Oil-resistant and abrasion-resistant dual-density shoe rubber outsole and preparation method thereof
A dual-density, rubber technology, applied in the field of rubber manufacturing, can solve problems such as poor wear resistance, poor strength, poor physical and chemical properties of wear marks, and high hardness of vulcanized rubber, achieving both processability, physical and chemical properties of vulcanized rubber, and raw materials Reasonable effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0080] Example 1 Oil-resistant and wear-resistant dual-density footwear rubber outsole and preparation method thereof
[0081] This embodiment provides an oil-resistant, wear-resistant dual-density footwear rubber outsole and a preparation method thereof. The specific preparation process is carried out in sequence according to the following steps:
[0082] (11) Rubber mastication
[0083] Put 30kg of natural rubber (model SCRWF) into an open mill or internal mixer for plastic smelting. After the plasticity reaches 0.45-0.50, the natural rubber A1 with plasticity meeting the requirements is obtained;
[0084] (12) Compounding of rubber
[0085] Put neoprene (20kg neoprene CR322 A, 18kg neoprene CR232 ) And 33 kg of butadiene rubber (model BR9000), respectively, after being thinned and broken, and then put into an open mill or internal mixer together with A1 for mixing. After mixing until the cross section of the plasticized rubber is uniform, flat and smooth, C1 is obtained;
[0086] (1...
Example Embodiment
[0093] Example 2-5 Oil-resistant, wear-resistant dual-density footwear rubber outsole and preparation method thereof
[0094] This example is an oil-resistant, wear-resistant dual-density footwear rubber outsole. Its preparation method is similar to Example 1, except that the ingredients of the product and the process parameters in the preparation process are different. See the table below for details. .
[0095] Table 1 Formula and process parameters of oil-resistant and wear-resistant dual-density footwear rubber outsole
[0096]
[0097] Note: The engine oil in Example 2-5 was added in two parts. For the specific time of adding, refer to the example, the first time to add 2 / 3 of the total amount; the other time to add the remaining 1 / 3.
Example Embodiment
[0098] Example 6-9 Oil-resistant, wear-resistant dual-density footwear rubber outsole and preparation method thereof
[0099] This embodiment is an oil-resistant, wear-resistant dual-density footwear rubber outsole, and its formula composition is shown in Table 2.
[0100]
[0101] The preparation method of the oil-resistant and wear-resistant dual-density footwear rubber outsole provided in Examples 6-9 is carried out in sequence according to the following steps:
[0102] (Ⅰ) Rubber plasticizing
[0103] Put the natural rubber into the open mill or internal mixer for plasticization, and the plasticity will reach 0.45-0.50 to obtain the natural rubber a with satisfactory plasticity;
[0104] (Ⅱ) Co-refining of rubber
[0105] After the chloroprene rubber and butadiene rubber are respectively thinly broken and put into an open mill or internal mixer together with a, they are mixed until the cross-section of the plasticized rubber is uniform and smooth, and c is obtained;
[0106] (Ⅲ) One-t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap