Preparation method of micro-crosslinked-structure high-temperature-resistant salt-resistant well cementing cement slurry filtrate loss reducer
A technology of cementing cement slurry and fluid loss reducing agent, which is applied in the direction of chemical instruments and methods, drilling compositions, etc., can solve the problems of no guidance plan and low reaction temperature, etc., and achieve strong water-locking ability, The effect of lowering the reaction temperature and increasing the conversion rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example 1: The preparation method of the micro-crosslinked structure, high temperature and salt resistance cement slurry fluid loss reducer of the present invention includes the following process steps: ① Weigh 2 according to the mass ratio of 21:5:3:1 -Acrylamido-2-methylpropanesulfonic acid, acrylamide, unsaturated polycarboxylic acid (itaconic acid), N-vinylpyrrolidone, these four materials are dissolved in deionized water to obtain a solution, and the pH of the solution is adjusted Value to 7 (30% NaOH solution can be used to adjust the pH value), add 0.2% of the total reactive monomers N, N-methylene bisacrylamide and the total reactive monomers 0.5% of the molecular weight regulator sodium methacrylic acid sulfonate, formulated into a solution with a monomer concentration of 20%. ②After that, pour the solution into a three-necked flask with a thermometer and a stirring device, and heat (react) in an oil bath to increase the temperature to 45°C. ③After the temperat...
Example Embodiment
[0023] Example 2: The preparation method of the micro-crosslinked structure, high temperature and salt resistance cement slurry fluid loss reducer of the present invention includes the following process steps: ①Weigh 2 according to the mass ratio of 19:4.5:2.5:1.2 -Acrylamido-2-methylpropanesulfonic acid, acrylamide, unsaturated polycarboxylic acid (maleic acid), N-vinylpyrrolidone, these four raw materials are dissolved in deionized water to obtain a solution, and the pH of the solution is adjusted Value to 6.5 (30% NaOH solution can be used to adjust the pH value), add the crosslinking agent N, N-methylene bisacrylamide which accounts for 0.13% of the total reactive monomers and the total reactive monomers It is 0.45% of the molecular weight regulator thioglycolic acid, formulated into a solution with a monomer concentration of 18%. ②Afterwards, pour this solution into a three-necked flask with a thermometer and a stirring device, and heat it in an oil bath to raise the tempe...
Example Embodiment
[0024] Example 3: The preparation method of the micro-crosslinked structure, high temperature and salt resistance cement slurry fluid loss reducer of the present invention includes the following process steps: ① Weigh 2 according to the mass ratio of 22:6.5:5:2 -Acrylamido-2-methylpropanesulfonic acid, acrylamide, unsaturated polycarboxylic acid (fumaric acid), N-vinylpyrrolidone, these four materials are dissolved in deionized water to obtain a solution, and the pH of the solution is adjusted Value to 7.5 (30% NaOH solution can be used to adjust the pH value), add the crosslinking agent N, N-methylene bisacrylamide which accounts for 0.18% of the total reactive monomers and the total reactive monomers It is 0.58% of the molecular weight regulator mercaptopropionic acid, formulated into a solution with a monomer concentration of 23%. ②Afterwards, pour this solution into a three-necked flask with a thermometer and a stirring device, and heat it in an oil bath to raise the temper...
PUM
Property | Measurement | Unit |
---|---|---|
Compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap