Ambient pressure drying method of fiber needled felt/silicon-aluminium aerogel composite insulation board
A technology of atmospheric drying and composite heat preservation, which is applied in the directions of aerogel preparation, drying solid materials, chemical instruments and methods, etc., can solve the problems of high production cost, complex preparation process, complex gel process, etc., and achieve high production efficiency. , the effect of slight powder drop and low equipment requirements
Pending Publication Date: 2016-07-06
ZHUO DA NEW MATERIAL TECH GRP
View PDF8 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Therefore, the production cost of raw materials for the traditional preparation of alumina airgel is expensive, and the gel process is complicated; if tetraethyl silicate is used for the preparation of traditional alumina airgel, the gel sol process also needs to undergo hydrolysis and polycondensation of raw materials. The preparation process is more complicated
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0033] The following will be further described in detail in conjunction with specific embodiments to clearly and completely describe the technical solutions of the present invention. Obviously, the described embodiments are only some of the embodiments of the present invention, not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.
[0034] The process of preparing silicon-aluminum composite airgel by inorganic salt method:
[0035] First configure a sodium metaaluminate solution with a certain mass concentration and stir until the sodium metaaluminate is completely hydrolyzed; then, dilute the water glass to meet the requirements of the process ratio; under stirring conditions, add Continue to stir the required amount of sodium metaaluminate solution for 1 to 2 minutes. When the solution is ensured to be e...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| density | aaaaa | aaaaa |
| transmittivity | aaaaa | aaaaa |
| water absorption | aaaaa | aaaaa |
Login to View More
Abstract
The invention provides an ambient pressure drying method of a fiber needled felt / silicon-aluminium aerogel composite insulation board. The method is characterized by firstly carrying out solvent exchange and hydrophobic modification on fiber needled felt / silicon-aluminium wet gel and then carrying out ambient pressure drying on hydrophobically modified wet gel at a low temperature of 80-120 DEG C and then drying wet gel at a high temperature of 300-400 DEG C for 40 minutes. The ambient pressure drying method provided by the invention has the excellent effects that the product produced by the method has high yield and high production efficiency, dusts slightly and can undergo industrial scaling up; the ambient pressure drying method can be integrated onto assembly lines; the whole preparation method is simple and easy to control, avoids strong acid and alkali corrosion, has low requirements for equipment and is suitable for industrial production after scaling up.
Description
technical field [0001] The invention relates to a drying method for a thermal insulation board, in particular to a normal-pressure drying method for a fiber needle-punched felt / silicon-aluminum airgel composite thermal insulation board. Background technique [0002] Airgel is the material with the lowest thermal conductivity among solid substances, which is only slightly higher than vacuum, about 0.013W / m·K. Airgel also has an extremely low density, which is recognized as the least dense solid in the world, and the lowest density can reach 3kg / m 3 , which is slightly denser than air. Therefore, airgel is the thermal insulation material with the best thermal insulation effect and the smallest density in the world. [0003] At present, there are many types of aerogels, including carbon aerogels, silicon-based aerogels, and alumina aerogels. The raw material for the preparation of silica airgel can be tetraethyl silicate or water glass, and the preparation process can use no...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B01J13/00C01B33/32F26B3/00
CPCB01J13/0091F26B3/00C01B33/32
Inventor 杨卓舒纪勇孟宪娴
Owner ZHUO DA NEW MATERIAL TECH GRP