Dawsonite and zinc tetrafluoroborate compounded flame retardant EVA electric cable material and preparation method thereof

A technology for compounding zinc fluoroborate and dawsonite, which is used in circuits, electrical components, plastic/resin/wax insulators, etc., can solve the problem that flame retardancy cannot meet the needs of the market, and achieve smoke suppression performance, non-toxic, Reduces acid fumes and has good heat aging resistance

Inactive Publication Date: 2016-12-21
ANHUI CHUNHUI INSTR CABLE GROUP
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, with the rapid development of the wire and cable manufacturing industry, the requirements for the flame retardancy of EVA cable mater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dawsonite and zinc tetrafluoroborate compounded flame retardant EVA electric cable material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] A flame-retardant EVA cable material compounded with dawsonite and zinc fluoroborate, which is made of the following raw materials (kg): EVA resin 65, chloromethoxy fatty acid methyl ester 16, polyphenylene sulfide 37, Bisphenol A polysulfone 32, zirconium oxychloride 13, pentachlorobiphenyl 8, diatomaceous earth 20, brominated paraffin wax 12, graphite tailings 22, dawsonite 16, zinc fluoroborate 12, barium stearate 3.5, cadmium stearate 2.5, zircon powder 12, sulfur-fixed ash 18.

[0012] A preparation method of dawsonite compound zinc fluoroborate flame-retardant EVA cable material, comprising the following steps:

[0013] (1) Mix diatomite, graphite tailings, and sulfur-fixed ash evenly, pulverize, sieve, and calcinate at 670-730°C for 1-3h, cool to room temperature, and prepare the calcined powder according to the solid-to-liquid ratio of 1:6-7 Add it into the sulfuric acid solution with a mass fraction of 20%, heat it in a water bath to 65-70°C, soak it for 1.5-2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a dawsonite and zinc tetrafluoroborate compounded flame retardant EVA electric cable material and a preparation method thereof, wherein the dawsonite and zinc tetrafluoroborate compounded flame retardant EVA electric cable material is prepared from the following raw materials by weight: 57-72 parts of an EVA resin, 14-18 parts of chloro-methoxy fat diethylene glycol dinitrate, 29-43 parts of polyphenylene sulfide, 25-40 parts of bisphenol A polysulfone, 10-15 parts of zirconyl chloride, 5-10 parts of pentachlorobibenzene, 17-23 parts of diatomaceous earth, 10-15 parts of brominated paraffin, 20-25 parts of graphite tailings, 12-18 parts of dawsonite, 10-15 parts of zinc tetrafluoroborate, 3-4 parts of barium stearate, 2-3 parts of cadmium stearate, 8-16 parts of zircon powder, and 15-20 parts of fixing sulfur ash. The dawsonite and zinc tetrafluoroborate compounded flame retardant EVA electric cable material of the present invention has advantages of high mechanical strength, good heat aging resistance, good flame retardant effect, good smoke suppression performance and no toxicity, and is suitable for all kinds of electric cables.

Description

technical field [0001] The invention relates to a dawsonite compound zinc fluoroborate flame-retardant EVA cable material and a preparation method thereof, belonging to the technical field of cable material manufacturing. Background technique [0002] Ethylene-vinyl acetate copolymer, English abbreviation: EVA, has a wide range of applications in the wire and cable industry because of its good physical and mechanical properties and processability, especially its high fillability. In recent years, with the rapid development of the wire and cable manufacturing industry, the requirements for the flame retardancy of EVA cable materials are getting higher and higher, and the flame retardancy of traditional EVA cable materials is increasingly unable to meet the needs of the market. Contents of the invention [0003] In view of the above-mentioned deficiencies in the prior art, the technical problem to be solved by the present invention is to provide a dawsonite compound zinc flu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08L81/02C08L81/06C08K13/06C08K9/02C08K3/34C08K3/26C08K3/38H01B3/44
CPCC08K2201/014C08L23/0853C08L2201/02C08L2203/202C08L2205/035H01B3/441C08L81/02C08L81/06C08K13/06C08K9/02C08K3/34C08K3/26C08K2003/387
Inventor 沈必亮
Owner ANHUI CHUNHUI INSTR CABLE GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap