A technology of release agent and co-emulsifier, which is applied in the petroleum industry, lubricating compositions, etc., can solve the problems of high cost, shortage, health hazards of operators, etc., and achieves no pollution to the environment, no corrosion of molds, and good cleaning performance. Effect

Pending Publication Date: 2016-11-02
刘方旭
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the domestic release agents are oil release agents. The raw materials of oil release agents are in short supply, the cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] An environmentally friendly emulsified release agent includes the following raw materials in parts by mass: 15 kg of dimethyl silicone oil, 4 kg of PVA-1788 polyvinyl alcohol, 4 kg of PVA-1799 polyvinyl alcohol, 6 kg of ricinoleic acid, 3 kg of dimer fatty acid kg, 1 kg of dodecyl diphenyl ether sulfonate, 4 kg of sorbitan palmitate, 2 kg of diglycolamine, 4.7 kg of triisopropanolamine, 1.0 kg of dodecyl dibasic acid, bactericidal 0.05 kg of agent and 45 kg of deionized water.

[0014] The preparation method is: 4 kg of PVA-1788 polyvinyl alcohol and 4 kg of PVA-1799 polyvinyl alcohol are dissolved in 20 kg of deionized water at 85°C to make a polyvinyl alcohol solution for use; In the container of the thermometer, add 2 kg of diglycolamine, 4.7 kg of triisopropanolamine and 1 kg of deionized water, mix well, then add 6 kg of ricinoleic acid, 3 kg of dimer fatty acid and dodecyl 1.0 kg of dibasic acid, stirred and reacted at 60-70°C for 2 hours, then added 15 kg of dim...

Embodiment 2

[0016] An environmentally friendly emulsified release agent includes the following raw materials in parts by mass: 20 kg of dimethyl silicone oil, 6.5 kg of PVA-1788 polyvinyl alcohol, 7.5 kg of ricinoleic acid, 4.5 kg of dimer fatty acid, sulfonate dimerization surface active 1.5 kg of agent, 4.5 kg of sorbitan oleate, 1.5 kg of monoisopropanolamine, 1.5 kg of triisopropanolamine, 3.2 kg of triethanolamine, 0.6 kg of undecanedibasic acid, 0.08 kg of fungicide, 52 kg of ionized water.

[0017] Its preparation method is: 6.5 kg of PVA-1788 polyvinyl alcohol is dissolved in 17 kg of deionized water at 80 ° C to make a polyvinyl alcohol solution for use; in a container with a stirrer and a thermometer, add diglycol 2 kg of alkanolamine, 4.7 kg of triisopropanolamine and 1.5 kg of deionized water, after mixing evenly, add 6 kg of ricinoleic acid, 3 kg of dimer fatty acid and 1.0 kg of dodecane dibasic acid. After stirring and reacting at 70°C for 3 hours, add 15 kg of simethicone...

Embodiment 3

[0019] An environmentally friendly emulsified release agent includes the following raw materials in parts by mass: 25 kg of dimethyl silicone oil, 5 kg of PVA-1792 polyvinyl alcohol, 9 kg of ricinoleic acid, 6 kg of dimer fatty acid, 5 kg of co-emulsifier, 1.6 kg of ethanolamine, 5.5 kg of triethanolamine, 0.4 kg of dodecane dibasic acid, 0.4 kg of undecane dibasic acid, 0.1 kg of bactericide, and 60 kg of deionized water.

[0020] Its preparation method is: 5 kg of PVA-1792 polyvinyl alcohol is dissolved in 15 kg of deionized water at 90 ° C to make a polyvinyl alcohol solution for use; in a container with a stirrer and a thermometer, add diethylene glycol 2 kg of amine, 4.7 kg of triisopropanolamine and 2 kg of deionized water, after mixing evenly, add 6 kg of ricinoleic acid, 3 kg of dimer fatty acid and 1.0 kg of dodecane dibasic acid. After stirring and reacting at ℃ for 3 hours, add 15 kg of simethicone, 2 kg of fatty alcohol polyoxyethylene ether and 5 kg of sorbitan st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environmentally friendly emulsified release agent, which comprises the following raw materials in parts by mass: 15-25 parts of dimethyl silicone oil, 5-8 parts of polyvinyl alcohol, 6-9 parts of ricinoleic acid, and 3-6 parts of dimer fatty acid 5-7 parts of co-emulsifier, 6-10 parts of hydroxyalkylamine, 0.6-1.0 part of organic dicarboxylic acid, 0.05-0.1 part of fungicide, 45-60 parts of deionized water; Synthetic main emulsifier and antirust agent with base amine, supplemented by co-emulsifier to emulsify simethicone oil in deionized water and polyvinyl alcohol to form a film, providing a method mainly used for epoxy resin and unsaturated polyester materials Emulsified mold release agent for external use of forming molds, sprayed on the surface of molds, to achieve the effect of easy molding of epoxy resin and unsaturated polyester products, no corrosion of molds, no bonding with molds, no residual decomposition products, and no influence on products Color and performance, good cleaning, no pollution to the environment and so on.

Description

technical field [0001] The invention relates to the technical field of release agents, in particular to an environmentally friendly emulsified release agent and a preparation method thereof. Background technique [0002] The release agent is a functional substance between the mold and the finished product. The release agent is an interface coating used on the surface of two objects that are easy to adhere to each other. It can make the surface of the object easy to release, smooth and clean. It is an indispensable additive to prevent the formed composite product from sticking to the mold, improve production efficiency, prolong the service life of the mold, and at the same time make the surface of the product smooth, the size is qualified, and reduce defective products. In industrial production, during the molding process of some molding materials such as epoxy resin and unsaturated polyester, it is required to have a certain thermal stability when demolding, not to corrode ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M173/02C10N40/36
Inventor 刘方旭
Owner 刘方旭
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap