Water-soluble acrylic resin and preparing method thereof

A technology of water-soluble acrylic acid and acrylic acid, applied in the field of chemical raw materials, can solve the problems of salt spray resistance, aging resistance, self-cleaning performance and poor weather resistance.

Inactive Publication Date: 2016-08-17
GUANGZHOU NUOBAO TECH DEV CO LTD
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] When the current water-soluble acrylic resin is used to prepare outdoor environmental protection coatin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] In order to more clearly illustrate the embodiments of the present invention or the technical solutions in the prior art, the present invention will be further described below through specific embodiments.

[0013] This specific embodiment adopts the following technical scheme: water-soluble acrylic resin, which is composed of the following components by weight: methyl methacrylate 100kg, n-butyl methacrylate 100kg, acrylic acid 40kg, n-butyl acrylate 70kg, acrylic acid-2-ethyl 70kg of methylhexyl ester, 150kg of isobornyl methacrylate, 60kg of hydroxypropyl acrylate, 10kg of dibenzoyl peroxide, 250kg of water, 50kg of neutralizing agent, and 100kg of isobutanol.

[0014] The preparation method of water-soluble acrylic resin, it comprises the steps:

[0015] 1. Put isobutanol into the reaction pot at room temperature, raise the temperature to 110 degrees, and start stirring;

[0016] 2. Put methyl methacrylate, n-butyl methacrylate, acrylic acid, n-butyl acrylate, 2-et...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to water-soluble acrylic resin and a preparing method thereof, and relates to the technical field of chemical raw materials. The water-soluble acrylic resin is prepared from methyl methacrylate, n-butyl methacrylate, acrylic acid, n-butyl acrylate, 2-ethylhexyl acrylate, methyl isobornyl acrylate, hydroxy-propyl acrylate, dibenzoyl peroxide, water, a neutralizing agent and isobutyl alcohol. The water-soluble acrylic resin is formed by (methyl) methacrylate monomers as a main raw material through chemical polymerization. According to the water-soluble acrylic resin and the preparing method thereof, the water-soluble acrylic resin can be matched with curing agents such as fully etherificated amino resin and closed isocyanate to prepare outdoor environment-friendly paint, and a paint film has excellent salt mist resistance, ageing resistance, self-cleaning performance and weather resistance.

Description

technical field [0001] The invention relates to the technical field of chemical raw materials, in particular to a water-soluble acrylic resin and a preparation method thereof. Background technique [0002] Water-soluble acrylic resins include acrylic resin emulsion, acrylic resin aqueous dispersion (also known as water dilutable acrylic acid) and acrylic resin aqueous solution. Emulsions are mainly synthesized by emulsifying oily ethylenic monomers in water under the initiation of water-based free radical initiators, while resin aqueous dispersions are synthesized by different processes such as free radical solution polymerization or stepwise solution polymerization. From the perspective of particle size: emulsion particle size > resin aqueous dispersion particle size > aqueous solution particle size. [0003] Acrylic emulsion is mainly used as the base material of latex paint, and it occupies an important application in the architectural coatings market. At present, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F220/18C08F220/14C08F220/06C08F220/28
CPCC08F220/18C08F220/14C08F220/1804C08F220/06C08F220/1806C08F220/281
Inventor 张志文
Owner GUANGZHOU NUOBAO TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap