Glass ink-jet printing ink

An inkjet printing and glass technology, which is applied in ink, household utensils, applications, etc., can solve the problems that the color component and the inorganic frit component cannot be evenly integrated on the glass surface, the color of the pattern is uneven, and the appearance of the finished product is affected. , to achieve the effect of being conducive to remote sales and transportation, improving color uniformity, and excellent chemical resistance and stability

Active Publication Date: 2015-12-16
宁波美科数码智能技术有限公司
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The disadvantage of the glass inkjet printing ink mentioned above is that due to the different densities of its components, it causes:
[0006] (1) Colorant components and inorganic frit components are easy to form multi-layer suspension layers in organic solvents, resulting in their agglomeration and precipitation, which can block the ink nozzles of printing equipment
This greatly restricts and inconveniences remote sales and users, and is likely to cause unnecessary waste
[0007]⑵After printing and high-temperature sintering, sometimes the pigment components and inorganic frit components cannot be evenly integrated with the glass surface, resulting in uneven color of the pattern, color Distortion, affecting the appearance of the finished product, resulting in a certain scrap rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A glass inkjet printing ink, comprising the following components calculated in weight percent:

[0055] Inorganic colored frit: 45%; organic solvent: 49.5%; dispersant: 5%; antistatic agent: 0.5%.

[0056] The dispersant is Solsperse20000, and the antistatic agent is CHEMSTAT3500.

[0057] Wherein, the total weight percentage of the inorganic colored frit is 100%, which includes the following components calculated in weight percentage:

[0058] 42% Bi 2 o 3 , 10%SiO2 2 , 15%B 2 o 3 , 1.5%ZrO 2 , 3%Al 2 o 3 , 1.5%K 2 O, 20% glass chromogen, 3% frit stabilizer, 3% ZnO, 1% MgO.

[0059] Described glass chromogenic agent selects TiO for use 2 ; Described frit stabilizer selects V for use 2 o 5 .

[0060] Wherein, based on the total weight percentage of the organic solvent as 100%, it includes the following components calculated by weight percentage: isopropanol: 48.6%, butyl acetate: 11%, cyclohexanone: 24%, diethylene glycol Monobutyl ether: 11.4%, petroleum...

Embodiment 2

[0072] A glass inkjet printing ink, comprising the following components calculated in weight percent:

[0073] Inorganic colored frit: 40%; organic solvent: 54.5%; dispersant: 5%; antistatic agent: 0.5%.

[0074] The dispersant is Solsperse20000, and the antistatic agent is CHEMSTAT3500.

[0075] Wherein, the total weight percentage of the inorganic colored frit is 100%, which includes the following components calculated in weight percentage:

[0076] 40.5% Bi 2 o 3 , 15%SiO2 2 , 15.5%B 2 o 3 , 8%ZrO 2 , 8%Al 2 o 3 , 2.5%K 2 O, 1% glass coloring agent, 3% frit stabilizer.

[0077] The glass chromogen is selected from CoO, and the frit stabilizer is selected from NH 4 h 2 PO 4 .

[0078] Wherein, based on the total weight percentage of the organic solvent as 100%, it includes the following components calculated in weight percentage: cyclohexanone: 24%; dipropylene glycol methyl ether: 48.6%; propylene glycol diacetate: 12%; Ethylene glycol monobutyl ether: 10.4%;...

Embodiment 3

[0090] A glass inkjet printing ink, comprising the following components calculated in weight percent:

[0091] Inorganic colored frit: 15%; organic solvent: 65%; dispersant: 1%; antistatic agent: 19%.

[0092] The dispersant is 0.7% Solsperse 8000 and 0.3% DISPERBYK-163; the antistatic agent is JWK-200, and the organic solvent is ethylene glycol.

[0093] Wherein, the total weight percentage of the inorganic colored frit is 100%, which includes the following components calculated in weight percentage:

[0094] 35% Bi 2 o 3 , 29.3%SiO2 2 , 5%B 2 o 3 , 15%ZrO 2 , 0.7%Al 2 o 3 , 2%K 2 O, 7.5% glass chromogen, 2% frit stabilizer, 10% ZnO;

[0095] Described glass chromogenic agent selects 3%TiO for use 2 , 3.5%NiO and 1%CoO, and the frit stabilizer is sodium antimonate.

[0096] The specific steps of manufacturing the glass inkjet printing ink of this embodiment are as follows:

[0097] 1. Weigh the components of the above-mentioned inorganic colored frit according to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a glass ink-jet printing ink. The ink comprises, by weight, 20-60% of inorganic colored frits, 35-65% of an organic solvent, 1-15% of a dispersing agent and 0.1-4.5 % of an antistatic agent, and all the components account for 100%. The inorganic colored frits comprise, by weight, 35-65% of Bi2O3, 10-40% of SiO2, 5-18% of B2O3, 1-5% of ZrO, 0.7-8% of Al2O3, 0.3-2.5% of K2O, 1-28% of a glass color former and 0.1-3% of a frit stabilizing agent. The frit stabilizing agent is selected from any one of vanadium pentoxide, sodium dihydrogen phosphate, sodium selenite, ammonium dihydrogen phosphate and sodium antimonite. The glass ink-jet printing ink is stable in quality, printed patterns are accurate, uniform and bright in color, the finished product is attractive, and the glass ink-jet printing ink has the good weather resistance and chemical-resistance stability.

Description

Technical field [0001] The present invention involves the field of glass decoration, which specifically involves a glass inkjet printing ink. Background technique [0002] Printing patterns on glass surface is a common way of decorative glass.At present, in China, the screen printing method is generally printed on the glass surface to achieve the decorative effect.However, the surface of the pattern obtained through the screen is rough, the color is monotonous, and the lines are rigid, and the effect is not ideal.In addition, the operation of the screen printing is more complicated, and it requires large manpower investment. The waste produced by printing also causes a certain degree of pollution to the environment. [0003] In the past ten years, inkjet printing has appeared abroad, and the digital patterns in the computer are printed on the glass surface through the sprinkler's non -contact type.This technology uses a dedicated printing device to print the ink ink ink that can ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/322C09D11/38
Inventor 刘斌游路春陈树明
Owner 宁波美科数码智能技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap