Nickel slag aerated concrete and preparation method thereof

A technology of aerated concrete and nickel slag, applied in the field of building materials, can solve the problems of land occupation of nickel-iron alloy slag, efficient resource utilization of environmental pollution, etc., to alleviate land occupation and environmental pollution, low water absorption, and promote development Effect

Inactive Publication Date: 2015-12-09
武汉天沭除尘设备有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a nickel slag aerated concrete and its preparation process, aiming to solve the p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of nickel slag aerated concrete of the present invention, the design dry apparent density is 600kg / m 3 ;

[0034] The design ratio of each component according to the weight ratio is: cement 20wt%, nickel slag fine powder 30wt%, quicklime 15wt%, machine-made sand 27wt%, gypsum 2wt%, waste fine powder 6wt%;

[0035] After the components are mixed, stir them evenly in a mortar mixer, then add 65°C hot water with a water-to-material ratio of 0.57, 1.0% admixture, and stir quickly for 2 minutes; continue to add the aqueous solution prepared by 0.10wt% aluminum powder paste, and stir quickly for 20 seconds , quickly poured into the triple mold;

[0036] Put the mold in a curing box at 50°C for 6 hours, and after cutting, put it into an autoclave for curing under 175°C and 0.8 MPa for 10 hours; Dry in a blast drying oven at 95°C for 20 hours;

[0037] After drying, the average absolute dry apparent density of each block is 621.2kg / m 3 , The average compressive stren...

Embodiment 2

[0039] A kind of nickel slag aerated concrete of the present invention, the design dry apparent density is 600kg / m3 ;

[0040] The design ratio of each component according to the weight ratio is: cement 10wt%, nickel slag fine powder 50wt%, quicklime 15wt%, machine-made sand 19wt%, gypsum 1wt%, waste fine powder 5wt%;

[0041] After the components are mixed, stir them evenly in a mortar mixer, then add 65°C hot water with a water-to-material ratio of 0.57, 1.0% admixture, and stir quickly for 2 minutes; continue to add the aqueous solution prepared by 0.10wt% aluminum powder paste, and stir quickly for 20 seconds , quickly poured into the triple mold;

[0042] Put the mold in a curing box at 50°C for 6 hours, and after cutting, put it into an autoclave for curing under autoclaving at 185°C and 1.1MPa for 8 hours; Dry in a blast drying oven at 95°C for 20 hours;

[0043] After drying, the average absolute dry apparent density of each block is 615.4kg / m 3 , The average compre...

Embodiment 3

[0045] A kind of nickel slag aerated concrete of the present invention, the design dry apparent density is 600kg / m 3 ;

[0046] The design ratio of each component by weight is: 10wt% of cement, 45wt% of nickel slag powder, 20wt% of quicklime, 19wt% of machine-made sand, 2wt% of gypsum, and 4wt% of waste powder;

[0047] After the components are mixed, stir them evenly in a mortar mixer, then add 65°C hot water with a water-to-material ratio of 0.57, 1.0% admixture, and stir quickly for 2 minutes; continue to add the aqueous solution prepared by 0.10wt% aluminum powder paste, and stir quickly for 20 seconds , quickly poured into the triple mold;

[0048] Put the mold in a curing box at 50°C for 6 hours, and after cutting, put it into an autoclave for curing under autoclaving at 185°C and 1.1MPa for 8 hours; Dry in a blast drying oven at 95°C for 20 hours;

[0049] After drying, the average absolute dry apparent density of each block is 611.1kg / m 3 , The average compressive ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apparent densityaaaaaaaaaa
Apparent densityaaaaaaaaaa
Apparent densityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of building material, and more specifically relates to a nickel slag aerated concrete and a preparation method thereof. The nickel slag aerated concrete comprises following main ingredients: a siliceous material, a calcareous material, a foaming agent, an additive, a conditioning agent, and water; the siliceous material comprises nickel slag micro powder, machine-made sand, and a waste material micro powder; the calcareous material comprises cement and quick lime; the foaming agent is aluminum paste; the conditioning agent is dihydrate gypsum; and the additive comprises triethanolamine, oleic acid, and water. The nickel slag aerated concrete is high in strength, excellent in thermal insulation performance, and low in water absorption; a large amount of ferronickel alloy slag can be recycled; industrial solid waste resource utilization is realized; resources are saved; the ecological environment is protected; added economic value is high; and the preparation method accords with the development direction of novel building wall materials at present.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a nickel slag aerated concrete and a preparation process thereof. Background technique [0002] Nickel-iron alloy submerged arc slag is a kind of industrial waste slag discharged in the process of smelting metal nickel, and the slag content accounts for about 80% to 90% of the raw materials. With the increasing demand and production scale of nickel-iron alloy in my country, the accumulation of a large amount of nickel slag has become an important problem for the development of enterprises. Nickel slag is weak acid slag, with FeO, MgO, Al 2 o 3 , SiO 2 As the main component, the main mineral phases are pyroxene, forsterite, copper nickel iron sulfide, a small amount of tricalcium silicate, dicalcium silicate and other mineral phases and more amorphous substances, with certain gelling activity . Due to high temperature thermal history, cooling effect, chemical composition and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/02C04B28/10C04B18/14
CPCY02W30/91
Inventor 田键申盛伟
Owner 武汉天沭除尘设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap