Vacuum plating UV coating for PET plastic cement

A vacuum electroplating and coating technology, applied in the direction of polyester coating, polyurea/polyurethane coating, coating, etc., can solve the problems of poor fullness, low surface tension of PET materials, difficult adhesion, etc., to overcome brittleness or false Sexual adhesion, improvement of poor plumpness, good overall adhesion effect

Inactive Publication Date: 2016-01-13
德阳森华涂料化工有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the surface tension of PET materials is extremely low, so it is very difficult to coat them. Many factories use pre-treatment agents, corona or chromic acid treatment when coating PET materials, otherwise it is difficult to have good adhesion.
However, some existing PET coatings on the market have more or less poor leveling, poor fullness, poor toughness, false adhesion (the adhesion was good at the time, but fell off after a few days of testing), poor coating performance, and the plating layer is uneven. Color and other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A PET plastic vacuum electroplating UV coating, comprising the following components by weight percentage: polyurethane modified acrylic oligomer 10-25%, polyester acrylate 10-20%, trimethylolpropane triacrylate 5-15% %, α-hydroxycyclohexyl benzophenone 1.5-4%, 10% acrylic functional resin 1-8%, methyl ethyl ketone 2-15%, ethyl acetate 35-50%, butyl acetate 5-20%, cyclohexene Ketones 1-8%.

[0024] The preparation method of above-mentioned a kind of PET plastic vacuum coating UV bottom coating, comprises the steps:

[0025] (1) Prepare polyurethane-modified acrylic oligomer, polyester acrylate, and trimethylolpropane triacrylate in proportion in turn, stir in the disperser at a speed of 600-800rpm for 20-25 minutes, and disperse to Mix well.

[0026] (2) Mix α-hydroxycyclohexyl benzophenone, 10% acrylic functional resin, methyl ethyl ketone, ethyl acetate, and butyl acetate cyclohexanone in proportion, and add it to step (1) under the condition of avoiding light. Stir...

Embodiment 2

[0029] A PET plastic vacuum electroplating UV coating, comprising the following components by weight percentage: polyurethane modified acrylic acid oligomer 15%, polyester acrylate 15%, trimethylol propane triacrylate 10%, α-hydroxyl ring Hexylbenzophenone 2%, 10% acrylic functional resin 3%, methyl ethyl ketone 5%, ethyl acetate 40%, butyl acetate 6%, cyclohexanone 4%.

[0030] Its preparation method is with embodiment 1.

Embodiment 3

[0032] A PET plastic vacuum electroplating UV coating, comprising the following components by weight percentage: polyurethane modified acrylic acid oligomer 10%, polyester acrylate 10%, trimethylolpropane triacrylate 15%, α-hydroxyl ring Hexylbenzophenone 4%, 10% acrylic functional resin 8%, methyl ethyl ketone 10%, ethyl acetate 35%, butyl acetate 5%, cyclohexanone 3%.

[0033] Its preparation method is with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
heat deflection temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a vacuum plating UV coating for PET plastic cement. The vacuum plating UV coating for the PET plastic cement is prepared from, by weight, 10%-25% of polyurethane-modified acrylic acid oligomers, 10%-20% of polyester acrylate, 5%-15% of trimethylolpropane triacrylate, 1.5%-4% of alpha-hydroxycyclohexyl phenyl ketone, 1%-8% of 10% acrylic acid function resin, 2%-15% of methyl ethyl ketone, 35%-50% of ethyl acetate, 5%-20% of n-butyl acetate and 1%-8% of cyclohexanone. According to the vacuum plating UV coating for the PET plastic cement, the vacuum plating UV coating is a UV vacuum aluminum plating primer which has the excellent adhesion on a PET plastic cement substrate, the high fullness, the excellent levelling property and the wonderful plating effect are achieved; the defect of over crispness or pseudo adhesion of similar products is overcome, and the excellent overall adhesion effect can be supplied; the excellent physical and chemical properties and the excellent levelling property and fullness are achieved.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a PET plastic vacuum electroplating UV coating. Background technique [0002] UV coating is a general term for all ultraviolet radiation curable coatings. Its film-forming method is that ultraviolet radiation triggers unsaturated double bond open-chain polymerization and quickly dries into film. No special process is required, and the overall performance is good; the coating with thin film That is, it has excellent fullness; particularly good adhesion; and very high gloss. [0003] PET material (polyethylene terephthalate chemical formula is -OCH2-CH2OCOC6H4CO-English name: polyethyleneterephthalate) compared to widely used ABS material (acrylonitrile-butadiene-styrene copolymer, English name: AcrylonitrileButadieneStyrene) Said that due to its excellent physical and mechanical properties in a wide temperature range, the long-term use temperature can reach 120 ° C, excellent el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D167/06C09D7/12
Inventor 钟华军吴大海
Owner 德阳森华涂料化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap