Economic and environment-friendly damping plate with high damping property and preparation method thereof

A high damping and damping plate technology, applied in the field of polymer materials, can solve the problems of carcinogenicity and harm to human health, and achieve the effects of long service life, low production cost, and conducive to large-scale industrial production.

Active Publication Date: 2016-05-25
JIANGSU TONGMENG AUTO PARTS IND CO LTD
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main components of asphalt and its smoke are phenols, compounds, and asphalt and its smoke are phenols, compounds, anthracene, naphthalene, pyridine, etc., which are irritating to the skin and mucous membranes, and the asphalt damping board has a strong Carcinogenic effect, which will endanger the health of personnel, so it is necessary to develop a damping plate that can use fly ash for shock absorption without using asphalt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] An economical and environment-friendly damping plate with high damping performance described in this embodiment includes the following raw materials: polyurethane elastomer, fly ash, mica, hydrogenated C5 petroleum resin, glass fiber, carbon black, anti-aging agent, antioxidant, Its mass ratio is: 220; 460; 445; 60; 7; 65; 5;

[0025] Its preparation method comprises the following steps:

[0026] (1) Turn on the vacuum kneader and raise the temperature to 180°C,

[0027] (2) Start the vacuum kneader, add polyurethane elastomer, antioxidant, antiaging agent, hydrogenated C5 petroleum resin, stir for 28 minutes,

[0028] (3) When the temperature drops to 148°C, add fly ash and stir for 15 minutes.

[0029] (4) Then add mica, carbon black, and glass fiber, stir for 58 minutes, and keep the pressure at 4.7MPa,

[0030] (5) Extrude with a screw extruder, start calendering, and die-cut to obtain a damping plate with high damping performance.

[0031] The economical and en...

Embodiment 2

[0033] An economical and environment-friendly damping plate with high damping performance described in this embodiment includes the following raw materials: polyurethane elastomer, fly ash, mica, hydrogenated C5 petroleum resin, glass fiber, carbon black, anti-aging agent, antioxidant, Its mass ratio is: 200; 500; 400; 80; 4; 100; 5;

[0034] Its preparation method comprises the following steps:

[0035] (1) Turn on the vacuum kneader and raise the temperature to 160°C,

[0036] (2) Start the vacuum kneader, add polyurethane elastomer, antioxidant, anti-aging agent, hydrogenated C5 petroleum resin, stir for 30 minutes,

[0037] (3) When the temperature drops to 140°C, add fly ash and stir for 20 minutes.

[0038] (4) Then add mica, carbon black, and glass fiber, stir for 55 minutes, and keep the pressure at 5MPa.

[0039] (5) Extrude with a screw extruder, start calendering, and die-cut to obtain a damping plate with high damping performance.

[0040] The economical and en...

Embodiment 3

[0042] An economical and environment-friendly damping plate with high damping performance described in this embodiment includes the following raw materials: polyurethane elastomer, fly ash, mica, hydrogenated C5 petroleum resin, glass fiber, carbon black, anti-aging agent, antioxidant, Its mass ratio is: 250; 410; 475; 40; 10; 20;

[0043] Its preparation method comprises the following steps:

[0044] (1) Turn on the vacuum kneader and heat up to 200°C,

[0045] (2) Start the vacuum kneader, add polyurethane elastomer, antioxidant, antiaging agent, hydrogenated C5 petroleum resin, stir for 25 minutes,

[0046] (3) Lower the temperature to 155°C, add fly ash, stir for 10 minutes,

[0047] (4) Then add mica, carbon black, and glass fiber, stir for 60 minutes, and keep the pressure at 4.5MPa,

[0048](5) Extrude with a screw extruder, start calendering, and die-cut to obtain a damping plate with high damping performance.

[0049] The economical and environment-friendly dampin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an economic and environment-friendly damping plate with high damping property. The economic and environment-friendly damping plate with high damping property is prepared from the following raw materials: a polyurethane elastomer, coal ash, mica, hydrogenated C5 petroleum resin, glass fiber, carbon black, an anti-aging agent and an antioxidant in a mass ratio of (200-250):(410-500):(400-475):(40-80):(4-10):(20-100):5:5. The economic and environment-friendly damping plate with high damping property has the advantages that materials are well chosen, waste coal ash is adopted as a functional damping filler, a waste material is changed into things of value, environment-friendly polyurethane is adopted for replacing harmful asphalt, energy conservation, emission reduction and ecological environmental protection are realized, production cost is low, period is short, a production technology is scientific, the economic and environment-friendly damping plate with high damping property is convenient to manufacture, and the product has good damping and soundproof effects, high damping coefficient, strong aging resistance, long service life and wide applicability and is beneficial to large-scale industrial production.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to an economical and environment-friendly damping plate with high damping performance and a preparation method thereof. Background technique [0002] Fly ash is one of the largest industrial wastes in my country. At present, the annual slag discharge in China has reached 30 million tons. With the development of the power industry, the discharge of fly ash from coal-fired power plants is increasing year by year. If a large amount of fly ash is not treated, it will generate dust and pollute the atmosphere; if it is discharged into the water system, it will cause river silting, and the toxic chemicals in it will also cause harm to humans and organisms. Therefore, the processing and utilization of fly ash has attracted widespread attention. Therefore, the state focuses on clearly encouraging and supporting policies from the following five aspects, mainly including...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L57/02C08K13/04C08K7/14C08K3/34C08K3/04
CPCC08L75/04C08L57/02C08K13/04C08K7/14C08K3/34C08K3/04C08K3/00
Inventor 邱春孝周毕萌
Owner JIANGSU TONGMENG AUTO PARTS IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com