Method for preparing ultrasonic dispersion zirconium carbide boron carbide-carbon fiber friction material

A zirconium carbide boron carbide and friction material technology, which is applied in the field of friction material preparation, can solve the problems of reduced friction performance and potential safety hazards, and achieves the effects of high friction performance, improved wear resistance and high manufacturing cost

Inactive Publication Date: 2016-04-13
SHANDONG UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the friction performance of C / C composite materials will be reduced in a humid environment, which will bring serious safety hazards to the use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] (1) Set the density to 1.8g / cm 3 The graphitized carbon fiber blanket is fed with a mixed gas of propane gas and nitrogen at a temperature of 900°C. The molar ratio of propane gas: nitrogen is 1:4, the flow rate is controlled at 50ml / min, and the carburizing treatment is performed for 24 hours to obtain a carburized carbon fiber blanket. ;

[0020] (2) Pass the above-mentioned carburized carbon fiber blanket into a mixed gas of boron trichloride, methane, hydrogen and argon at a temperature of 900 °C, and the molar ratio of boron trichloride: methane: hydrogen: argon is 1:1: 3:4, the flow rate is controlled at 50ml / min, and the deposited boron carbide is treated for 24 hours to obtain a deposited boron carbide carbon fiber blanket;

[0021] (3) Immerse the above-mentioned deposited boron carbide carbon fiber blanket into zirconium carbide slurry with a particle size of less than 0.3 μm and a content of 5%, place it in an ultrasonic cleaner and fill it with zirconium ca...

Embodiment 2

[0025] (1) Set the density to 0.8g / cm 3 The graphitized carbon fiber blanket is fed with a mixture of propane gas and nitrogen at a temperature of 1000°C. The molar ratio of propane gas: nitrogen is 1:5, the flow rate is controlled at 350ml / min, and the carburizing treatment is performed for 18 hours to obtain a carburized carbon fiber blanket. ;

[0026] (2) Pass the above-mentioned carburized carbon fiber blanket into a mixed gas of boron trichloride, methane, hydrogen and argon at a temperature of 1000 °C, and the molar ratio of boron trichloride: methane: hydrogen: argon is 1:1.5: 4.5:5, the flow rate is controlled at 350ml / min, and the deposited boron carbide is treated for 17 hours to obtain a deposited boron carbide carbon fiber blanket;

[0027] (3) Immerse the above-mentioned deposited boron carbide carbon fiber blanket into zirconium carbide slurry with a particle size of less than 0.3 μm and a content of 12%, place it in an ultrasonic cleaner and fill it with zirco...

Embodiment 3

[0031] (1) Set the density to 0.1g / cm 3 The graphitized carbon fiber blanket is fed with a mixed gas of propane gas and nitrogen at a temperature of 1100°C. The molar ratio of propane gas: nitrogen is 1:6, the flow rate is controlled at 600ml / min, and the carburizing treatment is performed for 10 hours to obtain a carburized carbon fiber blanket. ;

[0032] (2) Pass the above-mentioned carburized carbon fiber blanket into a mixed gas of boron trichloride, methane, hydrogen and argon at a temperature of 1100 °C, and the molar ratio of boron trichloride: methane: hydrogen: argon is 1:2: 6:6, the flow rate is controlled at 600ml / min, and the deposited boron carbide is treated for 10 hours to obtain a deposited boron carbide carbon fiber blanket;

[0033] (3) Immerse the above-mentioned deposited boron carbide carbon fiber blanket into a slurry with a particle size of less than 0.3 μm and a content of 20% zirconium carbide, place it in an ultrasonic cleaner and fill it with zirco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

A method for preparing an ultrasonic dispersion zirconium carbide boron carbide-carbon fiber friction material is characterized in that a graphitized carbon fiber blanket with the density being 0.1-1.8 g / cm<3> is subjected to carburizing treatment, then subjected to boron carbide deposition, subjected to ultrasonic dispersion zirconium carbide filling treatment and then subjected to embedding siliconizing, and then nitridation is carried out in the nitrogen atmosphere to prepare the ultrasonic dispersion zirconium carbide boron carbide-carbon fiber friction material. According to the method, the graphitized carbon fiber blanket is adopted, and the friction material is prepared through the steps of carburization, silicon carbide deposition, zirconium carbide filling, embedding siliconizing, nitridation and the like. The prepared friction material is high in strength, toughness and friction performance and can adapt to various climatic conditions.

Description

technical field [0001] The invention relates to a preparation method of a friction material composited by carbon fiber and ceramic material, and belongs to the technical field of composite material preparation. Background technique [0002] At present, carbon fiber and carbon (C / C) composite materials are mainly used as friction materials. Since the wear resistance of C / C composite materials is relatively low, people are looking for a method for preparing friction materials with higher wear resistance. In addition, the friction performance of C / C composite materials will be reduced in a humid environment, which will bring serious safety hazards to the use. Contents of the invention [0003] The object of the present invention is to provide a method for preparing a friction material that can overcome the above-mentioned defects, achieve higher strength, higher friction performance and adapt to various climatic conditions. Its technical solution is: [0004] The preparatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/00C04B35/80C04B35/563C04B35/56C04B35/591C04B35/65C04B35/622C04B35/634
CPCC04B35/5622C04B35/563C04B35/591C04B35/622C04B35/63444C04B35/806C04B38/00C04B2111/00362C04B2235/428C04B2235/46C04B2235/48C04B2235/5248C04B2235/5256C04B2235/616C04B2235/6567C04B2235/658C04B35/584
Inventor 唐竹兴
Owner SHANDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com