Organic silicon-boron ceramic precursor as well as preparation method and application thereof

A ceramic precursor, organic technology, applied in the direction of silicon-organic compounds, etc., can solve the problem of heat resistance, tracking resistance, and deterioration of mechanical properties and processing properties of addition-type liquid silicone rubber that have not been found in silicone-boron ceramic precursors. , poor compatibility of silicone rubber, etc., to achieve the effect of facilitating large-scale production, improving heat resistance and arc ablation resistance, and not easy to hydrolyze

Active Publication Date: 2015-12-16
SOUTH CHINA UNIV OF TECH
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of inorganic fillers as modifiers not only has a large amount of addition, but also has poor compatibility with silicone rubber, and deteriorates the mechanical properties and processing properties of addition-type liquid silicone rubber.
However, there is no research report on the heat resistance and tracking resistance of silicone rubber based on organosilicon‐boron ceramic precursors.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic silicon-boron ceramic precursor as well as preparation method and application thereof
  • Organic silicon-boron ceramic precursor as well as preparation method and application thereof
  • Organic silicon-boron ceramic precursor as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Add 6.7g of octamethylcyclotetrasiloxane (D4), 3.1g of methyltrimethoxysilane (MTMS) and 2.1g of boric acid (BA) into a four-necked 250mL flask equipped with mechanical stirring and a serpentine reflux tube, Then measure 10 mL of diethylene glycol dimethyl ether and add 0.1 g of concentrated sulfuric acid dropwise, pour it into a flask, raise the temperature to 30°C and stir for 15 minutes, then raise the temperature to 80°C, keep the temperature for 2 hours, then raise the temperature to 150°C, and react for 2 hours. Finally, the reaction system was cooled to normal temperature until excess boric acid was precipitated. After the reaction, the reaction system was transferred to a centrifuge tube, centrifuged at a rotation speed of 10,000 r / min for 10 min, and the liquid was separated. Subsequently, distilled under reduced pressure at 100°C until there was no droplet in the recovery bottle to obtain a gel-like product, cooled to 50°C, then added 40 mL of n-hexane to mech...

Embodiment 2

[0050] According to the method and process in Example 1, the difference is that the amount of BA is increased to 3.5g to prepare Si-BOCP-2 and apply it to the addition-type liquid silicone rubber. Compared with Comparative Example 1, Si-BOCP-2 improved the thermal stability of silicone rubber, and compared with Example 1, the initial decomposition temperature increased from 433.7°C to 438.4°C, and the heat-resistant modification effect was slightly better than that of Si-BOCP-2. For BOCP-1, the initial tracking time is extended to 3130s.

Embodiment 3

[0052] According to the method and process in Example 2, the amount of D4 and MTMS used remained unchanged, and the amount of BA was increased to 4.9g to prepare Si-BOCP-3, which was applied to the addition-type liquid silicone rubber. It can be seen from Table 2 that with the further increase in the amount of boric acid, the heat resistance modification effect of Si-BOCP-3 decreased compared with Si-BOCP-2, but compared with the comparative example, the addition of Si-BOCP- The heat resistance of the silicone rubber of 3 is still higher than that of the blank silicone rubber, in which the initial thermal decomposition temperature increases from 406.6°C to 427.5°C, and the initial tracking time also increases from 960s to 3250s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
polydispersity indexaaaaaaaaaa
decomposition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses an organic silicon-boron ceramic precursor as well as a preparation method and an application thereof. The preparation method comprises steps as follows: cyclotetrasiloxane, trifunctional siloxane and boric acid are stirred at the temperature of 25-35 DEG C for 10-20 min under the action of an acid catalyst, then heated to the temperature of 80-100 DEG C for a polycondensation reaction and finally heated to the temperature of 120-150 DEG C for a continuous reaction, and the organic silicon-boron ceramic precursor is obtained through after-treatment. The prepared ceramic precursor has the controllable boron content, is high in thermal stability and has good compatibility with silicone rubber, the preparation method is simple and environment-friendly, the heat resistance and the arc firing resistance of the additional liquid silicone rubber can be substantially improved through addition of only 1.0 part of the organic silicon-boron ceramic precursor by mass, and the organic silicon-boron ceramic precursor has the important application prospect in fields of aviation and aerospace, high-voltage and extra-high-voltage power transmission and transformation and the like.

Description

technical field [0001] The invention relates to a functional silicone resin, in particular to a high-temperature-resistant silicone-boron ceramic precursor, a preparation method thereof, and an application in addition-type liquid silicone rubber. Background technique [0002] In recent years, with the rapid development of aerospace and high-voltage and ultra-high-voltage transmission and transformation grids, addition-type liquid silicone rubber (ALSR) has been widely used in aerospace sealing materials, insulators, wires and cables, etc. High temperature performance and tracking resistance put forward higher requirements. [0003] At present, the heat resistance and tracking resistance of silicone rubber are mainly improved by adding heat-resistant inorganic fillers. Patent CN102532917A mixes cerium oxide, high-temperature-resistant ceramic powder and boehmite in a mass ratio of 10:45:45 as a high-temperature-resistant additive, and the addition amount is 40 parts. The hea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/07C08L83/05C08K13/02C08K5/55C08K3/36C07F7/08
Inventor 赖学军郭燕霞曾幸荣李红强张亚军
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap