Processing method of continuous injection shoe sole material, the material, and continuous injection shoes and processing method

A technology for shoe sole materials and processing methods, which can be used in footwear, applications, household appliances, etc., and can solve the problems that adhesives contain toxic and harmful substances, cannot be directly injection molded, and cannot be recycled.

Active Publication Date: 2017-07-07
福建斯达新材料科技有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The soles produced from ordinary sole materials cannot be directly injection molded due to their poor compatibility with the upper, which leads to the use of adhesives in the manufacturing process of shoes. The use of adhesives not only makes the production The process is complicated and the production cost is increased, and some adhesives contain toxic and harmful substances, which do not meet the standards of green environmental protection
The cooling rate of ordinary shoe materials is small, and the cooling time is long. After the shoe is formed, it takes a long time to cool down and cool down, resulting in low production efficiency of the shoe.
Ordinary shoe materials also have defects such as heavy weight, poor wear resistance, no cold resistance, poor processing performance, and non-recyclable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing method of continuous injection shoe sole material, the material, and continuous injection shoes and processing method
  • Processing method of continuous injection shoe sole material, the material, and continuous injection shoes and processing method
  • Processing method of continuous injection shoe sole material, the material, and continuous injection shoes and processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] The concrete processing method of the present embodiment is as follows:

[0058] (1) Preparation of oil-extended glue:

[0059] Styrene-Butadiene-Styrene Block Copolymer 80g naphthenic oil 50g mixing temperature 40℃ mixing time 3 hours

[0060] (2) Preparation of maleic anhydride modified propylene-based elastomer:

[0061] ExxonMobil 6102 50g Exxon Mobil 6202 50g maleic anhydride 2g dicumyl peroxide 0.5g Melting section temperature 200℃

[0062] (3) Preparation of hard material:

[0063] Oil-extended glue 130g polystyrene 20g K resin 25g Polyphenylene ether 20g Maleic anhydride modified propylene-based elastomer 5g Melting section temperature 180℃

[0064] (4) Preparation of soft material:

[0065]

[0066] (5) The hard material and the soft material are mechanically mixed according to the weight ratio of 1:2 to obtain the upper injection sole mat...

Embodiment 2

[0069] The concrete processing method of the present embodiment is as follows:

[0070] (1) Preparation of oil-extended glue:

[0071] Styrene-Butadiene-Styrene Block Copolymer 50g white mineral oil 20g mixing temperature 80℃ mixing time 3 hours

[0072] (2) Preparation of maleic anhydride modified propylene-based elastomer:

[0073] ExxonMobil 6102 150g ExxonMobil VM3000 50g maleic anhydride 7g dicumyl peroxide 0.05g Melting section temperature 150℃

[0074] (3) Preparation of hard material:

[0075] Oil-extended glue 70g polystyrene 30g K resin 26g Polyphenylene ether 5g heavy calcium powder 10g Maleic anhydride modified propylene-based elastomer 20g Melting section temperature 280℃

[0076] (4) Preparation of soft material:

[0077]

[0078]

[0079] (5) The hard material and the soft material are mechanically mixed according to the weight rat...

Embodiment 3

[0082] The concrete processing method of the present embodiment is as follows:

[0083] (1) Preparation of oil-extended glue:

[0084] Styrene-Butadiene-Styrene Block Copolymer 75g naphthenic oil 45g mixing temperature 50℃ mixing time 2 hours

[0085] (2) Preparation of maleic anhydride modified propylene-based elastomer:

[0086] ExxonMobil 6102 60g Exxon Mobil 6202 40g ExxonMobil VM3000 10g maleic anhydride 3g dicumyl peroxide 0.1g Melting section temperature 190℃

[0087] (3) Preparation of hard material:

[0088] Oil-extended glue 120g polystyrene 22g K resin 24g Polyphenylene ether 15g heavy calcium powder 2g Maleic anhydride modified propylene-based elastomer 10g Melting section temperature 200℃

[0089] (4) Preparation of soft material:

[0090]

[0091] (5) The hard material and the soft material are mechanically mixed according to the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Shore hardnessaaaaaaaaaa
Shore hardnessaaaaaaaaaa
Login to view more

Abstract

The invention provides a continuous injection shoe sole material and a processing method thereof. The continuous injection shoe sole material is prepared by mechanical mixing of a hard material and a soft material. The hard material is prepared by the melt extrusion and the granulation of oil filled rubber, polystyrene, K resin, polyphenylene ether, maleic anhydride modified propylene-based elastomer, and / or heavy calcium powder. The soft material is prepared by the mixing smelting and the granulation of oil filled rubber, methyl vinyl silicone rubber, C5 petroleum resin, foaming agent AC and expandable microsphere foaming agent. The oil filled rubber is prepared by mixing styrene-butadiene- styrene triblock copolymer and softening oil. The invention further provides a continuous injection shoe and processing method thereof. The prepared continuous injection shoe sole material has the following advantages that shoe surface and shoe sole can be formed by direct injection, and the continuous injection shoe sole material has the advantages of being light in weight, wear resistant, cold resistant, good in processing performance, and high in production efficiency, recyclable and environmental friendly and the like.

Description

technical field [0001] The invention belongs to the field of shoe sole material processing, and in particular relates to a processing method of upper injection sole material, the material, upper injection shoes and a processing method. Background technique [0002] The comfort level, service life, and special functions of shoes are all related to the performance of sole materials to a large extent. Ordinary shoe soles are not environmentally friendly because the preparation materials contain chlorine, lead, and polycyclic aromatic hydrocarbons. The soles produced from ordinary sole materials cannot be directly injection molded due to their poor compatibility with the upper, which leads to the use of adhesives in the manufacturing process of shoes. The use of adhesives not only makes the production The process is complicated and the production cost is increased, and some adhesives contain toxic and harmful substances, which do not meet the standards of green environmental pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L53/02
CPCB29B9/06B29D35/062B29D35/064C08L53/02C08L2205/035C08L91/00C08L51/06C08L25/06C08L83/04C08L57/02
Inventor 李贝林胜利叶晟林青华
Owner 福建斯达新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap