Environment-friendly oil removal phosphating solution and preparation method thereof

An environmentally friendly, phosphating solution technology, applied in the coating process of metal materials, etc., can solve the problems of few breakthroughs in phosphating technology, not in line with the development of clean production, and not fully clarified, and achieve a dense phosphating film Uniformity, low cost, and the effect of simplifying the degreasing process

Inactive Publication Date: 2016-11-02
WUXI EPIC TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although scientists have done a lot of research in this area, it is not yet fully understood
After the end of World War II, there were few breakthroughs in phosphating technology, but steady development and improvement.
However, the degreasing and phosphating agents currently on the market use strong alkaline hot solutions (high energy consumption, heavy pollution, and the floating oil on the surface of the working fluid will cause secondary oil pollution to the treated parts), or use strong acids, or use easy Combustible, explosive, and toxic organic solvents produce toxic, highly corrosive, and heavy pollution of gas, liquid, and solid wastes, and also do not meet the needs of clean production development in the existing society

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The environment-friendly degreasing and phosphating solution of this embodiment is prepared from the following components in parts by weight: 10 parts of methyl acrylate, 2 parts of hexamethylenetetramine, 6 parts of hydroxylamine sulfate, 2 parts of polyvinylpyrrolidone, 4 parts of ammonium sulfate, 2 parts of starch ether, 12 parts of zinc nitrate, 2 parts of polyvinyl benzyl trimethyl quaternary ammonium salt, 2 parts of triethanolamine stearate quaternary ammonium salt, 100 parts of water, 7 parts of sodium fluorosilicate .

[0012] Weigh each component according to the above weight ratio, then mix and stir, stir evenly to completely dissolve each component, and obtain the environment-friendly degreasing and phosphating solution.

[0013] In the present invention, the surface of the metal workpiece can be treated by directly soaking and spraying, and then naturally dried to obtain a phosphating film.

Embodiment 2

[0015] The environment-friendly degreasing and phosphating solution of this embodiment is prepared from the following components in parts by weight: 20 parts of methyl acrylate, 6 parts of hexamethylenetetramine, 9 parts of hydroxylamine sulfate, 6 parts of polyvinylpyrrolidone, 5 parts of ammonium sulfate, 6 parts of starch ether, 16 parts of zinc nitrate, 6 parts of polyvinyl benzyl trimethyl quaternary ammonium salt, 6 parts of triethanolamine stearate quaternary ammonium salt, 120 parts of water, 9 parts of sodium fluorosilicate , 7 parts of disodium hydroxylamine sulfate.

[0016] Weigh each component according to the above weight ratio, then mix and stir, stir evenly to completely dissolve each component, and obtain the environment-friendly degreasing and phosphating solution.

[0017] In the present invention, the surface of the metal workpiece can be treated by directly soaking and spraying, and then naturally dried to obtain a phosphating film.

Embodiment 3

[0019] The environment-friendly degreasing and phosphating solution of this embodiment is prepared from the following components in parts by weight: 10 parts of methyl acrylate, 2 parts of hexamethylenetetramine, 6 parts of hydroxylamine sulfate, 2 parts of polyvinylpyrrolidone, 4 parts of ammonium sulfate, 2 parts of starch ether, 12 parts of zinc nitrate, 2 parts of polyvinyl benzyl trimethyl quaternary ammonium salt, 2 parts of triethanolamine stearate quaternary ammonium salt, 100 parts of water, 7 parts of sodium fluorosilicate , 4 parts of disodium hydroxylamine sulfate, 3 parts of sodium lauryl sulfate.

[0020] Weigh each component according to the above weight ratio, then mix and stir, stir evenly to completely dissolve each component, and obtain the environment-friendly degreasing and phosphating solution.

[0021] In the present invention, the surface of the metal workpiece can be treated by directly soaking and spraying, and then naturally dried to obtain a phospha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly oil removal phosphating solution and a preparation method thereof. The environment-friendly oil removal phosphating solution is prepared from, by weight, 10-20 parts of methyl acrylate, 2-6 parts of hexamine, 6-9 parts of hydroxylamine sulphate, 2-6 parts of polyvinylpyrrolidone, 4-5 parts of ammonium peroxydisulfate, 2-6 parts of starch ether, 12-16 parts of zinc nitrate, 2-6 parts of polyethylene benzyl trimethyl quaternary ammonium salt, 2-6 parts of stearic acid triethanolamine ester quaternary, 100-120 parts of water, and 7-9 parts of sodium fluosilicate. A phosphating film prepared through the environment-friendly oil removal phosphating solution is compact and uniform; the oil removal procedure in the phosphating process is simplified, and the phosphating efficiency is improved; and the preparation method is simple and low in cost.

Description

technical field [0001] The invention relates to an environment-friendly degreasing and phosphating solution and a preparation method thereof. Background technique [0002] Phosphating is a commonly used pretreatment technology. In principle, it should belong to chemical conversion film treatment. It is mainly used for phosphating on the surface of steel, and non-ferrous metals (such as aluminum and zinc) can also be phosphating. Phosphating is a process in which chemical and electrochemical reactions form a phosphate chemical conversion film, and the formed phosphate conversion film is called a phosphating film. The purpose of phosphating is mainly to provide protection for the base metal and prevent the metal from being corroded to a certain extent; it is used as a primer before painting to improve the adhesion and anti-corrosion ability of the paint film layer; it can reduce friction in the metal cold processing process Lubrication. The phosphating process includes chemi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/34
CPCC23C22/34
Inventor 尤为
Owner WUXI EPIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap