Castable for grate cooler wall

A castable and grate cooler technology, applied in the field of refractory materials, can solve the problems of poor wear resistance, short service life, weak thermomechanical abrasion and chemical erosion, etc., achieve long service life, optimize construction performance, and improve wear resistance The effect of property and alkali corrosion resistance

Inactive Publication Date: 2016-11-09
张婷
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, mullite refractory castables are used in this field. The disadvantages are that the wear resistance is poor, the service life is relatively short, and the thermomechanical and chemical erosion effects on high-temperature clinker are relatively weak. It is urgent to develop a high-temperature-resistant, high-temperature Wear-resistant, high-alkali-resistant new materials to meet the performance requirements of this part

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Example 1, 17% of tabular corundum, 19% of silicon carbide, 30% of ferrochrome slag, 10% of zinc ferrite, 8% of magnesium zirconium olivine, 2% of magnesium potassium titanate, 1% of trizirconium aluminum nitride, magnesium 3% wollastonite, 5% alumina micropowder, 2% calcium zirconate aluminate, 3% high alumina cement; plus 1% Taiyuan purple gangue, Ti 3 SiC 2 0.5%, methallyl alcohol polyoxyethylene ether 0.1%, isopentenol polyoxyethylene ether 0.05%, aluminum potassium sulfate dodecahydrate 0.1%, chromium potassium sulfate dodecahydrate 0.05%; Pour the bagged castable into the mixer and stir evenly, then add 3-6% water, stir for 5 minutes and then cast.

Embodiment 2

[0013] Example 2, 22% of tabular corundum, 19% of silicon carbide, 29% of ferrochrome slag, 6% of zinc ferrite, 8% of magnesium zirconium olivine, 2% of magnesium potassium titanate, 1% of trizirconium aluminum nitride, magnesium 3% wollastonite, 5% alumina micropowder, 2% calcium zirconate aluminate, 3% high alumina cement; plus 1% Taiyuan purple gangue, Ti 3 SiC 2 0.5%, methallyl alcohol polyoxyethylene ether 0.1%, isopentenol polyoxyethylene ether 0.05%, aluminum potassium sulfate dodecahydrate 0.1%, chromium potassium sulfate dodecahydrate 0.05%. When using on site, pour the bagged castable into the mixer, stir evenly, then add 3-6% water, stir for 5 minutes and pour it for use.

Embodiment 3

[0014] Example 3, 22% of tabular corundum, 19% of silicon carbide, 28% of ferrochrome slag, 7% of zinc ferrite, 7% of magnesium zirconium olivine, 2% of magnesium potassium titanate, 2% of trizirconium aluminum nitride, magnesium 3% wollastonite, 5% alumina micropowder, 2% calcium zirconate aluminate, 3% high alumina cement; plus 1% Taiyuan purple gangue, Ti 3 SiC 2 0.5%, methallyl alcohol polyoxyethylene ether 0.1%, isopentenol polyoxyethylene ether 0.05%, aluminum potassium sulfate dodecahydrate 0.1%, chromium potassium sulfate dodecahydrate 0.05%. When using on site, pour the bagged castable into the mixer, stir evenly, then add 3-6% water, stir for 5 minutes and pour it for use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flame retardantaaaaaaaaaa
Login to View More

Abstract

The invention is aimed at providing a high-temperature-resistant, high-wear-resistance and high-alkaline-corrosion-resistance castable for a grate cooler wall for overcoming the defects in the prior art, and is also aimed at providing a preparation method of the castable. According to the technical scheme, the castable is characterized by being prepared from, by weight, 15-25 % of tabular corundum, 10-20% of silicon carbide, 23-30% of ferrochrome slag, 5-10% of zinc ferrite, 5-8% of magnesia-zirconia olivine, 1-3% of potassium magnesium titanate powder, 1-2% of trizirconium nitride aluminide, 3-5% of silica powder, 5-10% of alumina micro powder, 2-3% of zirconium calcium aluminate, 3-5% of high-alumina cement, 1% of added Taiyuan purple flower recrement, 0.5% of Ti3SiC2, 0.1% of methallyl alcohol polyoxyethylene ether, 0.05% of isopentenyl alcohol polyoxyethylene ether, 0.1% of aluminium potassium sulfate dodecahydrate and 0.05% of chromium potassium sulfate.

Description

technical field [0001] The invention belongs to the field of refractory materials, and in particular relates to a castable for grate cooler walls and a preparation method thereof. Background technique [0002] At present, my country's new dry process cement production line is developing rapidly, and the cement production capacity has been severely oversupplied. Therefore, it is the only way for cement production enterprises to increase unit production efficiency and reduce production costs to maximize profits. And improving the operation rate of the cement production line is an important condition for improving the production efficiency of the cement kiln. However, the life of the cement kiln grate cooler wall has an important impact on the operation cycle of the entire production line. The grate cooler wall of the cement kiln is used in harsh conditions. In addition to high temperature, it also bears the continuous discharge pressure of the cement kiln clinker, and the im...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
CPCC04B35/66
Inventor 张婷
Owner 张婷
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com