A silicone filled epdm insulation
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of thermal insulation material and silicone resin, applied in the field of rubber compound, to achieve the effect of hard and dense carbon layer, improving the scope of application, and improving the ability of scouring external stress
Active Publication Date: 2018-03-20
HUBEI INST OF AEROSPACE CHEMOTECHNOLOGY
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
As for other types of silicone resins, especially phenyl silicone resins and vinyl silicone resins, because of their excellent thermo-oxidative stability, cold resistance, weather resistance, electrical insulation, hydrophobicity and anti-adhesive release properties, they have been It is widely used in high and low temperature resistant insulating paints, special coatings, adhesives, molding compounds and other fields, but it is rarely reported as a filler in rubber
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1- Embodiment 5
[0039] Table 1 The formula and material type of embodiment 1-embodiment 5 *
[0043] (1) stocking: stocking according to the proportioning of each embodiment in table 1;
[0044] Description: The total number of fillers in Example 2-Example 5 is 169phr, respectively: EPDM, 100.0; ZnO, 3.0; SA, 1.0; vulcanizing agent, 3.0; surfactant, 3.0; tackifying resin, 10.0; Fiber, 8.0; Carbon Black (C), 5.0; SiO 2 , 10.0; smoke suppressant (MoO 3 ), 3.0; MMg, 3.0; silicone, 20.0. Embodiment 1 does not add silicone resin, and the total number of parts of material is 149phr.
[0046] (3) Performance test: Test the performance of the insulation ma...
Embodiment 6- Embodiment 9
[0052] The formula of table 3 embodiment 6-embodiment 9
[0053] (1)
[0054]
[0055] (2) stocking: stocking according to the proportioning of each embodiment in table 3;
[0056] The common basic formula of embodiment 6-embodiment 9 selects the material and proportion of embodiment 1, namely: EPDM, 100.0; ZnO, 3.0; SA, 1.0; DCP, 3.0; WD-70, 3.0; TR, 10.0; PA , 8.0; carbon black (C), 5.0; SiO 2 , 10.0; smoke suppressant (MoO 3 ), 3.0; MMg, 3.0, a total of 149phr.
[0058] (4) Performance test: Test the performance of the insulation material according to the corresponding standard specifications, and the specific results are shown in Table 4.
[0059] Example 6-Example 9 adjusted the amount of two silicone resins, SR-2 and SR-4, and added an appropriate amount of magnesium salt (MMg). From the results in Table 5, it can be se...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
density
aaaaa
aaaaa
Login to View More
Abstract
A silicone resin filled EPDM thermal insulation material, its composition (parts by weight, phr) is EPDM rubber 100, silicone resin 20‑60, metal compound 3‑20, reinforcing agent 15‑20, organic fiber 8‑15 , tackifying resin 8‑12, other additives 3‑12. By adding an appropriate amount of silicone resin and metal compounds to the EPDM thermal insulation material, using its pyrolysis and reaction at high temperature, a molten silicateviscous liquid film is formed in situ, which can adhere to the surface of the cracked solid residue and pass through the liquid film. The bonding effect of the solid residue forms a solidnetwork structure in the form of physical crosslinking, which increases the self-supporting ability of the carbonized layer of the thermal insulation layer and resists the scouring effect of external stress, and effectively improves the erosion resistance and ablation resistance of the thermal insulation material. . The invention can be widely used in manufacture of electric wire and cable materials which can be porcelained and other fields requiring fireproofing and flame retardant, besides being applicable to the rubber-type heat-insulating material of the engine.
Description
technical field [0001] The invention relates to a rubber compound filled with organosilicon polymers, in particular to a silicone-filled EPDM heat-insulating material, and at the same time relates to the effect of the silicone resin on the performance of the EPDM heat-insulated material. Background technique [0002] EPDM rubber has the advantages of low density, good weather resistance, aging resistance, heat resistance, etc., and its density is 0.86g / cm 3 Left and right, it has a large filling coefficient, and has good compatibility with various propellants and shell composite materials, and is an ideal thermal insulation material in the engine shell. At present, the commonly used EPDM insulation materials are mostly composed of organic fibers, flame retardants, tackifiers, reinforcing agents (mostly silica) and other functional additives. It is very easy to be cracked into small molecular gas by heat, and the pyrolysiscarbon layer and inorganic filler remain. Since the ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More