Flexible CO room temperature sensor and preparation method thereof

A sensor and room temperature technology, applied in the field of gas sensing, can solve the problems of complex preparation process, insufficient sensitivity, high cost, etc., and achieve the effects of uniform diameter distribution, high gas detection sensitivity, and controllable composition

Inactive Publication Date: 2016-10-05
SUZHOU INST OF NANO TECH & NANO BIONICS CHINESE ACEDEMY OF SCI
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the film-state polyaniline sensors prepared at this stage are not sensitive enough, and generally detect gases at the ppm level; in other

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flexible CO room temperature sensor and preparation method thereof
  • Flexible CO room temperature sensor and preparation method thereof
  • Flexible CO room temperature sensor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0038] In view of the many shortcomings in the prior art, the inventor of this case was able to propose the technical solution of the present invention after long-term research and extensive practice. The technical solution, implementation process and principle of the present invention will be further explained below in conjunction with several embodiments and drawings.

[0039] See figure 1 In a typical embodiment of the present invention, a preparation process of a flexible CO room temperature sensor based on polyaniline nanofiber membrane may include the following steps:

[0040] (1) Preparation of nanofiber membrane template: uniformly disperse the template polymer in a solvent, and obtain the corresponding nanofiber membrane by electrospinning;

[0041] (2) Preparation of polyaniline-coated nanofiber membrane: the nanofiber membrane template is immersed in a solution containing aniline and acid, and then an oxidant is added at low temperature for oxidative polymerization to obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a flexible CO room temperature sensor which includes a polyaniline fiber film which is mainly formed by coating a nano fiber thin film with polyaniline. The polyaniline fiber film is electrically connected to an electrode. The invention also discloses a preparation method of the flexible CO room temperature sensor. The method includes the steps of: soaking the nano fiber thin film in a solution containing aniline and an acid, adding an oxidizing agent to polymerize the aniline and coat the nano fiber thin film with polyaniline to obtain a flexible polyaniline fiber film; and electrically connecting the polyaniline fiber film to the electrode to form the flexible CO room temperature sensor. The flexible CO room temperature sensor has simple structure, high sensitivity, wide detection range and high detection speed. The flexible fiber film can be combined with substrates in different materials easily. The sensor is simple in preparation method, is low in cost and is suitable for large-scale production and application.

Description

technical field [0001] The invention relates to a gas sensor, in particular to a flexible CO room temperature sensor and a preparation method thereof, belonging to the technical field of gas sensing. Background technique [0002] CO is a common toxic gas, which mainly comes from the incomplete combustion of fossil fuels and the emission of gas tail gas. CO has great harm to human health. People's sense of smell cannot determine its concentration. Therefore, the detection of CO necessary. At the same time, CO gas is a neutral molecule, and it is difficult for general sensing materials to generate detectable signals with it. Currently, only materials doped with noble metals can effectively detect CO gas. Therefore, the detection of CO has also attracted people's attention. [0003] As far as the current research on sensing materials is concerned, metal oxides are the most researched category, but metal oxide materials are only active at high temperatures, have low sensitivit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N27/04
Inventor 陈韦赵晶晶胡颖
Owner SUZHOU INST OF NANO TECH & NANO BIONICS CHINESE ACEDEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap