Oxidation-resistant material and method employing same for preparing tantalum-tungsten alloy anti-oxidation coating

A technology of anti-oxidation coating, tantalum-tungsten alloy, applied in the direction of metal material coating process, coating, etc., to achieve the effect of strong continuous static load oxidation resistance

Active Publication Date: 2015-12-02
NINGXIA ORIENT TANTALUM IND +1
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But so far, there is no coating material that has good compatibility with tantalum-tungsten alloys, a wide range of anti-oxidation working temperature, and excellent anti-oxidation ability in high and low temperature environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oxidation-resistant material and method employing same for preparing tantalum-tungsten alloy anti-oxidation coating
  • Oxidation-resistant material and method employing same for preparing tantalum-tungsten alloy anti-oxidation coating
  • Oxidation-resistant material and method employing same for preparing tantalum-tungsten alloy anti-oxidation coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] 1) Two groups of high-temperature anti-oxidation materials are:

[0053] ①Cr is 5Wt%, Fe is 3Wt%, Ti is 2Wt%, Y 2 o 3 2Wt%, W is 1Wt%, HfO 2 5Wt%, Nb is 3Wt%, SiC is 2.8Wt%, B is 1.2Wt, and the balance is Si;

[0054] ②Mo is 7.2Wt%, W is 2.2Wt%, Nb is 3Wt%, Y is 2Wt%, HfO 2 4wt%, B 2 o 3 is 1.2wt%, BaO is 0.8wt%, Ta is 0.6wt%, and the balance is Si.

[0055] Mix the above two groups of materials evenly in proportion, use a planetary ball mill to grind them into powders of no more than 300 mesh at high speed, and put them into two different containers;

[0056] 2) In the ① group antioxidant material (powder), add respectively the nitro varnish (Hangzhou Paint Co., Ltd., Pagoda brand nitro varnish) of powder quality 80Wt% and the NaF of 3Wt% as binding agent and catalyst, then add powder Ethyl acetate with twice the volume was used as a carrier, mixed evenly, ball milled with corundum beads at a speed of 150r / min for 8h, and then made into a slurry. Coat the slurr...

Embodiment 2

[0068] 1) Two groups of high-temperature anti-oxidation materials are:

[0069] ①Cr is 3Wt%, Ti is 5Wt%, Y 2 o 3 2Wt%, W is 1.5Wt%, Nb is 3Wt%, HfO 2 3wt%, MoSi 2 is 2.5Wt%, S is 1Wt%, and the balance is Si;

[0070] ② Mo is 6.2Wt%, W is 3Wt%, Nb is 3Wt%, Y is 1.8Wt%, HfO 2 4wt%, Al 2 o 3 3.5wt%, B 2 o 3 is 1.2wt%, BaO is 0.8wt%, Ta is 2.2wt%, and the balance is Si.

[0071] Mix the above two groups of materials evenly in proportion, use a planetary ball mill to grind them into powders of no more than 300 mesh at high speed, and put them into different containers;

[0072] 2) Add 120Wt% nitro varnish (Zhejiang Paint Co., Ltd., Pagoda brand nitro varnish) and 3Wt% NH varnish respectively to the ① group antioxidant material 4 Cl was used as a binder and a catalyst, and ethyl acetate twice the volume of the powder was added as a carrier. After mixing evenly, ball milling with corundum beads at a speed of 150r / min for 8 hours was used to make a slurry. Coat the slurry e...

Embodiment 3

[0076] 1) Two groups of high-temperature anti-oxidation materials are:

[0077] ①Cr is 5Wt%, Ti is 2Wt%, Y 2 o 3 2Wt%, W is 0.5Wt%, Nb is 1.8Wt%, HfO 2 3.5wt%, TiB 2 is 0.25Wt%, Ir is 0.5%, and the balance is Si;

[0078] ②Mo is 7.2Wt%, W is 2Wt%, Nb is 2.2Wt%, Y is 1.5Wt%, HfO 2 4Wt%, La 1.2Wt%, B 2 o 3 is 3.7wt%, BaO is 0.8wt%, V is 0.8wt%, and the balance is Si.

[0079] Mix the above two groups of materials evenly in proportion, use a planetary ball mill to grind them into powders of no more than 300 mesh at high speed, and put them into different containers;

[0080] 2) Add polyethylene glycol (Tianjin Kemiou Co., Ltd., analytically pure grade, polyethylene glycol 3000-8000) with a powder mass of 3Wt% to the anti-oxidation material in group ① as a binder, and add 1.2Wt % NH 4 Cl and 1.8wt% NaF were used as catalysts, and ethyl acetate twice the volume of the powder was added as a carrier. After mixing evenly, ball milling with corundum beads at a speed of 180r / mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an oxidation-resistant material and a method employing the same for preparing a tantalum-tungsten alloy anti-oxidation coating. The oxidation-resistant material is characterized by comprising a first anti-oxidation material and a second anti-oxidation material, wherein the first anti-oxidation material comprises 1-5wt% of Cr, 1-5wt% of Ti, 0.1-2wt% of Y2O3, 0.5-3wt% of W, 0.5-3wt% of Nb, 1-5wt% of HfO2, and the balance Si; the second anti-oxidation material comprises 6-15wt% of Mo, 0.5-3wt% of W, 0.5-3wt% of Nb, 0.3-2.2wt% of Y, 1-5wt% of HfO2, and the balance Si. The tantalum-tungsten alloy anti-oxidation coating prepared by the method has a wide operating temperature range, and is high in continuous static load and antioxidant capacities, and is particularly suitable for high-temperature structural components such as a thrust chamber, a nozzle jet, a front edge and a guide tube of an airspace engine.

Description

technical field [0001] The invention relates to an anti-oxidation material and a method for preparing an anti-oxidation coating of a tantalum-tungsten alloy by using it. Background technique [0002] Tantalum-tungsten alloy is an important member of the tantalum-based alloy family. Its melting point is as high as 3000°C and has excellent high-temperature mechanical properties. It also has good welding performance and high-temperature creep resistance. It has the potential to become a new generation of high-temperature structural materials for aerospace and aero engines. necessary condition. However, tantalum-tungsten alloys, like C103, TZM and other refractory metal alloy materials, will fail to pulverize due to "pest" oxidation at temperatures above 500 ° C, so anti-oxidation protection must be implemented for them. [0003] Common anti-oxidation protection methods for refractory metal materials include alloying protection and coating protection. Alloying protection can i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C30/00C22C32/00C22C30/00C22C28/00
Inventor 赵刚周小军罗文王立斐韩建川王蓉杜宝盈田进鹏杨国启
Owner NINGXIA ORIENT TANTALUM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More