Mothproof additive used for processing microlite wood floors

A technology of stone and wood flooring and additives, applied in the fields of application, biocide, pest control, etc., can solve problems such as moth-eaten, and achieve the effects of moth-proof improvement, safety and environmental protection, and stable properties

Inactive Publication Date: 2015-12-23
安徽温禾新材料科技股份有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional anti-moth treatment is to put insect repellant when installing the floor, but moth-eaten phenomenon still occurs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] Preparation of modified gypsum powder: first disperse 35 parts of gypsum powder and 12 parts of carboxymethyl cellulose in 100 parts of ethanol, then ultrasonically treat it at an ultrasonic frequency of 22kHz and a power of 100W for 30min, filter, wash with water, and dry the filter residue with Add 5 parts of nano-aluminum chloride into the ball mill and mill for 45 minutes.

[0016] Preparation of traditional Chinese medicine extract: 35 parts of ginkgo biloba, 25 parts of dandelion, 20 parts of mugwort, 15 parts of cherry leaf, 15 parts of leek, 12 parts of coptis, 12 parts of Sophora flavescens, 10 parts of mint, 10 parts of basil, 8 parts of longevity Add chrysanthemum, 8 parts of balsam pear, 5 parts of garlic and 5 parts of Malacock grass to 400 parts of water, heat to boiling state and keep warm for 60 minutes, filter, the filtrate is concentrated into a paste, then sent to a freeze dryer for drying, crushed and passed through a 100-mesh sieve That's it.

Embodiment 1

[0018] (1) First add 5 parts of nano-copper oxide and 5 parts of nano-zinc oxide into 30 parts of ethanol, then ultrasonically treat at an ultrasonic frequency of 22 kHz and a power of 100 W for 15 minutes, then add 4 parts of sulfur, and continue ultrasonic treatment for 10 minutes to obtain material I ;

[0019] (2) Dry 20 parts of tea leaves and 10 parts of coffee grounds and pulverize them into powder, then add 12 parts of tea seed powder, 6 parts of chili powder, 3 parts of Chinese prickly ash and 2 parts of castor bean powder, and heat up the mixed powder to Stir at 70-80°C for 15 minutes to obtain material II;

[0020] (3) Dissolve 8 parts of sodium chloride in 300 parts of water, then add 90 parts of modified gypsum powder, 30 parts of slaked lime, 8 parts of Chinese medicine extract, material I and material II, mix well and add to the ball mill, and ball mill until The fineness is less than 0.1mm, and it can be passed through a 120-mesh sieve after drying and crushin...

Embodiment 2

[0022] (1) First add 6 parts of nano-copper oxide and 6 parts of nano-zinc oxide into 35 parts of ethanol, then ultrasonically treat for 15 minutes at an ultrasonic frequency of 22 kHz and a power of 100 W, then add 5 parts of sulfur, and continue ultrasonic treatment for 10 minutes to obtain material I ;

[0023] (2) Dry 25 parts of tea leaves and 10 parts of coffee grounds and pulverize them into powder, then add 15 parts of tea seed powder, 8 parts of chili powder, 5 parts of Chinese prickly ash and 3 parts of castor bean powder, and the mixed powder is heated to Stir at 70-80°C for 15 minutes to obtain material II;

[0024] (3) Dissolve 10 parts of sodium chloride in 300 parts of water, then add 85 parts of modified gypsum powder, 35 parts of slaked lime, 10 parts of Chinese medicine extract, material I and material II, mix well and add to the ball mill, and ball mill until The fineness is less than 0.1mm, and it can be passed through a 120-mesh sieve after drying and cru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a mothproof additive used for processing microlite wood floors, relating to the technical field of floor processing. The mothproof additive is prepared from the following raw materials in parts by weight: 12-18 parts of tea seed powder, 5-8 parts of nano copper oxide, 5-8 parts of nano zinc oxide, 80-90 parts of modified gypsum powder, 30-40 parts of slaked lime, 20-25 parts of tea dregs, 10-15 parts of coffee dregs, 8-12 parts of traditional Chinese medicine extract, 8-12 parts of sodium chloride, 6-10 parts of chilli powder, 3-6 parts of Chinese prickly ash powder, 3-6 parts of sulfur, 2-4 parts of castor seed powder, 30-40 parts of ethanol and 300-350 parts of water. The prepared mothproof additive has the characteristics of light and fragrant taste, stable properties, safety and environment friendliness, can be used for effectively mothproofing the floors and improving the indoor air quality, can be directly added to floor manufacturing raw materials when being used, and has comprehensive and durable mothproof effects.

Description

Technical field: [0001] The invention relates to the technical field of floor processing, in particular to an anti-moth additive for microcrystalline stone wood floor processing. Background technique: [0002] Microcrystalline stone wood flooring is made of modern technology. The board is made of high-calcium microcrystalline stone powder, germanium stone, medical stone, natural resin and plant powder as the main base material, and is made by adding more than ten kinds of auxiliary materials through high temperature and high pressure extrusion. The surface is made of wood grain pattern by transfer printing, which has beautiful and natural texture, comfortable foot feeling, never deformed, not afraid of blisters, no termites, no fading, strong weather resistance of surface coating, resistance to cigarette butt burns, scratch resistance, wear resistance, etc. It is a high-performance product developed through years of research and repeated practice by scientific researchers. I...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A01N65/42A01P17/00A61L9/013A01N59/06A01N59/20A01N59/16A61L101/56
Inventor 温中苏
Owner 安徽温禾新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com