions of dissolution, addition of water repellents, chemical instruments and methods, etc., can solve the problems of large amount of particle components, low concentration of ASA emulsion, unfavorable emulsion storage, etc., and achieve high stability. , The effect of low emulsification cost and low dosage

Active Publication Date: 2015-11-18
山东熙来淀粉有限公司
View PDF8 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adverse effects brought by the surfactant cannot be completely avoided, and the addition of the particle component is too large, the concentration of the prepared ASA emulsion is very low, which is not conducive to the storage of the emulsion, and the hydrolysis of ASA is serious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Preparation of biodegradable solid particle emulsifiers (CPs): hydrolyze microcrystalline cellulose with 64% sulfuric acid solution at 45°C and 100 rpm magnetic stirring for 30 minutes, then centrifuge and wash to remove the remaining acid solution , and then through dialysis and ultrasonic treatment to obtain cellulose nanocrystal columnar particles. The cellulose nanocrystals with a length of 10-500nm and a width of 1-50nm are prepared with deionized water to form a cellulose nanocrystal solution with a mass fraction of 2%.

[0031]Dissolving polylactic acid-glycolic acid copolymer with a molecular weight of 92000-110000g / mol and an intrinsic viscosity of 0.9-1.3dL / g in chloroform to prepare a polylactic acid-glycolic acid copolymer-chloroform solution with a mass fraction of 5%; The polylactic acid-glycolic acid copolymer-chloroform solution was magnetically stirred for 2 hours, then mixed with water at a volume ratio of 1:1, and sheared and stirred for 15 minutes to...

Embodiment 2

[0035] The cellulose nanocrystals with a length of 10-500nm and a width of 1-50nm are prepared with deionized water to form a cellulose nanocrystal solution with a mass fraction of 2%.

[0036] The molecular weight is 92000-110000g / mol, the polylactic acid-glycolic acid copolymer that intrinsic viscosity is 0.9-1.3dL / g is dissolved in chloroform, is made into the polylactic acid-glycolic acid copolymer-chloroform solution that mass fraction is 3%, After magnetically stirring for 2 hours, mix with water at a volume ratio of 5:2, and shear and stir for 15 minutes to obtain a mixed liquid of polylactic acid-glycolic acid copolymer-chloroform-water, and to the obtained polylactic acid-glycolic acid copolymer- The chloroform-water mixed liquid is added with a mass fraction of 2% cellulose nanocrystal aqueous solution, wherein the volume ratio of the polylactic acid-glycolic acid copolymer-chloroform-water mixed liquid to the cellulose nanocrystal aqueous solution is 7:20, ultrasonic...

Embodiment 3

[0040] The cellulose nanocrystals with a length of 10-500nm and a width of 1-50nm are prepared with deionized water to form a cellulose nanocrystal solution with a mass fraction of 2%.

[0041] The molecular weight is 92000-110000g / mol, the polylactic acid-glycolic acid copolymer that intrinsic viscosity is 0.9-1.3dL / g is dissolved in chloroform, is made into the polylactic acid-glycolic acid copolymer-chloroform solution that mass fraction is 7%, After magnetic stirring for 2 hours, mix with water at a volume ratio of 5:1, and shear and stir for 15 minutes to obtain a mixed liquid of polylactic acid-glycolic acid copolymer-chloroform-water, and to the obtained polylactic acid-glycolic acid copolymer- The chloroform-water mixed liquid is added with a mass fraction of 2% cellulose nanocrystal aqueous solution, wherein the volume ratio of the polylactic acid-glycolic acid copolymer-chloroform-water mixed liquid to the cellulose nanocrystal aqueous solution is 7:20, ultrasonic vib...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a biodegradable solid particle emulsifier and a papermaking sizing agent and belongs to the technical field of papermaking sizing agents and related industrial emulsifiers. The biodegradable solid particle emulsifier short for CPs is prepared from cellulose nanocrystals and polylactic-co-glycolic acid. An ASA emulsion prepared from CPs is a Pickering emulsion, has the liquid drop particle size being about 3.4 mu m, has higher stability and cannot gather particles, precipitate or separate out water after being placed for 24 hours; the emulsion can still keep good performance of the papermaking sizing agent after being placed for 3 hours; the preparation process is simple, few emulsifiers are used, the emulsification cost is low, and the emulsifier has biodegradability and has little pollution to the environment.

Description

technical field [0001] The invention relates to a biodegradable solid particle emulsifier and a papermaking sizing agent, belonging to the technical field of papermaking sizing agents and related industrial emulsification. Background technique [0002] Water-insoluble papermaking sizing agents need to be emulsified into oil-in-water emulsions to be compatible with papermaking systems that use water as the medium. In recent years, ASA sizing agent has been widely used in high-grade paper and cardboard internal sizing due to its high reactivity, low sizing material cost and fast aging rate, especially for large high-speed paper machines with in-machine coating. . However, ASA is a highly reactive paper-making neutral sizing agent, and its hydrolysis speed is very fast. After its emulsion is stored at room temperature for more than 1 hour, the sizing effect will decrease, and the hydrolyzate will cause obstacles to papermaking and reduce sizing efficiency. Therefore, when usi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01F17/52B01F17/00D21H21/16C09K23/52C09K23/00
Inventor 于得海刘温霞王慧丽李国栋宋兆萍
Owner 山东熙来淀粉有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com