Nano flocculation material for water treatment and preparation method of nano flocculation material

A nano-water and flocculation technology, which is applied in the direction of flocculation/sedimentation water/sewage treatment, etc., can solve the problems of high consumption of flocculants, slow flocculation and sedimentation speed, high cost of use, etc., achieve good adsorption and flocculation performance, simple preparation method, The effect of good stability

Inactive Publication Date: 2016-01-27
苏州书瑞环保科技有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Inorganic flocculants can be divided into low-molecular flocculants and high-molecular flocculants. Low-molecular flocculants include aluminum salts and iron salts. The cost of low-molecular flocculants is low, but their flocculation and precipitation speed is slow and the consumption of flocculants is high. ; Commonly used polymer flocculants include basic polyaluminum chloride, polyaluminum sulfate, and polyferric sulfate. Poor processing effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Weigh 45 kg of dimethylaminoethylene methacrylate, 8 kg of dimethyl diallyl ammonium chloride, 8 kg of mannitol, 7 kg of N-(5-hydroxyethyl) nicotinamide nitrate, hydroxypropyl Methylcellulose 3kg, polyoxyethylene sorbitan monooleate 2kg, cetyl alcohol 3kg, diameter are activated carbon fiber 1kg, borax 0.5kg of 40 nanometers, stir;

[0027] (2) Put it into a high-pressure homogenizer and mix it at 65°C and 15MPa for 5 minutes, then cool to room temperature to obtain the nanometer water treatment flocculation material.

[0028] The performance test results of the prepared nano-flocculation materials for water treatment are shown in Table 1.

Embodiment 2

[0030] (1) Weigh 55 kg of dimethylaminoethylene methacrylate, 12 kg of dimethyl diallyl ammonium chloride, 11 kg of mannitol, 9 kg of N-(5-hydroxyethyl) nicotinamide nitrate, hydroxypropyl Methylcellulose 5kg, polyoxyethylene sorbitan monooleate 3kg, cetyl alcohol 5kg, diameter are activated carbon fiber 1.5kg, borax 1kg and polylysine 2kg of 55 nanometers, stir;

[0031] (2) Put it into a high-pressure homogenizer and mix it at 75°C and 18MPa for 10 minutes, and cool to room temperature to obtain the nanometer water treatment flocculation material.

[0032] The performance test results of the prepared nano-flocculation materials for water treatment are shown in Table 1.

Embodiment 3

[0034] (1) Weigh 50 kg of dimethylaminoethylene methacrylate, 10 kg of dimethyl diallyl ammonium chloride, 9 kg of mannitol, 8 kg of N-(5-hydroxyethyl) nicotinamide nitrate, hydroxypropyl Methylcellulose 4kg, polyoxyethylene sorbitan monooleate 2.5kg, cetyl alcohol 4kg, diameter are activated carbon fiber 1kg, borax 0.8kg and polylysine 1kg of 45 nanometers, stir;

[0035] (2) Add to a high-pressure homogenizer and mix at 70°C and 17MPa for 8 minutes, and cool to room temperature to obtain nanometer water treatment flocculation material.

[0036] The performance test results of the prepared nano-flocculation materials for water treatment are shown in Table 1.

[0037] The flocculation material of Examples 1-3 is used for sewage treatment: when it is used in sewage with a COD of 600mg / L, a good treatment effect can be achieved with an amount of flocculation material of 0.2g / L, see the table for specific results 1.

[0038] Table 1

[0039] Test items Turbidity (N...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano flocculation material for water treatment and a preparation method of the nano flocculation material. The nano flocculation material for water treatment comprises components in parts by weight as follows: 45-55 parts of dimethylamino ethyl methacrylate, 8-12 parts of diallyl dimethyl ammonium chloride, 8-11 parts of mannitol, 7-9 parts of N-(5-ethoxy) nicotinamide nitrate, 3-5 parts of hydroxypropyl methyl cellulose, 2-3 parts of polyoxyethylene sorbitan monooleate, 3-5 parts of cetyl alcohol, 1-1.5 parts of activated carbon fiber and 0.5-1 part of borax. The invention further provides a preparation method of the nano flocculation material for water treatment.

Description

technical field [0001] The invention belongs to the field of water treatment materials, in particular to a nanometer water treatment flocculation material and a preparation method thereof. Background technique [0002] Water treatment can effectively remove the turbidity in the water to be treated and reduce the pollution load of the subsequent treatment of sewage. Commonly used water treatment reagents include flocculants, which can be divided into inorganic flocculants and organic flocculants according to their chemical composition. Among them, organic flocculants include organic coagulants and organic polymer flocculants; organic flocculants include synthetic organic polymer flocculants, natural organic polymer flocculants and microbial flocculants. Inorganic flocculants can be divided into low-molecular flocculants and high-molecular flocculants. Low-molecular flocculants include aluminum salts and iron salts. The cost of low-molecular flocculants is low, but their floc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/52C02F1/54C02F1/56
Inventor 魏锋
Owner 苏州书瑞环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com