Composite slag lotion for electric furnace and converter and preparation method thereof

A technology for compounding slag and lotion, applied in the field of metallurgical auxiliary materials, can solve the problems of low slag basicity, long slag-forming time, and increased acid-soluble aluminum content, and achieve the advantages of reducing refining procedures, reasonable component composition, and reducing smelting costs. Effect

Active Publication Date: 2017-09-15
HENAN TONGYU METALLURGY MATERIALS GRP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Or compounding, the oxygen potential in the molten steel cannot be effectively reduced after adding the alloy, and it is necessary to add deoxidized alloys such as ferrosilicon, aluminum, silicon-aluminum-barium-calcium during use, resulting in too low alkalinity in the slag and acid in the molten steel Increased dissolved aluminum content is unfavorable to desulfurization function and adsorption inclusion effect
If lime and desulfurization materials are added in the later refining process, the amount of slag will increase and the slagging time will be too long, which will increase the cost of smelting and the pollution of the environment and molten steel by additional components, and the slag has no dephosphorization and phosphorus-fixing elements, which cannot be achieved. The effect of dephosphorization needs to be dephosphorized during the pretreatment of molten iron
The above-mentioned defects are extremely unfavorable to the current steel situation and the development of high-end varieties of steel. It is necessary to convert the material components of the original refining agent and slag washing agent to solve the current use defects and meet the current cost and various components of molten steel. Control Index Requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite slag lotion for electric furnace and converter and preparation method thereof
  • Composite slag lotion for electric furnace and converter and preparation method thereof
  • Composite slag lotion for electric furnace and converter and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Take 30 parts of 100-mesh high-calcium white ash, 20 parts of 60-mesh AD powder, 20 parts of 100-mesh barium carbonate (barium oxide content ≥ 75wt%), 15 parts of 100-mesh light-fired dolomite, and 15 parts of calcium carbide below 3mm, pass through the disc. After mixing and stirring evenly, lower the plate to obtain the base material; then send it into the silo of the ball extruder through the conveying device; then the base material is input into the powerful ball extruder through the screw distributor in the silo of the ball extruder, and the base material is transported by the hydraulic device. The material is extruded into spherical objects; the spherical objects are screened out by the conveying and screening device at the lower part of the extruder to obtain spherical products with a particle size of 25-35 mm, which are packaged to obtain a qualified composite slag lotion product.

[0038]The mass percentage of the active ingredients of the finished product is as...

Embodiment 2

[0040] Take 40 parts of 100-mesh high-calcium white ash, 25 parts of 100-mesh AD powder, 15 parts of 100-mesh barium carbonate (barium oxide content ≥ 75wt%), 10 parts of 100-mesh light-fired dolomite, and 10 parts of calcium carbide below 3mm, pass through the disc. After mixing and stirring evenly, lower the plate to obtain the base material; then send it into the silo of the ball extruder through the conveying device; then the base material is input into the powerful ball extruder through the screw distributor in the silo of the ball extruder, and the base material is transported by the hydraulic device. The material is extruded into spherical objects; the spherical objects are screened out by the conveying and screening device at the lower part of the extruder to obtain spherical products with a particle size of 25-35 mm, which are packaged to obtain a qualified composite slag lotion product.

[0041] The mass percentage content of the active ingredients of the finished pro...

Embodiment 3

[0043] Take 45 parts of 100-mesh high-calcium white ash, 30 parts of 60-mesh AD powder, 7 parts of 100-mesh barium carbonate (barium oxide content ≥ 75wt%), 10 parts of 100-mesh light-fired dolomite, and 10 parts of calcium carbide below 3mm, pass through the disc. After mixing and stirring evenly, lower the plate to obtain the base material; then send it into the silo of the ball extruder through the conveying device; then the base material is input into the powerful ball extruder through the screw distributor in the silo of the ball extruder, and the base material is transported by the hydraulic device. The material is extruded into spherical objects; the spherical objects are screened out by the conveying and screening device at the lower part of the extruder to obtain spherical products with a particle size of 25-35 mm, which are packaged to obtain a qualified composite slag lotion product.

[0044] The mass percentages of the active ingredients of the finished product are ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a compound slag cleaning agent for electric furnaces and converters and a preparation method thereof, and belongs to the technical field of metallurgical auxiliary materials. The compound slag cleaning agent comprises the following components in percentage by weight: calcium oxide 30-50%, alumina oxide 20-40%, barium oxide 5-20%, magnesium oxide 3-15%, and a reducing agent 5-15%. The comprehensive performance of the slag cleaning agent is outstanding the deoxidization, desulphurization and dephosphorization effect of the existing slag cleaning agent is improved and increased, the LF refining time is obviously shortened, the impurity absorption capacity is good, impurities are not introduced during smelting of molten steel; moreover, the kinds and proportion of the raw materials are reasonable, so that compared with the existing dephosphorization slag cleaning agent, the cost of the compound slag cleaning agent is obviously reduced, and the compound slag cleaning agent has obvious market advantage.

Description

technical field [0001] The invention belongs to the technical field of metallurgical auxiliary materials, and particularly relates to a composite slag lotion for electric furnaces and converters and a preparation method thereof. Background technique [0002] Composite slag lotion is a metallurgical auxiliary material that enters molten steel slag during the tapping process of electric furnace and converter, and can remove unstable inclusions and harmful substances in steel. It is one of the important means to realize molten steel purification. By adding compound slag washing agent to the ladle, the basicity and oxidizing property of the ladle slag are changed, so that the molten slag after slag washing has a calcium aluminate slag system with high basicity, low melting point, low iron oxide and rich CaO content. The dynamic conditions of the impact of the steel flow in the steel process increase the reaction interface of the slag steel to achieve the purpose of desulfurizati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C7/076
CPCY02P10/20
Inventor 李秀峰李秀忠
Owner HENAN TONGYU METALLURGY MATERIALS GRP