A kind of foaming master batch for ABS microcellular foaming material and preparation method thereof

A foaming masterbatch and microporous material technology, applied in the field of foaming masterbatch and its preparation, to achieve high compatibility, saving ABS raw materials, and low equipment requirements

Active Publication Date: 2017-11-28
GUIZHOU MATERIAL IND TECH INSTITUE
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Document 2 "Patent Application No. 201310315454.3 Chinese Patent" discloses a foaming masterbatch for microcellular foaming of polystyrene. The foaming masterbatch involved in this invention is also not suitable for the micropores of ABS and its composite materials. foaming

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of foaming master batch for ABS microcellular foaming material and preparation method thereof
  • A kind of foaming master batch for ABS microcellular foaming material and preparation method thereof
  • A kind of foaming master batch for ABS microcellular foaming material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) First, mix 45 parts of ABS, 4 parts of zinc oxide, 0.75 parts of zinc stearate and 0.25 parts of white oil in a mixer, and then use a twin-screw extruder to extrude and granulate. The barrel temperature is 190- 200°C, screw speed 200r / min;

[0025] (2) After mixing 39.8 parts of SBS, 9.95 parts of azodicarbonamide with a particle size of 1-20 μm, and 0.25 parts of white oil in a mixer, extrude and granulate with a twin-screw extruder. 125-145°C, screw speed 150r / min;

[0026] (3) Take the pellets in the above step (1) and the pellets in step (2), mix them evenly, and extrude pellets in the twin-rotor continuous kneader and single-screw extruder unit. The barrel temperature 100-120°C, screw speed 120r / min, to obtain foam masterbatch.

[0027] (4) After blending the foam masterbatch and ABS obtained in the above step (3) evenly at a weight ratio of 1:9, prepare a standard sample on the injection molding machine, and the performance test results are shown in Table 1....

Embodiment 2

[0029] (1) First, mix 29.8 parts of ABS, 2.76 parts of zinc oxide, 0.57 parts of zinc stearate and 0.17 parts of DOP in a mixer, and then extrude and granulate with a twin-screw extruder. The barrel temperature is 190-210 °C, screw speed 200r / min;

[0030] (2) After mixing 53.1 parts of SBS, 13.27 parts of azodicarbonamide with a particle size of 1-20 μm, and 0.33 parts of DOP in a mixer, extrude and granulate with a twin-screw extruder at a barrel temperature of 125 -145℃, screw speed 150r / min;

[0031] (3) Take the pellets in the above step (1) and the pellets in step (2), mix them evenly, and extrude pellets in the twin-rotor continuous kneader and single-screw extruder unit. The barrel temperature 110-130°C, screw speed 120r / min, to obtain foam masterbatch.

[0032] (4) After blending the foam masterbatch and ABS obtained in the above step (3) at a weight ratio of 3:17, prepare a standard sample on the injection molding machine, and the performance test results are shown i...

Embodiment 3

[0034] (1) First, mix 29.8 parts of ABS, 2.76 parts of zinc oxide, 0.57 parts of zinc stearate and 0.17 parts of white oil in a mixer, and then use a twin-screw extruder to extrude and granulate. The barrel temperature is 190- 200°C, screw speed 200r / min;

[0035] (2) Mix 59.7 parts of HIPS, 6.64 parts of azodicarbonamide with a particle size of 1-20 μm, and 0.36 parts of white oil in a mixer, and then use a twin-screw extruder to extrude and granulate. 110-130°C, screw speed 150r / min;

[0036] (3) Take the pellets in the above step (1) and the pellets in step (2), mix them evenly, and extrude pellets in the twin-rotor continuous kneader and single-screw extruder unit. The barrel temperature 100°C, screw speed 100-120r / min, to obtain foam masterbatch.

[0037] (4) After blending the foam masterbatch and ABS obtained in the above step (3) at a weight ratio of 3:17, prepare a standard sample on the injection molding machine, and the performance test results are shown in Table ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a foaming masterbatch for ABS microporous materials and a preparation method thereof. The foaming masterbatch consists of 20-70 parts of polymer carrier, acrylonitrile-butadiene-styrene copolymer (ABS resin) 15-60 parts, 2-20 parts of blowing agent, 1-7 parts of activator, 0.1-1 part of lubricant, firstly, ABS resin, activator and lubricant are mixed and granulated; secondly, polymer carrier, Foaming agent and lubricant are mixed and granulated; finally, the obtained two kinds of granules are granulated in a twin-rotor continuous mixer and a single-screw extruder unit to obtain foaming masterbatch. The masterbatch prepared by the present invention has high compatibility with ABS and ABS-based composite materials, and the foaming agent can be better dispersed in the matrix material, and the resulting cell structure is more uniform and dense, and can obtain small size and uniform distribution. It saves the amount of ABS while maintaining the cell structure with high cell density, and is especially suitable for large-scale industrial production.

Description

technical field [0001] The invention relates to a foaming masterbatch and a preparation method thereof, in particular to a foaming masterbatch for acrylonitrile-butadiene-styrene copolymer (ABS) microcellular foaming materials and a preparation method thereof The invention belongs to the technical field of microporous foam materials. Background technique [0002] ABS is a copolymer grafted from polybutadiene rubber, monomer styrene and acrylonitrile. It has impact resistance, low temperature resistance, excellent insulation performance, good surface gloss, easy to paint and color, etc. Advantages, mainly used in machinery, automobiles, building materials and electronics, electrical industries. [0003] Compared with unfoamed materials, the density of foamed plastics can be reduced by 5% to 95%, thereby reducing raw material consumption and cost. At the same time, it has the advantages of good sound insulation and heat insulation performance, shock load absorption, good cush...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L53/02C08L51/04C08L55/02C08L91/00C08K13/02C08K3/22C08K5/098C08K5/12C08J9/10
Inventor 张翔蒋团辉龚维何力王醴均黄斌
Owner GUIZHOU MATERIAL IND TECH INSTITUE