Sponge city ecological water-permeable pavior brick, and preparation method thereof

A technology of permeable pavement brick and sponge city, applied in the field of ecological permeable pavement brick of sponge city, can solve the problems of easy cracking, insufficient compressive strength, poor bending resistance, etc., and achieve excellent wear resistance and anti-skid performance, low production cost, Excellent water permeability

Active Publication Date: 2016-12-21
绍兴职业技术学院
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The application of desert sand to the preparation of permeable bricks has gradually attracted attention, but the current perm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] A sponge city ecological permeable pavement brick, the pavement brick includes a sand-based surface layer and a cement concrete structure layer, and the sand-based surface layer, in parts by weight, includes the following components:

[0062] 50 parts of coated sand, 8 parts of polyethersulfone resin,

[0063] 2 parts of glass fiber, 20 parts of epoxy resin,

[0064] 5 parts of alkali lignin;

[0065] The cement concrete structure layer includes the following components in parts by weight:

[0066] 60 parts of cement, 50 parts of fly ash,

[0067] 80 parts of quartz sand, 20 parts of turpentine rock powder,

[0068] 1 part of yellow dextrin, 5 parts of polypropylene fiber,

[0069] 1 part of water reducer, 40 parts of water;

[0070] Described coated sand comprises the following components in parts by weight:

[0071] 70 parts of desert aeolian sand, 15 parts of polyurethane resin,

[0072] 5 parts of magnesia fine powder, 4.5 parts of sodium humate,

[0073] 0....

Embodiment 2

[0082] A sponge city ecological permeable pavement brick, the pavement brick includes a sand-based surface layer and a cement concrete structure layer, and the sand-based surface layer, in parts by weight, includes the following components:

[0083] 100 parts of coated sand, 12 parts of polyethersulfone resin,

[0084] 4 parts of glass fiber, 30 parts of epoxy resin,

[0085] 10 parts of alkali lignin;

[0086] The cement concrete structure layer includes the following components in parts by weight:

[0087] 80 parts of cement, 75 parts of fly ash,

[0088] 100 parts of quartz sand, 40 parts of turpentine rock powder,

[0089] 6 parts of yellow dextrin, 10 parts of polypropylene fiber,

[0090] 4 parts of water reducer, 50 parts of water;

[0091] Described coated sand comprises the following components in parts by weight:

[0092] 70 parts of desert aeolian sand, 15 parts of polyurethane resin,

[0093] 5 parts of magnesia fine powder, 4.5 parts of sodium humate,

[0...

Embodiment 3

[0103] A sponge city ecological permeable pavement brick, the pavement brick includes a sand-based surface layer and a cement concrete structure layer, and the sand-based surface layer, in parts by weight, includes the following components:

[0104] 60 parts of coated sand, 9 parts of polyethersulfone resin,

[0105] 2.5 parts of glass fiber, 22 parts of epoxy resin,

[0106] 6 parts of alkali lignin;

[0107] The cement concrete structure layer includes the following components in parts by weight:

[0108] 65 parts of cement, 55 parts of fly ash,

[0109] 85 parts of quartz sand, 30 parts of turpentine rock powder,

[0110] 2 parts of yellow dextrin, 6 parts of polypropylene fiber,

[0111] 2 parts of water reducer, 42 parts of water;

[0112] Described coated sand comprises the following components in parts by weight:

[0113] 70 parts of desert aeolian sand, 15 parts of polyurethane resin,

[0114] 5 parts of magnesia fine powder, 4.5 parts of sodium humate,

[0115...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a sponge city ecological water-permeable pavior brick. The sponge city ecological water-permeable pavior brick comprises a sand foundation surface layer and a cement concrete structural layer. The sand foundation surface layer comprises, by weight, 50 to 100 parts of coated sand, 8 to 12 parts of polyether sulfone resin, 2 to 4 parts of glass fiber, 20 to 30 parts of epoxy resin, and 5 to 10 parts of alkali lignin. The cement concrete structural layer comprises, by weight, 60 to 80 parts of cement, 50 to 75 parts of fly ash, 80 to 100 parts of quartz sand, 20 to 40 parts of pitchstone powder, 1 to 6 parts of yellow dextrin, 5 to 10 parts of polypropylene fiber, 1 to 4 parts of a water reducing agent, and 40 to 50 parts of water. The invention also discloses a preparation method of the sponge city ecological water-permeable pavior brick. The sponge city ecological water-permeable pavior brick possesses excellent water permeability, wear resistance, and slip resistance, high flexural and compressive strength, and high temperature resistance, and is low in preparation cost.

Description

Technical field: [0001] The invention relates to the field of building materials, in particular to a sponge city ecological permeable pavement brick. Background technique: [0002] With the development of the economy, the surface of modern cities is more and more covered by buildings and concrete. This "hardening" of the surface makes it difficult for atmospheric precipitation to penetrate into the ground in time, and the surface runoff increases, forming the "heat island effect". As well as environmental problems such as waterlogging and urban surface subsidence caused by insufficient drainage. As an environmental material, porous permeable bricks are applied to the paving of roads and squares, which can allow part of the precipitation to infiltrate into the ground and reduce surface runoff, thus better solving the above problems. [0003] In my country, the total area of ​​desert is about 637,000 km 2 , Accounting for about 6.8% of the country's land, mainly distributed ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B26/14E01C5/06E01C11/22
CPCC04B26/14C04B28/00C04B2111/00284C04B2111/0075E01C5/065E01C11/225C04B14/06C04B24/28C04B14/42C04B24/24C04B18/08C04B24/38C04B16/0633C04B2103/302
Inventor 汤薇沈龙蒋晓燕孙秋砚孔爱散
Owner 绍兴职业技术学院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products