Internal sizing agent emulsion and preparation method and application of same

A technology of sizing and emulsion in slurry, which is applied in the field of emulsion, can solve the problems of reduced water resistance and achieve the effect of improving hydrophobicity

Inactive Publication Date: 2017-01-11
SHANGHAI DONGSHENG NEW MATERIALS
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN201110368172.0 discloses a hydrophilic nano-titanium dioxide or laponite dispersed in deionized water, mixed with polyaluminum sulfate sol as the water phase, alkenyl succinic anhydride as the oil phase, and the water phase and the oil phase are mixed Uniformly obtained sizing solution, however, due to the addition of hydrophilic substances, its water resistance to ASA is reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Internal sizing agent emulsion and preparation method and application of same
  • Internal sizing agent emulsion and preparation method and application of same
  • Internal sizing agent emulsion and preparation method and application of same

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] The invention provides a method for preparing a sizing agent emulsion in a slurry, which is characterized in that the cationic polymer and water are mixed, alkenyl succinic anhydride (ASA) is added, stirred homogeneously, and aluminum sulfate is added to obtain the slurry sizing agent emulsion. Sizing agent emulsion;

[0038] Wherein, the cationic polymer is an aqueous dispersion formed by copolymerization of cationic monomers, (methyl)styrene, and silane. In this preparation method, 2,2'-azobis(amidinopropyl) disalt The acid salt is used as an initiator, and the solution is prepared by radical solution polymerization using the above-mentioned mixed monomers, and then a surfactant is added to obtain the required cationic polymer.

[0039] In a preferred embodiment of the present invention, the preparation method of the slurry internal sizing agent emulsion comprises:

[0040] Step 1: Mix the cationic polymer and water at 50-70°C with a stirring speed of 8000-10000rpm / m...

Embodiment 1

[0070] 1. Preparation method of cationic polymer

[0071] a) Mix 5 grams of styrene and 5 grams of vinyltriisopropoxysilane to make a mixed monomer, and set aside.

[0072] b) Mix 90 grams of dimethylaminoethyl methacrylate monochloromethane quaternary ammonium with 10 grams of deionized water, dissolve completely, and set aside.

[0073] c) Mix 0.2 g of 2,2'-azobis(amidinopropyl) dihydrochloride and 10 g of deionized water, dissolve completely, and set aside.

[0074] d) Add 133.5 grams of deionized water into the reactor, raise the temperature to 95°C, add the aqueous solution of 2,2'-azobis(amidinopropyl) dihydrochloride in step c), and then add dropwise at 95°C Step a) Mix the monomers with the cationic monomer solution in b) for 1 hour.

[0075] e) Incubate at 95°C for 1 hour. Add 2g of cetyltrimethylammonium chloride at the end of the heat preservation, cool down to 25°C, and filter through a 100-mesh sieve. The obtained cationic polymer had a weight solid content of...

Embodiment 2

[0080] 1. Preparation method of cationic polymer

[0081] a) Mix 10 grams of methyl styrene and 10 grams of γ-methacryloxypropyltrimethoxysilane to make a mixed monomer, and set aside.

[0082] b) Mix 80 grams of dimethylaminoethyl methacrylate benzyl quaternary ammonium chloride with 10 grams of deionized water, dissolve completely, and set aside.

[0083] c) Mix 2 g of 2,2'-azobis(amidinopropyl) dihydrochloride and 10 g of deionized water, dissolve completely, and set aside.

[0084] d) Add 428 grams of deionized water into the reactor, raise the temperature to 95°C, add the aqueous solution of 2,2'-azobis(amidinopropyl) dihydrochloride in step c), and then drop it at 95°C Add the mixed monomer in step a) and the cationic monomer solution in b) for 3 hours.

[0085] e) Incubate at 60°C for 2 hours. At the end of the heat preservation, add 10 g of octadecyltrimethylammonium chloride, cool down to 25° C., and filter through a 100-mesh sieve. The obtained cationic polymer h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an internal sizing agent emulsion. A preparation method comprises the steps of mixing cationic polymer with water, adding alkenyl succinic anhydride (ASA), stirring and homogenizing the materials, and adding aluminum sulfate to obtain the internal sizing agent emulsion. The cationic polymer is a aqueous dispersion of a cationic monomer, (methyl)styrene, and silane through copolymerization, the preparation method takes 2,2'-azo-bis (amidino-propyl) dihydrochloride as an initiator, uses the above mixing monomer for free radical solution polymerization to obtain the solution, a surfactant is added, and the cationic polymer is prepared. The internal sizing agent emulsion provided by the invention is high-performance and environment-friendly product capable of being used for the papermaking coating. The product is used for internal sizing of papers, and can obviously improve the hydrophobicity of the papers, reduce the Cobb value and increase the surface strength of the papers.

Description

technical field [0001] The invention relates to an emulsion, in particular to an emulsion of an internal sizing agent and a preparation method and application thereof. Background technique [0002] Paper is mainly composed of hydrophilic cellulose fibers, so most paper is made with water as the medium, and a certain amount of water resistance is given to the paper by adding an appropriate amount of sizing agent. Paper sizing agents are generally water-insoluble amphiphilic substances. Through the reaction and combination of their hydrophilic groups and cellulose fibers, the macromolecules of the sizing agent are oriented in the paper, that is, the large hydrophobic groups are directed outwards. Reduce the surface energy of the paper and give the paper water resistance. At present, the sizing agent is mostly added to the papermaking system in the form of oil-in-water emulsion, and the amount of low-molecular surfactants should be reduced as much as possible in the emulsifica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H21/16
Inventor 施晓旦尹东华
Owner SHANGHAI DONGSHENG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com