A kind of polypropylene filament oil and method of using the same

A technology of filament oil agent and polypropylene fiber, which can be used in fiber types, textiles and papermaking, fiber treatment, etc. It can solve the problem of non-yellowing of polypropylene filaments, improve lubricity, good wettability, and reduce staining Effect

Inactive Publication Date: 2017-10-24
SUZHOU SHENGDEZHU TECH DEV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the oil agent can meet the requirements of environmental protection, it still cannot overcome the defect that the polypropylene filament does not turn yellow after use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polypropylene filament oil and method of using the same
  • A kind of polypropylene filament oil and method of using the same
  • A kind of polypropylene filament oil and method of using the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Present embodiment provides a kind of polypropylene filament oil agent, it is made up of following components by weight percentage:

[0026]

[0027] The method of using the polypropylene filament oil agent includes the following steps:

[0028] (a) Dissolve each component of the formulation amount in deionized water at 20° C., stir for 45 minutes to form an aqueous solution with a total mass concentration (the sum of the mass concentrations of all components) of 10%;

[0029] (b) Add the aqueous solution into an oiling roller or a metering pump, and oil the polypropylene fibers at an oiling rate of 1% of the fiber weight.

Embodiment 2

[0031] Present embodiment provides a kind of polypropylene filament oil agent, it is made up of following components by weight percentage:

[0032]

[0033] The method of using the polypropylene filament oil agent includes the following steps:

[0034] (a) dissolving each component of the formula amount in deionized water at 30°C, stirring for 30 minutes to form an aqueous solution with a total mass concentration of 30%;

[0035] (b) adding the aqueous solution into an oiling roller or a metering pump, and oiling the puffed carpet filaments at an oiling rate of 2% of the fiber weight.

Embodiment 3

[0037] Present embodiment provides a kind of polypropylene filament oil agent, it is made up of following components by weight percentage:

[0038]

[0039]

[0040] The method of using the polypropylene filament oil agent includes the following steps:

[0041] (a) dissolving each component of the formula amount in deionized water at 25°C, stirring for 40 minutes to form an aqueous solution with a total mass concentration of 17%;

[0042] (b) Add the aqueous solution into an oiling roller or a metering pump, and oil the stretched twisted flat yarn at an oiling rate of 1.5% of the fiber weight.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a polypropylene filament oil agent and its use method, which is composed of the following components by weight percentage: 20-25% of isooctyl stearylate; 10-15% of high-grade fatty acid ester; Acid ammonium salt 12~18%; Oleic acid polyoxyethylene ether 12~18%; Castor oil polyoxyethylene ether 12~18%; Alkyl imidazoline betaine sodium salt 8~15%; Oleic acid imidazoline 10~15% %; natural fatty acid ester 3~8%; dodecylsulfonate salt 2~8%; polyoxyethylene 2~5%. On the one hand, oleic acid ammonium salt, oleic acid polyoxyethylene ether, oleic acid imidazoline and other ingredients are added to the raw material formula; The wettability, clustering, smoothness and antistatic properties of the fiber improve the lubricity of the fiber to the metal, and it also has a certain bactericidal property, which can prevent the microbial reproduction caused by the shedding oil agent in the water jet weaving; the shedding will not Attached to the green body, reducing the staining of the green body; the important thing is that it has good heat resistance, and there is very little deposit on the heating rod and heating plate at a temperature of 149~154 °C.

Description

technical field [0001] The invention belongs to the field of synthetic fiber auxiliary oil, relates to a polypropylene filament oil, in particular to a polypropylene filament oil and a use method thereof. Background technique [0002] Polypropylene fiber has light weight, good strength and toughness, good chemical stability, slow heat transfer, good moisture conductivity, small fabric shrinkage, no change in strength when wet, light and warm fabric, good elasticity, low manufacturing cost, and abundant sources. Low price, easy recycling and processing, etc., although it does not absorb moisture itself, but because of its good wicking effect, it can transfer moisture out through the capillaries in the fabric to keep the skin dry, so it is widely used in filter materials, non-toxic In addition to industrial textiles such as woven fabrics and geotextiles, in recent years, fine-denier polypropylene fiber has been more used in the manufacture of internationally popular functional...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M13/224D06M13/463D06M13/256D06M13/352D06M15/53D06M101/20
Inventor 杨莱衍
Owner SUZHOU SHENGDEZHU TECH DEV