Starch-polyamide anti-aging and anti-fogging greenhouse film and preparation method thereof

A polyamide and anti-fog technology, applied in the field of plastic films, can solve the problems of increased cost and short aging time of greenhouse films, etc., and achieve the effect of long anti-aging time and broad application prospects

Inactive Publication Date: 2017-01-04
TONGCHENG ZHONGHUI PLASTIC IND CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the aging time of the common greenhouse film is short, and it is generally replaced within one year when the greenhouse is closed, which greatly increases the cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A starch-polyamide anti-aging and anti-fog droplet greenhouse film, weighing the following components by weight: 50 kg of polyamide, 8 kg of calcium carbonate, 1 kg of nano-titanium dioxide, 10 kg of triphenyl phosphite, and alkylbenzenesulfonic acid Sodium 7kg, tetrabutyl titanate 1.2kg, chitosan 12kg, corn starch 60kg, gelatin 2kg, magnesium stearate 1kg, acetyl tributyl citrate 13kg, 2,6-di-tert-butyl Base-4-, methylphenol 1kg, 3-hydroxybenzoic acid 4kg, polyvinylpyrrolidone 1kg, plant saponin 4kg.

[0017] Made with the following specific steps:

[0018] (1) Mix cornstarch and sodium alkylbenzene sulfonate evenly, put them in an oven, dry them at 130°C for 120 minutes, take them out, cool them to room temperature, and vibrate the mixed powder ultrasonically for 30-40 minutes (control water bath The temperature is 30°C, the ultrasonic power is 100W), and then the mixed powder is transferred to a stirring tank, and tetrabutyl titanate is added, the temperature is con...

Embodiment 2

[0023] A starch-polyamide anti-aging and anti-fog droplet greenhouse film, which weighs the following components: 60 kg of polyamide, 15 kg of calcium carbonate, 4 kg of nano-titanium dioxide, 20 kg of triphenyl phosphite, and alkyl benzene sulfonate Sodium 9kg, Tetrabutyl titanate 1.4kg, Chitosan 14kg, Corn starch 65kg, Gelatin 3kg, Magnesium stearate 2kg, Acetyl tributyl citrate 15kg, 2,6-Ditert-tert Butyl-4-, methylphenol 1.5kg, 3-hydroxybenzoic acid 6kg, polyvinylpyrrolidone 2kg, plant saponin 6kg.

[0024] Made with the following specific steps:

[0025] (1) Mix cornstarch and sodium alkylbenzene sulfonate evenly, put them in an oven, dry them at 130°C for 120 minutes, take them out, cool them to room temperature, and vibrate the mixed powder ultrasonically for 30-40 minutes (control water bath The temperature is 30°C, the ultrasonic power is 100W), and then the mixed powder is transferred to a stirring tank, and tetrabutyl titanate is added, the temperature is controlle...

Embodiment 3

[0030] A starch-polyamide anti-aging and anti-fog droplet greenhouse film, the following components are weighed: 55 kg of polyamide, 10 kg of calcium carbonate, 3 kg of nano-titanium dioxide, 15 kg of triphenyl phosphite, and alkyl benzene sulfonate Sodium 8 kg, Tetrabutyl titanate 1.3 kg, Chitosan 13 kg, Corn starch 63 kg, Gelatin 2 kg, Magnesium stearate 2 kg, Acetyl tributyl citrate 13 kg, 2,6-Ditert-tert Butyl-4-, methylphenol 1kg, 3-hydroxybenzoic acid 5kg, polyvinylpyrrolidone 1kg, plant saponin 5kg.

[0031] Made with the following specific steps:

[0032] (1) Mix cornstarch and sodium alkylbenzene sulfonate evenly, put them in an oven, dry them at 130°C for 120 minutes, take them out, cool them to room temperature, and vibrate the mixed powder ultrasonically for 30-40 minutes (control water bath The temperature is 30°C, the ultrasonic power is 100W), and then the mixed powder is transferred to a stirring tank, and tetrabutyl titanate is added, the temperature is contr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses starch-polyamide anti-aging and anti-fogging greenhouse film and a preparation method thereof. The starch-polyamide anti-aging and anti-fogging greenhouse film is prepared from, by weight, 50-60 parts of polyamide, 8-15 parts of calcium carbonate, 1-4 parts of nano-titanium dioxide, 10-20 parts of triphenyl phosphate, 7-9 parts of sodium alkyl benzene sulfonate, 1.2-1.4 parts of tetrabutyl titanate, 12-14 parts of chitosan, 60-65 parts of corn starch, 2-3 parts of gelatin, 1-2 parts of magnesium stearate, 13-15 parts of acetyl tributyl citrate, 1-1.5 parts of 2,6-di-tert-butyl-4-methylphenol, 4-6 parts of 3-hydroxybenzoic acid, 1-2 parts of polyvinyl pyrrolidone and 4-6 parts of plant saponin. According to the greenhouse film prepared from the materials, the anti-aging time is long, the film does not need to be replaced in three years after being arranged on a greenhouse in a covering mode, the effective anti-fogging time of the greenhouse film reaches up to 900 h, and a wide application prospect is achieved.

Description

technical field [0001] The invention relates to the technical field of plastic films, in particular to a starch-polyamide anti-aging and anti-fogging drop greenhouse film and a preparation method thereof. Background technique [0002] As the covering material of the greenhouse, the greenhouse film isolates the crops from the external environment, so that the crops are in a relatively closed and controllable growth environment. Through the greenhouse covering materials, the indoor or shed environment where the crops grow is constantly exchanging and circulating energy (light, heat) and substances (water, gas fertilizer, etc.) with the external environment, and the two influence each other. interaction. Therefore, the greenhouse covering material is one of the most important components in the greenhouse. The variety and characteristics of the greenhouse covering material directly affect the growth of the crops in the greenhouse. The selection of greenhouse covering materials...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L3/02C08L77/00C08L5/08C08L89/00C08L39/06C08K13/02C08K3/26C08K3/22C08K5/526C08K5/098B29C47/92A01G9/14B29C48/92
CPCA01G9/1438B29C48/92B29C2948/92704C08J5/18C08J2303/02C08J2477/00C08K2201/011C08L3/02C08L2203/16C08L2205/035C08L77/00C08L5/08C08L89/00C08L39/06C08K13/02C08K2003/265C08K2003/2241C08K5/526C08K5/098Y02A40/25
Inventor 潘卫兵
Owner TONGCHENG ZHONGHUI PLASTIC IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap