Novel porous brick and preparation method thereof

A porous brick, a new type of technology, applied in the field of building materials, can solve the problems of secondary pollution, save resources, enhance the ability of tensile strength and plastic deformation, and improve thermal stability.

Inactive Publication Date: 2016-07-06
欧士玺
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem mainly solved by the present invention is to provide a new type of porous brick and its preparation method, which uses waste concrete, saves resources, and solves the problem of se

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A new type of porous brick and its preparation method. The raw materials (by weight) are 20 parts of ceramsite, 10 parts of pottery sand, 40 parts of recycled fine aggregate, 20 parts of fly ash, 5 parts of montmorillonite, and plant straw powder 8 parts, 2 parts of lignocellulose, 1 part of coal gangue, 0.1 part of water reducing agent, and 0.2 part of foaming agent. The regenerated fine aggregate is obtained directly from waste concrete after crushing and filtering. Aggregate particle size is less than 5mm.

[0012] The preparation method of the above-mentioned porous brick is as follows: put ceramsite, ceramsite, regenerated fine aggregate and lignocellulose into a high-speed mixer in proportion, stir and mix at a speed of 500-800rpm at room temperature for 20-30min; Coal ash, montmorillonite, plant straw powder, coal gangue, water reducing agent, and foaming agent are added to a high-speed mixer and mixed; after mixing evenly, a high-pressure brick machine is used t...

Embodiment 2

[0015] A new type of porous brick and its preparation method. The raw materials (by weight) are 22 parts of ceramsite, 15 parts of pottery sand, 42 parts of recycled fine aggregate, 23 parts of fly ash, 6.5 parts of montmorillonite, and plant straw powder. 8.5 parts, 3 parts of lignocellulose, 2 parts of coal gangue, 0.15 parts of water reducing agent, and 0.25 parts of foaming agent. The regenerated fine aggregate is obtained directly from waste concrete after crushing and filtering. Aggregate particle size is less than 5mm.

[0016] The preparation method of the above-mentioned porous brick is as follows: put ceramsite, ceramsite, regenerated fine aggregate and lignocellulose into a high-speed mixer in proportion, stir and mix at a speed of 500-800rpm at room temperature for 20-30min; Coal ash, montmorillonite, plant straw powder, coal gangue, water reducing agent, and foaming agent are added to a high-speed mixer and mixed; after mixing evenly, a high-pressure brick machine...

Embodiment 3

[0019] A new porous brick and its preparation method. The raw materials (by weight) are 23 parts of ceramsite, 15 parts of pottery sand, 45 parts of recycled fine aggregate, 25 parts of fly ash, 6 parts of montmorillonite, and plant straw powder. 9 parts, 3.5 parts of lignocellulose, 2 parts of coal gangue, 0.15 parts of water reducer, and 0.3 parts of foaming agent. The regenerated fine aggregate is obtained directly from waste concrete after crushing and filtering. Aggregate particle size is less than 5mm.

[0020] The preparation method of the above-mentioned porous brick is as follows: put ceramsite, ceramsite, regenerated fine aggregate and lignocellulose into a high-speed mixer in proportion, stir and mix at a speed of 500-800rpm at room temperature for 20-30min; Coal ash, montmorillonite, plant straw powder, coal gangue, water reducing agent, and foaming agent are added to a high-speed mixer and mixed; after mixing evenly, a high-pressure brick machine is used to press ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel porous brick and a preparation method thereof. Raw materials (in parts by weight) comprise 20 parts of ceramsite, 10 parts of Tauscha, 40 parts of recycled fine aggregates, 20 parts of fly ash, 5 parts of montmorillonite, 8 parts of plant straw powder, 2 parts of lignocellulose, 1 part of coal gangue, 0.1 part of a water reducer and 0.2 part of a foaming agent, wherein the recycled fine aggregates are obtained by directly crushing and filtering abandoned concrete, and the particle sizes of the recycled fine aggregates are less than 5 mm. The porous brick prepared by the invention adopts the abandoned concrete to save resources and solve the problem of secondary pollution on the environment caused by the abandoned concrete; the strength and ductility of a porous brick masonry formed by pressing are improved, and the seismic capacity of the porous brick formed by pressing is enhanced.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a novel porous brick and a preparation method thereof. Background technique [0002] With the popularization of building energy saving and the continuous improvement of people's demand for the comfort of living environment, thermal insulation materials have been paid more and more attention by people. As one of the house insulation materials, the porous brick is more and more popular because of its heat preservation, sound insulation, fire prevention, and strength superior to traditional insulation materials. In order to meet the needs of building bricks, pressed porous bricks have emerged as a new energy-saving, land-saving, high-strength and green wall material, and are a good substitute for clay brick products. There are many holes in the press-molded porous brick, which can reduce the amount of materials used, and have better heat and sound insulation effects. In...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/10C04B30/02C04B20/02C04B18/24
CPCC04B20/023C04B30/02C04B14/02C04B18/16C04B18/08C04B14/104C04B18/24C04B16/02C04B18/12C04B2103/302C04B24/20C04B24/14C04B24/085C04B38/10Y02W30/91
Inventor 欧士玺
Owner 欧士玺
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap