Peelable blue plastic and preparation method thereof

A technology of blue glue and curing resin, applied in the field of peelable blue glue and its preparation, can solve the problems of cumbersome stripping process, high curing temperature and long time, and achieve the effects of fast curing speed, simple process and easy control.

Inactive Publication Date: 2016-04-13
SHANGHAI INST OF TECH
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The current peelable blue glue is generally cured by heating above 100°C, the curing temperature is high, and the general peelable blue glue also has a long time, and the peeling process is cumbersome and has problems such as residue.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Peelable blue plastic and preparation method thereof
  • Peelable blue plastic and preparation method thereof
  • Peelable blue plastic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A kind of strippable blue glue, calculated by weight, its raw material composition and content are as follows:

[0040]

[0041] Wherein: described UV curable resin A is calculated in parts by weight, and its composition and content are as follows:

[0042]

[0043] Described UV curing resin A is carried out as follows:

[0044] Add 10 parts of methyl hydrogen-containing silicone oil and 10 parts of ethoxylated trimethylolpropane triacrylate into a 500ml three-necked flask, then add 0.01 part of polymerization inhibitor hydroquinone, pass in protective gas, and stir And heat it up to 60°C, add 0.03 parts of chloroplatinic acid complex, keep stirring for 3 hours, stop heating, and wait until the temperature of the flask drops to room temperature to obtain UV curable resin A.

[0045] Described UV curing resin B is a toughening resin, such as a mixture of epoxy acrylate and polyurethane acrylate in a mass ratio of 1:1;

[0046] The leveling agent is TegoGlide410; ...

Embodiment 2

[0060] A kind of strippable blue glue, calculated by weight, its raw material composition and content are as follows:

[0061]

[0062] Wherein: described UV curable resin A is calculated in parts by weight, and its composition and content are as follows:

[0063]

[0064] Described UV curing resin A is carried out as follows:

[0065] Add 20 parts of methyl hydrogen-containing silicone oil and 20 parts of ethoxylated trimethylolpropane triacrylate into a 500ml three-necked flask, then add 0.02 parts of polymerization inhibitor hydroquinone, pass through protective gas, and stir And heat it up to 80°C, add 0.05 part of chloroplatinic acid complex, keep stirring for 5 hours, stop heating, and wait until the temperature of the flask drops to room temperature to obtain UV curable resin A.

[0066] Described UV curing resin B is a toughening resin, such as a mixture of epoxy acrylate and polyurethane acrylate in a mass ratio of 2:1;

[0067] The leveling agent is a mixture...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a peelable blue plastic and a preparation method thereof. The peelable blue plastic comprises the following components in parts by weight: 60-150 parts of UV curing resin A, 60-150 parts of UV curing resin B, 0.05-0.1 part of a leveling agent, 1-10 parts of a wetting agent, 0.2-1 part of a defoamer, 1-10 parts of UV color paste, 3-5 parts of a photoinitiator A and 3-5 parts of a photoinitiator B. After coating, through irradiation of a 365 nm UV LED lamp, the peelable blue plastic coating is high in curing ability, good in binding force, easy to peel, complete in peeling, and free of residue; the peelable blue plastic can be applied to insulation protection, moisture and pollution prevention and anti-scratch protection of materials of PET, ITO conductive films, ITO glass, mobile glass, tempered glass windows and the like.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a strippable blue glue and a preparation method thereof. Background technique [0002] In recent years, the rapid development of digital products has driven the rapid development of the touch screen industry. The high-performance touch screen preparation process requires inks with anti-corrosion functions or "peelable blue glue" and "surface protection glue" for metal surface processing protection. When manufacturing printed boards, some parts of the board are often covered with peelable glue to avoid being splashed by tin when soldering, such as gold fingers, interface cards, carbon conductive keys and large-area boards, all of which require Selective soldering and multiple continuous soldering, such as SMD mixed assembly, reflow soldering manual and automatic and other soldering processes, etc. Drawing on the protection method of the peelable blue glue i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/07C09D163/10C09D175/14C09D5/20C09D7/12C08G77/38
CPCC08G77/38C08L2205/03C09D5/20C09D7/63C09D183/06C08L63/10C08L75/14
Inventor 张英强梁华丽李烨
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com