Walnut shell plant fiber synthetic resin and preparation process thereof

A plant fiber and synthetic resin technology, applied in the field of walnut shell plant fiber synthetic resin and its preparation process, can solve the problems of unfavorable degradation, damage to soil water permeability, high cost, etc., to alleviate the shortage of resources, increase farmers' income, and have a long service life Effect

Inactive Publication Date: 2016-12-21
安徽科邦树脂科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing tableware, furniture, kitchen utensils and other daily necessities on the market are all made of wood, bamboo, ordinary plastics and other products. Pollution" destroys the water permeability of the soil, while wood and bamboo products require deforestation and waste water pollution during the manufacturing process, so they are not very good environmental protection materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A walnut shell plant fiber synthetic resin, comprising the following raw materials in parts by weight: 30 parts of walnut shell powder, 5 parts of methyl cellulose, 15 parts of polyvinyl alcohol, 3 parts of aliphatic dicarboxylic acid, 15 parts of amino resin, sorbose 3 parts of alcohol, 3 parts of gelatin powder, 5 parts of alkyl sulfonate, 10 parts of polylactic acid fiber;

[0021] Its preparation process comprises the following steps:

[0022] (1), walnut shells are subjected to ultra-fine grinding processing to obtain fine particle walnut shell powder;

[0023] (2), put sorbitol and aliphatic dicarboxylic acid into the high-speed mixer, add methyl cellulose and stir evenly to obtain the initial mixed material;

[0024] (3) Put the walnut shell powder in step (1) into a high-speed mixer and mix it with the primary mixing material in step (2), add amino resin and stir evenly, then cool to room temperature, and pulverize after solidifying into a block , to get walnu...

Embodiment 2

[0031] A walnut shell plant fiber synthetic resin, comprising the following raw materials in parts by weight: 60 parts of walnut shell powder, 10 parts of methyl cellulose, 40 parts of polyvinyl alcohol, 8 parts of aliphatic dicarboxylic acid, 40 parts of amino resin, sorbose 8 parts of alcohol, 8 parts of gelatin powder, 10 parts of alkyl sulfonate, 20 parts of polylactic acid fiber;

[0032] Its preparation process comprises the following steps:

[0033] (1), walnut shells are subjected to ultra-fine grinding processing to obtain fine particle walnut shell powder;

[0034] (2), put sorbitol and aliphatic dicarboxylic acid into the high-speed mixer, add methyl cellulose and stir evenly to obtain the initial mixed material;

[0035] (3) Put the walnut shell powder in step (1) into a high-speed mixer and mix it with the primary mixing material in step (2), add amino resin and stir evenly, then cool to room temperature, and pulverize after solidifying into a block , to get wal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention specifically relates to a walnut shell plant fiber synthetic resin and a preparation process thereof, belonging to the field of chemical materials. The walnut shell plant fiber synthetic resin comprises the following raw materials: walnut shell powder, methyl cellulose, polyvinyl alcohol, aliphatic dicarboxylic acid, amino resin, sorbitol, gelatin powder, alkyl sulfonate and polylactic acid fiber. The preparation process comprises the following steps: (1) preparing fine-grain walnut shell powder; (2) preparing a preliminarily mixed material; (3) preparing walnut shell fiber powder; (4) preparing a mixed additive; and (5) uniformly mixing the mixed additive and the polylactic acid fiber under stirring and carrying out blending, extrusion and injection molding so as to obtain the walnut shell plant fiber synthetic resin. According to the invention, resources like waste crop materials are prevented from wasting and made full use of, and environmental pollution is reduced; and the preparation process is low in production cost and wide in an application scope, can give full play to the resource advantage of rural areas and provides an effective method and approach for rational utilization of waste crops.

Description

technical field [0001] The invention relates to the field of chemical materials, in particular to a walnut shell plant fiber synthetic resin and a preparation process thereof. Background technique [0002] As a large agricultural country, with the continuous harvest of agriculture, the output of crop straws and other wastes has also increased significantly, of which the output of bare straws is about 650 million t / year. Except for the development and utilization of feed and fertilizer, most of them are burned, which not only wastes resources, but also seriously endangers the natural ecological environment. Therefore, the comprehensive utilization of abandoned crops is of great significance. While human beings create modern civilization, it also brings negative impacts - white pollution. Disposable tableware, disposable plastic products, and agricultural mulch are difficult to recycle, and their treatment methods are mainly incineration and landfill. Incineration will produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/00C08L1/02C08L1/28C08L29/04C08L61/20C08L89/00C08L67/04C08K5/092C08K5/053C08K5/42
CPCC08L97/005C08L2201/06C08L2205/02C08L2205/035C08L2205/16C08L1/02C08L1/28C08L29/04C08L61/20C08L89/00C08L67/04C08K5/092C08K5/053C08K5/42
Inventor 袁振洲
Owner 安徽科邦树脂科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap