Preparation method of mobile telephone shell

A mobile phone shell, yttrium oxide technology, applied in branch equipment, telephone structure, telephone communication, etc., can solve the problems of general mechanical strength of mobile phone shells, and achieve the effects of easy operation, uniform pores and high strength

Active Publication Date: 2016-05-04
DONGGUAN XINBO STRUCTURAL CERAMICS CO LTD
View PDF3 Cites 50 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the mechanical strength of the mobile phone shell made by injection molding process is average, and there is still a technical demand for further improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of mobile telephone shell

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] In order to make the above objects, features and advantages of the present invention more comprehensible, specific implementations of the present invention will be described in detail below in conjunction with the accompanying drawings. In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present invention. However, the present invention can be implemented in many other ways different from those described here, and those skilled in the art can make similar improvements without departing from the connotation of the present invention, so the present invention is not limited by the specific implementations disclosed below.

[0024] Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the technical field of the invention. The terminology used herein in the description of the present invention is only for the purpos...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a mobile telephone shell. The preparation method comprises weighing yttrium oxide-stabilized zirconia powder and a surfactant according to a mass ratio of the surfactant to yttrium oxide-stabilized zirconia powder of 1-5: 100, adding ethanol into the weighed materials, carrying out ball milling mixing, carrying out drying and sieving to obtain slurry, mixing the slurry and a binder, carrying out mixing and granulation to obtain feed for injection, wherein the binder comprises polyethylene glycol, oxidizing high density polyethylene, polyvinyl butyral and stearic acid, carrying out injection molding on the feed to obtain a green body, carrying out staining detection on the green body, putting the green body into water, carrying out water debinding, carrying out thermal debinding to obtain a blank, sintering the blank to obtain a semifinished product, and carrying out machining and polishing on the semifinished product to obtain the mobile telephone shell. The mobile telephone shell has high strength, is not easily broken and has high density and uniform apertures. The preparation method has simple processes, operation easiness and high production efficiency.

Description

technical field [0001] The invention relates to the technical field of zirconia ceramics, in particular to a method for preparing a mobile phone casing. Background technique [0002] As a new type of high-tech ceramics, zirconia ceramics have properties such as high strength, high fracture toughness, high hardness, excellent heat insulation performance and high temperature resistance, and are widely used in the fields of structural ceramics and functional ceramics. In addition, zirconia is non-magnetic, non-conductive, non-rusting, and wear-resistant. It is also widely used in the field of biomedical equipment, props, and tools. Recently, partially stabilized zirconia (TZP) can be used to prepare magnetically shielded watch cases, corrosion-resistant watch parts and other instrument parts by powder metallurgy. In addition to the above applications, TZP is also widely used in decoration, life, medicine, piezoelectric ceramics, sensor ceramics and other fields. [0003] The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/48C04B35/622C04B35/634C04B35/638H04M1/02
CPCC04B35/48C04B35/622C04B35/6346C04B35/638C04B2235/3225C04B2235/60C04B2235/77C04B2235/96H04M1/0283
Inventor 利剑肖群顺王高翔陈兰桂孙亮王文利
Owner DONGGUAN XINBO STRUCTURAL CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com