A plastic and gravure technology, applied in ink, household utensils, applications, etc., can solve the problems of large solvent residue, unusable for cooking, excessive benzene content, etc., to facilitate storage, improve adhesion fastness, and reduce anti-stickiness Effect

Inactive Publication Date: 2016-09-28
LUOHE YINGHUA PACKAGING MATERIALS CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The advantages of this ink are low price, fast volatilization speed, good printing adaptability, excellent adhesion fastness, and good composite performance, etc., which are favored by the color printing industry; the disadvantage is that the solvent residue is large, especially the benzene content exceeds the standard, so it cannot be used for cooking. use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] In this embodiment, the mass ratio of the cooking type ester-soluble plastic gravure composite ink components is:

[0018] Raw material name % by weight

[0019] n-Propyl Acetate 27%

[0020] Polyurethane resin 30%

[0021] Vinyl resin 2%

[0022] 24000 Dispersant 0.2%

[0023] Titanium dioxide 30%

[0024] Isopropanol 10%

[0025] OK412 0.8%

[0026] After the above formula is adjusted by dispersion and grinding, the cooking type ester-soluble plastic gravure composite white ink can be produced.

[0027] According to the formula of the cooking type ester-soluble plastic gravure composite ink, the cooking type ester-soluble plastic gravure composite ink which is superior to the industry standard can be produced, and its various performance indicators are:

[0028] 1 Fineness: 7µm

[0029] 2 Viscosity: 43S

[0030] 3 initial dryness: 32mm

[0031] 4 Adhesion fastness: 100%

[0032] 5 Benzene residues: None.

Embodiment 2

[0034] In this embodiment, the mass ratio of the cooking type ester-soluble plastic gravure composite ink components is:

[0035] Raw material name % by weight

[0036] n-Propyl Acetate 45%

[0037] Polyurethane resin 29%

[0038] Vinyl resin 3%

[0039] 24000 Dispersant 0.2%

[0040] No. 14 Everlasting Yellow 10%

[0041] Isopropanol 7%

[0042] OK412 0.8%

[0043] Butyl acetate 5%

[0044] After the above formula is adjusted by dispersion and grinding, the retort-type ester-soluble plastic gravure compound yellow ink can be produced.

[0045] According to the formula of the cooking type ester-soluble plastic gravure composite ink, the cooking type ester-soluble plastic gravure composite ink which is superior to the industry standard can be produced, and its various performance indicators are:

[0046] 1 Fineness: 5µm

[0047] 2 Viscosity: 28S

[0048] 3 initial dryness: 33mm

[0049] 4 Adhesion fastness: 100%

[0050] 5 Benzene residues: None.

Embodiment 3

[0052] In this embodiment, the mass ratio of the cooking type ester-soluble plastic gravure composite ink components is:

[0053] Raw material name % by weight

[0054] n-Propyl acetate 40.6%

[0055] Polyurethane resin 29%

[0056] Vinyl resin 3%

[0057] 24000 Dispersant 0.4%

[0058] No. 146 Everlasting Rosé 10%

[0059] Isopropanol 8%

[0060] OK412 1%

[0061] Butyl acetate 8%

[0062] After the above formula is adjusted by dispersion and grinding, the cooking type ester-soluble plastic gravure composite red ink can be produced.

[0063] According to the formula of the cooking type ester-soluble plastic gravure composite ink, the cooking type ester-soluble plastic gravure composite ink which is superior to the industry standard can be produced, and its various performance indicators are:

[0064] 1 Fineness: 7µm

[0065] 2 Viscosity: 43S

[0066] 3 Initial dryness: 28mm

[0067] 4 Adhesion fastness: 100%

[0068] 5 Benzene residues: None.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to cooking-type ester-soluble plastic gravure compound printing ink. The cooking-type ester-soluble plastic gravure compound printing ink is prepared from, by weight, 25%-50% of n-propyl acetate, 25%-35% of polyurethane resin, 1%-5% of vinyl chloride-vinyl acetate resin, 0.1%-1% of dispersing agent, 0.5%-1% of OK412, 8%-35% of pigment and filler and 8%-20% of solvents, wherein the solvents are isopropyl alcohol and butyl acetate, the polyurethane resin is polyurethane resin of which the cooking temperature is lower than 121 DEG C, the dispersing agent is a Lubrizol 24000 dispersing agent, and OK412 is Degussa gas-phase method silicon dioxide extinction powder. The cooking-type ester-soluble plastic gravure compound printing ink has the advantages that no poisonous and harmful solvent is contained, the adhesion of the printing ink is improved, the dispersity is improved, and storage is convenient.

Description

technical field [0001] The invention belongs to the technical field of plastic gravure composite ink, and in particular relates to a cooking type ester-soluble plastic gravure composite ink. Background technique [0002] Traditional plastic composite inks use toluene and xylene as the main solvent, and ethyl ester, methyl ethyl ketone, and isopropanol as auxiliary solvents or co-solvents. The advantages of this ink are low price, fast volatilization speed, good printing adaptability, excellent adhesion fastness, good composite performance, etc., and are favored by the color printing industry; the disadvantage is that the residual solvent is large, especially the benzene content exceeds the standard, so it cannot be used for cooking. use. For the sake of environmental protection and safety, the United States and many European countries have established strict environmental protection and hygiene standards for inks, adhesives and even film materials used in the field of food ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/03C09D11/033C09D11/102C09D11/106
CPCC09D11/03C09D11/033C09D11/102C09D11/106
Inventor 王学林岳长德李国伟银松超崔帅黄娟
Owner LUOHE YINGHUA PACKAGING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap