A kind of mold and technology for preparing amorphous ring

A technology for molds and rings, which is applied in the field of molds and processes for preparing amorphous rings. It can solve the problems of high requirements for amorphous forming ability, inability to make amorphous, and poor thermal conductivity of mold materials, so as to save raw materials and achieve high yields. , process reliable effect

Active Publication Date: 2017-07-18
UNIV OF SCI & TECH BEIJING
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this method can obtain bulk amorphous with complex shapes, it is not suitable for precious metal alloy systems such as gold-based or silver-based alloys due to poor thermal conductivity, low strength and low surface roughness of the mold material, which requires high amorphous forming ability. At the same time, there are many amorphous defects prepared by this method, and the surface needs further treatment to appear metallic color. The preparation process of high-pressure casting method and copper mold casting is similar, and both can form non-crystalline objects with solid structure. For crystal structure parts, the copper mold is divided into upper and lower parts, and it is impossible to make amorphous hollow structures such as rings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of mold and technology for preparing amorphous ring
  • A kind of mold and technology for preparing amorphous ring

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The technical scheme of the present invention will be further described below in conjunction with the accompanying drawings.

[0029] Such as figure 1 As shown, the present invention is a mold for preparing an amorphous ring, the mold includes a cylindrical body, and the cylindrical body is composed of a molten pool section 1, a core section 2 and a base section 3 arranged sequentially from top to bottom , The molten pool section 1 is made of pure copper; the core section 2 and base section 3 are made of steel, aluminum and aluminum alloy, titanium and titanium alloy, or magnesium and magnesium alloy.

[0030] The molten pool section 1 includes a molten pool section main body 1-1 and an adjustment ring 1-2, the top of the molten pool section main body 1-1 is provided with a melting pool 1-4, and the middle part of the molten pool section main body is Forming cavity 1-6, the adjusting ring 1-2 is arranged in the forming cavity 1-6, the adjusting ring 1-2 is used to adju...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of amorphous alloy materials, and in particular, relates to a mold for preparing an amorphous ring and a process thereof. The mold comprises a cylindrical body; the cylindrical body consists of a molten pool section, a middle core section and a base section arranged in sequence from top to bottom; the molten pool section adopts a material of pure copper; and the middle core section and the base section adopt materials of steel, aluminum and aluminum alloys, titanium and titanium alloys or magnesium and magnesium alloys. The preparation process comprises the following steps: firstly, a master alloy is heated for melting under the condition of high vacuum; then, a master alloy melt is quickly sucked in a core-carried split metal mold by a sucking casting method; after the master alloy melt is cooled, an amorphous body is demolded; and finally, the amorphous body is cut to form a ring shape for polishing. The taper of a core is 1-2 degrees, so that the demolding is convenient. The amorphous ring preparation method is near final molding, simple, reliable and fast in cooling speed, can be matched with a non-self-consumption vacuum arc smelting furnace more conveniently, and is controllable in process, excellent in surface molding, high in product surface quality, high in yield and suitable for batch production.

Description

technical field [0001] The invention belongs to the field of amorphous alloy materials, and in particular relates to a mold for preparing an amorphous ring and a process thereof. Background technique [0002] Amorphous alloy (metallic glass) is a new type of metal material with special atomic arrangement and excellent performance. Different from the long-range ordered atomic arrangement of traditional metal materials, the atomic arrangement of amorphous alloys has the structural characteristics of long-range disorder and short-range order, and there are no defects such as grain boundaries and dislocations in its microstructure. Therefore, amorphous alloys exhibit excellent properties such as high strength, high hardness, high elastic limit, low modulus, and corrosion resistance that cannot be compared with traditional crystalline alloys. At the same time, amorphous alloys have a smooth surface, so they are especially suitable for making rings, etc. jewelry pieces. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D25/02
CPCB22D25/026
Inventor 王辉吕昭平吴渊刘雄军
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products