Production process of cushion rubber

A production process and cushioning rubber technology, applied in the field of rubber, can solve the problems of easy permanent deformation, high price of natural rubber, large rubber loss factor, etc., and achieve the effect of increasing elasticity, not being prone to permanent deformation, and long service life

Inactive Publication Date: 2016-07-20
SANLIAN PUMP IND CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although NR has a small loss factor, it has the best overall performance, excellent elasticity, good fatigue resistance, low heat generation, small creep, good adhesion to metal parts, cold resistance, electrical insulation and processing performance. , so NR is widely used for shock absorption purposes, but a single type of rubber has certain weaknesses, the price of natural rubber is high, and some rubbers have a large loss factor, and some rubbers are weak and prone to permanent deformation. Some have low toughness and are easy to crack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of production technology of buffer rubber, comprises the following steps,

[0018] (1), ingredients: equipped with raw materials, the raw materials include 20 to 30 parts by weight of natural rubber, 16 parts of butadiene rubber, 10 parts of tread reclaimed rubber, 3 parts of toughening agent, 3 parts of elastic agent, silicic acid 0.2 parts of calcium, 1 part of zinc oxide, 0.05 parts of stearic acid, 0.3 parts of plasticizer, 20 parts of anti-aging agent and 10 parts of calcium carbonate; the toughening agent is polyvinyl butyral and dioctyl phthalate, two The addition ratio of the three is 2:1; the elastic agent is butadiene copolymer, ethyl acetate and maleic acid, and the addition ratio of the three is 2:1.5:1;

[0019] (2) Mixing: After fully mixing the raw materials, put them into the mixer for mixing treatment, the mixing temperature is 40°C, and the mixing time is 30 minutes;

[0020] (3) Mold forming: use a mold to shape the kneaded raw materials, and ...

Embodiment 2

[0025] A kind of production technology of buffer rubber, comprises the following steps,

[0026] (1), batching: be equipped with raw material, described raw material comprises 30 parts by weight of natural rubber, 26 parts of butadiene rubber, 20 parts of tread reclaimed rubber, 8 parts of toughening agent, 8 parts of elastic agent, calcium silicate 0.8 part, 1.5 parts of zinc oxide, 0.08 part of stearic acid, 0.5 part of plasticizer, 30 parts of anti-aging agent and 15 parts of calcium carbonate; Described toughening agent is polyvinyl butyral and dioctyl phthalate, The addition ratio of the two is 2:1; the elastic agent is butadiene copolymer, ethyl acetate and maleic acid, and the addition ratio of the three is 2:2:1;

[0027] (2) Mixing: After fully mixing the raw materials, put them into the mixer for mixing treatment, the mixing temperature is 70°C, and the mixing time is 40 minutes;

[0028] (3) Mold forming: use a mold to shape the kneaded raw materials, and then cool...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A production process of cushion rubber is related to the technical field of rubber and comprises the following steps: burdening: preparing materials, including, by weight: 20-30 parts of natural rubber, 16 parts of cis-butadiene rubber, 10 parts of tread reclaimed rubber, 3 parts of a toughener, 3 parts of an elastic agent, 0.2-0.8 part of calcium silicate, 1 part of zinc oxide, 0.05 part of stearic acid, 0.3 part of a plasticizer, 20 parts of an antiaging agent, and 10 parts of calcium carbonate, the toughener being polyvinyl butyral and dioctyl phthalate having an addition ratio of 2:1, and the elastic agent being butadiene copolymer, ethyl acetate and maleic anhydride having an addition ratio of 2:1.5:1; mixing: blending well the materials, and mixing in a mixer at 40 DEG C for 30 min; mold forming: forming the mixed materials with a mold, and cooling. The rubber produced herein has low price, high elasticity, high toughness, long service life and permanent deformation resistance.

Description

Technical field: [0001] The invention relates to the technical field of rubber, in particular to a production process of buffer rubber. Background technique: [0002] The loss factor of the rubber material used for shock absorption is not only related to the structure of the rubber itself, but also related to temperature and frequency. At normal temperature, the loss factor of natural rubber (NR) and butadiene rubber (BR) is small, styrene-butadiene rubber (SBR), neoprene rubber (CR), ethylene-propylene rubber (EPR), polyurethane rubber (PU) and silicone rubber The loss factor is in the middle, and the loss factor of butyl rubber (HR) and nitrile rubber (NBR) is the largest. [0003] There are generally five types of rubber materials used for shock absorption, namely NR, SBR, and BR are ordinary rubber materials; NBR is used for oil-resistant vulcanized rubber; CR is used for weather-resistant vulcanized rubber; IIR is used for high damping vulcanized rubber; Heat resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/00C08L17/00C08L29/14C08L47/00C08K13/02C08K3/34C08K3/22C08K5/12C08K5/101
CPCC08L7/00C08L2205/035C08L9/00C08L17/00C08L29/14C08L47/00C08K13/02C08K3/34C08K2003/2296C08K5/12C08K5/101
Inventor 何祥炎杭正飞孙国政
Owner SANLIAN PUMP IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap